Preparation method of composition material for ball bearing retainer

A composite material and cage technology is applied in the field of preparation of composite materials for ball bearing cages, which can solve the problem that tensile strength, flexural elastic modulus, linear expansion coefficient, and impact strength do not meet the requirements for high-temperature and high-speed precision ball bearing cages. and other problems, to achieve the effect of high bending elastic modulus, reasonable process parameter setting and high impact strength

Inactive Publication Date: 2013-05-15
LUOYANG BEARING SCI & TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] High-speed precision ball bearings often use cotton-phenolic as the base material of the cage, but the properties of cotton-phenolic ring tensile strength, flexural modulus, linear expansion coefficient, impact strength, etc. have not met the requirements of high-temperature high-speed precision ball bearings. Rack requirements
[0005] The phenolic aramid fiber cloth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] The invention is a preparation method of a composite material for a ball bearing cage.

[0022] In the preparation method of the present invention, the aramid fiber cloth woven perpendicular to the diameter and weft is used as the matrix, and the prepared phenolic resin is used as the binder, and then dipped by the dipping machine, and hot-rolled by the three-roller coiling machine. The composite material for the rolling bearing cage is prepared by winding and post-curing treatment. The phenolic resin formulated involves phenol, formaldehyde, ammonia and absolute ethanol, and aramid fiber cloth, phenol, formaldehyde, ammonia water, which is woven from the weft and weft orthogonally. And absolute ethanol are available on the market.

[0023] The preparation method of the present invention actually goes through four steps. Firstly, it is formulated into phenolic resin, secondly, the aramid fiber cloth is impregnated with the phenolic resin on the dipping machine to make the gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of a composite material for a ball bearing retainer. The method comprises the following steps of: dipping through an impregnator, conducting hot-pressing coiling through a three-roller tube coiling machine and performing post-curing treatment by taking aramid fiber cloth orthogonally weaved by wefts and warps as a base body and prepared phenolic resin as a bonder to prepare the composition material for the ball bearing retainer. The composite material for the ball bearing retainer can be used for a long time, wherein the temperature is in a range of 150-200 DEG C, the coefficient of linear expansion is less than or equal to 1.2*10 to the power of 6/DEG C, the modulus of elasticity in static bending is greater than or equal to 40MPa, and the circular strength of extension is greater than or equal to 200MPa. The process parameters are reasonably set, which are the basic conditions for the composition material for the ball bearing retainer to be in a higher using temperature range, and the basic conditions for improving other performances. Therefore, the composite material for the ball bearing retainer prepared by the invention can satisfy the using demands of high-temperature high-speed precise ball bearing retainers.

Description

[0001] technical field [0002] The invention belongs to the technical field of cage materials, and in particular relates to a preparation method of a composite material for a ball bearing cage. [0003] Background technique [0004] High-speed precision ball bearings often use cotton-phenolic as the base material of the cage, but the properties of cotton-phenolic ring tensile strength, flexural modulus, linear expansion coefficient, impact strength, etc. have not met the requirements of high-temperature high-speed precision ball bearings. Rack usage requirements. [0005] The phenolic aramid fiber cloth made of radial and weft orthogonal weaving and phenolic aramid fiber cloth is one of the important directions for the development of high-temperature and high-speed precision ball bearing cages. The use temperature of this cage material is There is no relevant report on phenolic aramid fiber cloth with a temperature lower than 150°C and a temperature greater than 150°C. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/40B29C70/54B29C53/58
Inventor 孙小波王枫宁仲贾会粉冀恩光王子君
Owner LUOYANG BEARING SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap