Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of super cool feel polyester fiber blended yarn and spinning method thereof

A polyester fiber and fiber blending technology, which is applied in yarn, textiles and paper making, can solve the problems of unseen processing technology, achieve comfortable wearing, smooth hand feeling, and reduce carbon dioxide emissions

Active Publication Date: 2016-04-20
SHANGHAI DEFULUN CHEM FIBER
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In practice, there are no reports on the products and processing technology of blended yarns containing ultra-cool polyester fibers and other fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Yarn count 40S, fiber blending ratio: super cool feeling polyester fiber 35%, bamboo fiber 50%, cotton 15%

[0009] Spinning process: using conventional cotton spinning equipment, the blended fiber is opened into rolls by blowing → carding → drawing → roving → spinning → winding and other processing procedures. Among them: 1. Open to roll: (1) Arrange the super cool polyester fiber and bamboo fiber evenly in the cotton grabber according to the blending ratio (or send the blended fiber to the cotton box by manual feeding according to the blending ratio. Blender), (2) The blended fibers are grasped by the cotton grabber for opening, and are transported to the cotton box blender by pipes. (3) The blended fibers are sent to the cotton box blender through the pipe or manually, and then processed into The lap machine is made into cotton rolls and enters the back carding process; 2. Carding process: the blending of ultra-cool polyester fiber and bamboo fiber in the carding proces...

Embodiment 2

[0011] Yarn count 40S, fiber blending ratio: super cool polyester fiber 40%, viscose 60%

[0012] Spinning process: using conventional cotton spinning equipment, the blended fiber is opened into rolls by blowing → carding → drawing → roving → spinning → winding and other processing procedures. Among them: 1. Open to roll: (1) According to the blending ratio, evenly arrange the blended fibers of super cool polyester fiber and viscose fiber in the plucker pan (or according to the blending ratio, the blended fiber is fed manually Send to the cotton box blender), (2) The blended fiber is grabbed by the cotton grabbing machine for opening, and is transported to the cotton box blender by the pipe, (3) The blended fiber is sent to the cotton box blender through the pipe or manually , And then through the lap machine to make cotton laps (or direct blowing and carding) into the back carding process; 2. Carding process: blended fiber carding sliver quantitative is 22.5g / 5m, doffer speed is...

Embodiment 3

[0014] Yarn count 40S, fiber blending ratio: super cool polyester fiber 35%, modal 65%

[0015] Spinning process: using conventional cotton spinning equipment, the blended fiber is opened into rolls by blowing → carding → drawing → roving → spinning → winding and other processing procedures. Among them: 1. Open to roll: (1) Arrange the blended fibers of ultra-cool polyester fiber and modal fiber evenly in the pan of the cotton grab according to the blending ratio (or send the blended fiber by manual feeding according to the blending ratio) (Into the cotton box blender), (2) the blended fiber is grasped by the cotton grabber to open it, and then transported to the cotton box blender by the pipe, (3) the blended fiber is sent to the cotton box blender through the pipe or manually, Then it is made into a cotton roll by a lap machine, and then enters the back carding process; 2. Carding process: the carding amount of the blended fiber is 19g / 5m, the doffer speed is 18r / min, and the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel supercool polyester fiber blended yarn and a method for spinning the blended yarn on cotton spinning equipment. Particularly, the blended yarn consists of 30 to 100 percent of supercool polyester fiber and 70 to 0 percent of other fibers, wherein the other fibers comprise tencel, modal, viscose, cotton, bamboo fiber, polyester and the like. The blended yarn is spun on the cotton spinning equipment by the special process comprising the steps of blowing, cotton carding, drawing, roving, spinning spun yarn and spooling. Various fibers are blended and the advantages of the fibers are complementary. The blended product has variable styles, has the characteristics of hygroscopicity, air permeability, wearing comfortability and smooth and glutinous handfeel, has the effect of cooling instantly, can achieve instant cooling of 1 to 2 DEG C after contacting with skin and achieve cooling temperature difference of 5 to 6 DEG C after being irradiated by sunlight, can absorb and convey sweat moisture on the surface of the skin to the surface of the fabric and diffuse after the skin excretes sweat, and is mainly applied to T-shirt, sportswear, socks and bedclothes.

Description

Technical field [0001] The invention relates to a super-cool feeling polyester fiber blended yarn and a spinning method thereof, in particular to using a super-cool feeling polyester fiber and other materials that can release the cool element material and the fiber cross section is a special-shaped cross section. Blended yarn made of textile fiber blending, and the spinning method of this super cool polyester fiber blended yarn on cotton spinning equipment. Background technique [0002] With the development of the economy, people have higher and higher requirements for the comfort, health, safety and environmental protection of clothing products. People spend more time outdoors, and the mutual penetration and integration of casual wear and sportswear is also increasingly affected. Favored by consumers, the fabrics of this type of clothing require both good comfort and require that when you are enjoying activities, once sweating occurs, the clothing should not be pasted on the ski...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04
Inventor 孔彩珍陆正辉陈辉华杨卫忠邱杰峰朱亚宏闫吉付
Owner SHANGHAI DEFULUN CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com