Preparation method of waterproof shell fabric

A technology of waterproof fabrics and sizing materials, which is applied in manufacturing tools, textiles and papermaking, and fiber processing. It can solve problems affecting fabric quality, warp yarn fluffing, and reducing production efficiency, so as to improve weavability and product quality, and improve durability. Breaking strength and the effect of reducing end breakage rate

Active Publication Date: 2015-04-15
江苏晨越高新材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially for the processing of high-density fabrics, due to the shedding, picking, and beating-up movements of the loom, the yarn is subject to strong mechanical effects such as stretching, impact, and twists, and it is also closely related to loom components such as healds, reeds, and warp stoppers. There is a severe friction effect; in addition, each warp yarn not only has friction between each other, but also contacts with tens of thousands of weft yarns successively. These are easy to cause the warp yarns to fluff and even break, causing serious parking, which not only reduces production efficiency, but also affects the quality of the fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of waterproof shell fabric
  • Preparation method of waterproof shell fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of waterproof fabric, adopts the nylon of 20D / 12F, comprises the following steps:

[0032] 1. Raw silk inspection

[0033] 2. Warp yarn treatment: including the steps of hanging yarn, warping, sizing, doubling, splitting, drawing in heald and reeding.

[0034] Warping: The warp yarns are drawn out from the creel at the same time, and wound on the warp beam in parallel to form a warp beam. The humidity in the workshop is controlled at 55%, the speed of the machine is 250m / min, and the tension of the yarn is controlled at a total tension of 8.9kg / single yarn The tension is 5.6g, and the hairiness index is 3.3;

[0035] Sizing: combining warp beams, sizing and pressing, drying in a drying room and winding into weaving beams, wherein the size used for sizing consists of 18% (weight percent) of acrylate polymer and 3% of emulsified paraffin , ethanol 3%, water 76%, the slurry temperature is 44 ℃, the sizing rate during sizing is 10.5%, the spee...

Embodiment 2

[0043] A preparation method of a waterproof fabric, comprising the following steps:

[0044] 1. Raw silk inspection

[0045] 2. Warp yarn treatment: including the steps of hanging yarn, warping, sizing, doubling, splitting, drawing in heald and reeding.

[0046] Warping: Draw the warp yarns from the single creel at the same time, and wind them in parallel on the warp beam to form a warp beam. The humidity in the workshop is controlled at 65%, the speed of the vehicle is 270m / min, and the tension of the yarn is controlled at a total tension of 9.1kg. The hairiness index is 3.5;

[0047] Sizing: combining warp beams, sizing and pressing, drying in a drying room and winding into weaving beams, wherein the size used for sizing consists of 20% (by weight) of acrylate polymer and 4% of emulsified paraffin , 4% ethanol, 74% water, the slurry temperature is 48°C, the sizing rate during sizing is 11.5%, the vehicle speed is 270m / min, and the dipping roller pressure is 3.7kg / cm 2 , t...

Embodiment 3

[0055] A preparation method of a waterproof fabric, comprising the following steps:

[0056] 1. Raw silk inspection

[0057] 2. Warp yarn treatment: including the steps of hanging yarn, warping, sizing, doubling, splitting, drawing in heald and reeding.

[0058]Warping: The warp yarns are drawn out from the single creel at the same time, and wound on the warp beam in parallel to form a warp beam. The humidity in the workshop is controlled at 60%, the speed of the machine is 260m / min, and the tension of the yarn is controlled at a total tension of 9kg. Index is 3.5;

[0059] Sizing: the warp beams are combined, sizing, pressing, and winding into a weaving beam after being dried in a drying room, wherein the size used for sizing is composed of 19% (weight percent) of acrylate polymer and 3.5% of emulsified paraffin , ethanol 3.5%, water 74%, slurry temperature 47 ℃, the sizing rate during sizing is 115%, the vehicle speed is 260m / min, dipping roller pressure (the warp yarn is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a waterproof shell fabric. The preparation method comprises the steps of examining precursor fiber, treating warp, weaving on a weaving machine and cropping; the warp treatment comprises six steps, namely hanging yarn, beaming, slashing, combining axles, leasing, as well as drafting and scrabbling reed. Starching is performed on warp, reasonable technological parameters are adopted, and specific sizing percentage control is performed, so that the inner layer of yarn is immersed in seriflux, cohesive force between fibers is increased, and breaking-resisting strength of yarn is improved; a layer of protective film is formed on the surface of the yarn, so that the yarn is smoother and wear-resisting, the warp can bear strong mechanical action of the weaving machine and repeated abrasion among yarns, the end breakage rate of the warp during weaving is reduced, and the weavability of the warp and the quality of the waterproof shell fabric are improved.

Description

technical field [0001] The invention relates to a preparation method of a fabric, in particular to a preparation method of a waterproof fabric. Background technique [0002] The yarns used for weaving fabrics include natural fibers such as cotton, wool, hemp, and silk, and chemical fibers such as polyester and acrylic fibers. During the weaving process, the warp and weft yarns must bear different forces. Especially for the processing of high-density fabrics, due to the shedding, picking, and beating-up movements of the loom, the yarn is subject to strong mechanical effects such as stretching, impact, and twists, and it is also closely related to loom components such as healds, reeds, and warp stoppers. There is a severe friction effect; in addition, each warp yarn not only has friction between each other, but also contacts with tens of thousands of weft yarns successively. These are easy to cause the warp yarns to fluff and even break, causing serious parking, which not only...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06B3/04D02H3/00D06M15/263D06M13/02D06M13/144
Inventor 彭可群唐林海姜亭肖兵洑建明刘培佩
Owner 江苏晨越高新材料有限公司