Binding agent for regulating stemming plasticity

A binder and plasticity technology, which is applied in the field of refractory materials, can solve the problems of affecting the performance of blasting clay, poor plasticity of blasting clay, and easy hardening, etc., and achieve the effect of improving plasticity, good effect, and improving plasticity at room temperature

Inactive Publication Date: 2015-05-06
武汉钢铁有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a binder for adjusting the plasticity of the blasting clay. The application of the binder helps to overcome the poor plasticity of the blasting clay at normal temperature, which is easy to harden and difficult to adjust, and affects the mud beating performance of the gun clay at the iron hole. technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The binder for adjusting the plasticity of the clay is composed of the following components in parts by weight: tar: 85 parts; ethanol: 2 parts; ethylene glycol: 10 parts; dichloroethyl ether: 3 parts.

[0017] The above-mentioned tar by weight and the other three solvents are respectively added and mixed evenly during the stirring process, and packaged for storage. Add the solid raw material of the gun clay and mix and roll; the measured value of the plasticity index Maxia of the gun clay is 0.9Mpa; after standing for 7 days, the Maxia value is 1.3Mpa.

Embodiment 2

[0019] The binder for adjusting the plasticity of the gun clay is composed of the following components in parts by weight: tar: 70 parts; ethanol: 5 parts; ethylene glycol: 5 parts; dichloroethyl ether: 10 parts; toluene: 5 parts; o-xylene: 5 servings.

[0020] The tar in the above ratio and other five different solvents are respectively added and mixed evenly during the stirring process, and packaged for storage. Add the solid raw material of the gun clay and mix and roll; the measured value of the plasticity index of the gun clay is 0.7MPa; after standing for 7 days, the Maxilla value is 1.1Mpa.

Embodiment 3

[0022] The composition range of the binder for adjusting the plasticity of the clay is: tar: 90 parts; ethylene glycol: 3 parts; dichloroethyl ether: 1 part; toluene: 3 parts; p-xylene: 3 parts.

[0023] The above-mentioned tar and four other different solvents are added and mixed evenly during the stirring process, and packaged for storage. Add the solid raw materials of the gun clay and mix and roll; the measured value of the plasticity index of the gun clay is 0.95MPa; after being placed for 7 days, the Maxia value is 1.3Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a binding agent for regulating the stemming plasticity. The binding agent consists of the following components in parts by weight: 70 to 90 parts of tar, 0 to 5 parts of ethanol, 1 to 10 parts of ethylene glycol, 1 to 10 parts of dichloroether, 0 to 10 parts of toluene, and 0 to 10 parts of dimethylbenzene. According to the binding agent, the tar can be in a good dissolving state, the normal temperature plasticity of the stemming can be effectively improved, and the stemming regulation can be facilitated; the boiling points of ethylene glycol and dimethylbenzene in the added solvent components can be relatively higher, stable at normal temperature, and cannot be easily volatilized, so that the plasticity of stemming can be constantly improved; and the product is low in cost, and has a good effect.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a binder for adjusting the plasticity of gun clay. Background technique [0002] Most of the blast furnace clay binders used in large blast furnaces are tar, but the blast clay produced with tar alone tends to harden and difficult to adjust at room temperature, and has poor plasticity, making it difficult to perform mud drilling operations, which affects the workability of the blast clay at the tap hole. Combining resins such as phenolic resin with tar or anthracene oil can improve the plasticity of gun clay, but resins are generally not easy to mix with tar, and the price of resins is still very high. Contents of the invention [0003] The purpose of the present invention is to provide a binder for adjusting the plasticity of the blasting clay. The application of the binder helps to overcome the poor plasticity of the blasting clay at normal temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/02C04B35/66
Inventor 周旺枝徐国涛
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap