A treatment method for continuous casting hot steel slag

A processing method and technology for hot steel slag, applied in the field of metallurgical industry production, can solve problems such as environmental pollution and energy waste, and achieve the effects of reducing production costs, reducing pollution, reducing smelting time and power consumption

Active Publication Date: 2015-07-29
WUHU XINXING DUCTILE IRON PIPES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, hot slag contains a large amount of CaO, which is necessary for steelmaking, and carries a large amount of heat. If it is discarded directly, it will not only cause energy waste, but also cause serious pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The specific implementation of the present invention will be described in further detail below through the description of the embodiments, so as to help those skilled in the art have a more complete, accurate and in-depth understanding of the inventive concepts and technical solutions of the present invention.

[0027] The invention relates to a treatment method for continuous casting hot steel slag, which is applied to the molten steel smelting process. The molten steel smelting process is: electric furnace→LF furnace→VD furnace→continuous casting.

[0028] In order to solve the problems existing in the prior art and overcome its defects, realize the purpose of reducing the environmental pollution caused by the hot steel slag after the ladle is poured, and reduce the smelting cost, the technical scheme adopted by the present invention is as follows:

[0029] The processing method of continuous casting hot steel slag provided by the present invention is to recycle the re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a treatment method for continuous casting of thermal steel slag, which is applied to molten steel smelting processes. A molten steel smelting flow is as follows: passing through an electric furnace, an LF (ladle furnace), and a VD (Vacuum Degassing) furnace, and performing continuous casting; the treatment method comprises the following step of: recycling thermal refined steel slag remained by continuous casting steel to a next ladle of molten steel, and taking the thermal refined steel slag as refining slag for recycling. After the technical scheme is adopted, in the premise of guaranteeing the quality of the refined molten steel, slag-making materials, such as lime and fluorite are saved, the smelting time is shortened and the power consumption is reduced, the losses of electrodes and refractory materials are reduced, the consumption of steel and iron is decreased, thus the production cost is reduced; meanwhile, the rapid refined slagging is promoted, the refined treatment cycle is shortened, the corrosion of an electric arc on a steel ladle wall refractory material is reduced during heating, the service life of a steel ladle is prolonged, and the pollution of thermal steel slag to an environment after ladle pouring is reduced.

Description

technical field [0001] The invention belongs to the technical field of metallurgical industry production and relates to a new technology for recycling hot steel slag in continuous casting production. More specifically, the present invention relates to a treatment method for continuous casting hot steel slag. Background technique [0002] The hot steel slag remaining in the ladle after continuous casting of molten steel. In the prior art, the treatment of hot slag is to pour it into a slag basin to cool and then transport it to a slag yard for disposal. However, hot slag contains a large amount of CaO, which is necessary for steelmaking, and carries a large amount of heat. If it is discarded directly, it will not only cause energy waste, but also cause serious pollution to the environment. [0003] Practice has proved that returning the hot slag to the refining process can not only solve the above problems but also reduce the consumption of LF slagging material, save the sl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/076C21B3/06
CPCY02W30/543Y02W30/54Y02P10/20Y02W30/50
Inventor 赵明张洪彪谢华振徐雷黄雁
Owner WUHU XINXING DUCTILE IRON PIPES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products