Compressive strength test method for surface strengthening layer and substrate of axial part

A technology of surface strengthening layer and compressive strength, which is applied in the direction of applying stable tension/compression to test the strength of materials and the preparation of test samples, so as to achieve reliable and accurate data and strong operability

Active Publication Date: 2015-01-14
TIANJIN ENG MACHINERY INST
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in order to ensure the normal use of the parts and the safe operation of the machine, the compressive strength of the carburized shaft must be measured, but so far, there is no published data

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compressive strength test method for surface strengthening layer and substrate of axial part
  • Compressive strength test method for surface strengthening layer and substrate of axial part

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] In order to further understand the invention content, characteristics and effects of the present invention, the following examples are given, and detailed descriptions are as follows in conjunction with the accompanying drawings:

[0027] The structural shape of a workpiece that has been ground to a flat side is as follows figure 1 figure 2 shown.

[0028] A method for testing the compressive strength of a surface strengthening layer and a matrix of a shaft part, comprising the following steps:

[0029] a. Carburizing heat treatment steps: For the workpiece after machining, the gas carburizing method is adopted, the heating temperature is 900-930°C, the holding time is 4-7h, the carburized test part is cooled to 760-850°C and quenched directly, and then Temper at 160-200°C for 2-3 hours.

[0030] b. The finishing step of the surface of the tested part, the finishing step is grinding the outer circle of the part on a cylindrical grinding machine, and the surface roug...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a compressive strength test method for the surface strengthening layer and the substrate of an axial part. The method comprises the following steps: loading workpieces step by step to determine the pressure range for realizing damage on the workpieces, and then adopting a bisection approach method to precisely determine the pressure value for realizing damage. The method is simple, convenient and intuitive and has the advantages of strong operability reliable and accurate data and the like.

Description

technical field [0001] The invention belongs to the technical field of mechanical property detection technology of metal materials, and in particular relates to a method for testing the compressive strength of a surface strengthening layer and a matrix of shaft parts. Background technique [0002] In practical applications, shaft parts are often required to have comprehensive properties such as high strength, toughness, surface hardness and wear resistance. Carburizing is a chemical heat treatment process that is often used. After carburizing, quenching and low-temperature tempering can improve the surface and core structure, and obtain a high-hardness and high-strength surface layer, a certain toughness sub-surface layer and the core. Hard and tough inside, combining high strength and certain toughness on the same part. [0003] Under certain conditions of use, the compressive strength of carburized shafts is an important factor in determining the service life of shaft par...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N3/08G01N1/44G01N1/28
Inventor 刘俊英蒋伯平张慧星胡晓丽张国胜
Owner TIANJIN ENG MACHINERY INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com