Blended yarn, fabric and production process of seaweed fiber, wool and sulfonamide fiber

A technology of seaweed fiber and production process, which is applied in the direction of yarn, textile, textile and papermaking, etc., to achieve the effect of excellent flame retardant function, good dyeability and comfortable wearing

Active Publication Date: 2015-09-16
RUGAO CITY DINGYAN TEXTILE
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, there are many kinds of blended fibers, and the blending of seaweed fiber, wool and sulfonamide has not yet appeared.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended yarn, fabric and production process of seaweed fiber, wool and sulfonamide fiber
  • Blended yarn, fabric and production process of seaweed fiber, wool and sulfonamide fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Spinning

[0024] (1) Spinning specifications

[0025] Seaweed Fiber / Wool / Aramid Fiber: 30% / 0% / 70%

[0026] Yarn density ①Weaving yarn 14.8tex; ②Knitting yarn 18.5tex

[0027] (2) Process flow

[0028] 30% seaweed fiber + 70% sulfonamide fiber (first artificially mixed evenly) → cleaning (including multi-compartment blending machine) → carding → drawing (first, second) → roving → spun yarn → winding

[0029] a.

[0030] The fibers used in the present invention have good uniformity, and it is only necessary to remove the hard parallel threads in the fibers. After the seaweed fibers and sulfonamide fibers are fully mixed manually, the beaters of the cotton opening and cleaning machine adopt a soft opening process at a lower speed. The speed is controlled within 400~750r / min to reduce fiber damage.

[0031] b. Carding process

[0032] FA231A carding machine is selected, the rotation speed of the cylinder is 320r / min, the rotation speed of the licker-in roller is ...

Embodiment 2

[0053] (1) Spinning

[0054] (1) Spinning specifications

[0055] Seaweed Fiber / Wool / Aramid Fiber: 25% / 15% / 60%

[0056] Yarn density 58.5tex

[0057] (2) Process flow

[0058]

[0059] a.

[0060] The seaweed fiber and sulfonamide fiber are opened and cleaned separately into rolls, and the uniformity of the rolls is less than 0.8%. The fibers used in the invention have good orderness, and only need to remove the hard and parallel threads in the fibers. The beaters of the cotton opening and cleaning machine adopt a soft opening process at a low speed, and the speed of each beater is controlled within 400-750r / min to reduce fiber damage.

[0061] b. Carding process

[0062]FA231A carding machine is selected, the rotation speed of the cylinder is 320r / min, the rotation speed of the licker-in roller is 650r / min, the 5-point gauge of the cylinder cover plate is 0.30, 0.28, 0.28, 0.28, 0.30 (mm), and the total draft ratio is 112 , raw sliver weight 18.5g / 5m.

[0063] c. W...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention provides blended yarns of seaweed fibers, wools and polysulfonamide fibers, a shell fabric and a production process. The components of the fabrics include, by weight, 25-45% of the seaweed fibers, 0-35% of the wools and 35-75% of the polysulfonamide fibers. The seaweed fibers have natural fire-resistant performance, are good in moisture absorption, and are anti-bacterial and good in affinity with the human skin. The polysulfonamide fibers are also good in the fire-resistant performance; the polysulfonamide fibers have significant advantages in high-temperature heat-resistance, high-temperature strength loss rate and high-temperature dimensional stability as compared with other aramid fibers in the same variety. The wools have the most significant advantages in the fire-resistant performance in natural fibers, are hollow, good in fiber elastic recovery and are capable of heat insulating; and the wools have noble-like performance in the natural fibers. The three varieties of fibers are blended, and strong points are adopted and weak points are overcome; the shell fabric spun by the blended yarns has significant fire-resistant performance, good clothing-adopting performance and comfort, and is adaptable to the fields of superior health-preserving clothing, special protective clothing, special protective apparatuses and the like.

Description

Technical field [0001] The present invention involves a multi -fiber blend, the production process of the blended yarn, and the fabrics made by the blewed yarn, especially the blending yarn, production process and its production technology and its in seaweed fiber, wool and gramite fiberThe fabric belongs to the field of textile engineering. Background technique [0002] Nowadays, people pay more and more attention to safety protection in various work and life activities, especially for flame retardant protection of fire; more and more focused on the premise of satisfying the main functionality of clothing fabrics, while paying attention to the aesthetics and comfort of clothing.Sexuality and environmental protection.With the development of textile fiber science, innovative fiber raw materials are constantly developed, especially some urgent needy functional and functional textile fibers have initially entered industrial production, which has further adapted to the new and higher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D03D15/12D04B1/14D04B21/00D03D15/20D03D15/233D03D15/283D03D15/47D03D15/50D03D15/513
Inventor 陈坚朱张林
Owner RUGAO CITY DINGYAN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com