Tire with low rolling resistance

A technology with low rolling resistance and rolling resistance coefficient, which is applied in the direction of rolling resistance optimization, special tires, tire parts, etc., and can solve problems such as poor wear performance, serious wear on the shoulder part, and uneven wear.

Active Publication Date: 2013-10-30
CHENG SHIN RUBBER CHINA
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Tires with low rolling resistance are designed to use a large amount of silica filler in the tread rubber composition to reduce the rolling resistance of the tire. However, the wear performance of this filler is poor, which will shorten the se

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tire with low rolling resistance
  • Tire with low rolling resistance
  • Tire with low rolling resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0094] The brand produced by 350g JSR company is the styrene-butadiene rubber of SBR1502, the brand produced by 150g Shanghai Gaoqiao Company is the butadiene rubber of BR9000, the brand produced by 175g Shanghai Cabot Company is the carbon black of N234, the 250g United Silica company produces The brand is 7000GR white carbon black, 20g bis-(3-triethoxysilylpropyl)-tetrasulfide produced by DEGUSSA company, 100g H&R GROUP company produced process oil of VIVATEC500, 10g stearic acid, 10g synthetic Wax, 10g of zinc oxide powder and 10g of 6PPD anti-aging agent produced by Taian Sennics Chemical Co., Ltd. were pre-mixed at high speed for 30s in a mechanical container, then mixed at medium speed for 3min, and finally mixed at 145°C. Unload, cool, and place for 4h. Then the obtained mixture was mixed with 4g of DPG accelerator produced by Shandong Shangshun Chemical Co., Ltd., 9g of CBS accelerator produced by Zhenjiang Zhenbang Company and 9.5g of sulfur at a low speed for 40s and...

Embodiment 2

[0102]250g of styrene-butadiene rubber produced by JSR company with the brand name of SBR1502, 206g of styrene-butadiene rubber produced by JSR company with the brand name of HP755, 100g of cis-butadiene rubber produced by Shanghai Gaoqiao Company with the brand name of BR9000, 50g of butadiene rubber produced by Shanghai Cabot Company The grade is carbon black of N234, 450g of white carbon black of 7000GR produced by United Silica company, 36g of DEGUSSA company's production containing bis-(3-triethoxysilanepropyl)-tetrasulfide, 44g of H&R GROUP company's production VIVATEC 500 process oil, 10g stearic acid, 10g synthetic wax, 10g zinc oxide powder and 10g 6PPD anti-aging agent produced by Taian Sennics Chemicals were pre-mixed in a mechanical container at high speed for 30s. The resulting mixture was then mixed at medium speed for 3 min and discharged at 155° C., cooled and left to stand for 4 h. Then the obtained mixture was mixed with 7.5g of DPG accelerator produced by Sh...

Embodiment 3

[0108] 200g of styrene-butadiene rubber with the brand name SBR1502 produced by JSR Company, 275g of styrene-butadiene rubber with the brand name of HP755 produced by JSR Company, 100g of butadiene rubber with the brand name of BR9000 produced by Shanghai Gaoqiao Company, and 200g of butadiene rubber produced by Shanghai Cabot Company The brand is the carbon black of N234, the brand that 250g United Silica company produces is the white carbon black of 7000GR, the bis-(3-triethoxysilyl propyl group)-tetrasulfide that 20g DEGUSSA company produces, 25g H&R GROUP company produces VIVATEC 500 process oil, 10g stearic acid, 10g synthetic wax, 10g zinc oxide powder and 10g 6PPD anti-aging agent produced by Taian Sennics Chemical Co., Ltd. were pre-mixed at high speed for 30s in a mechanical container, and then The resulting mixture was discharged at 145° C. after mixing for 3 min at medium speed, cooled and left to stand for 4 h. Then mix the obtained mixture with 4g of DPG antioxida...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a tire with low rolling resistance. The abrasion resistance of the tire is improved. The rolling resistance coefficient of the tire is smaller than 10.5kg/t. The tire comprises a tire tread which has a split-type structure and consists of a tire crown, a tire shoulder and a tire side, wherein the tire shoulder consists of the following rubber compositions in percentage by weight: 0-30 percent of cis alkadiene elastomer, 15-50 percent of copolymerization olefin polymer, 8-30 percent of carbon black, 10-40 percent of white carbon black and 3.5-35 percent of rubber additive. The tire shoulder of the tire with the low rolling resistance provided by the invention consists of the rubber compositions comprising 8-30 percent of carbon black; by the carbon black, the abrasion resistance of the tire shoulder is improved, the whole use cycle of the tire is prolonged, and the service life of the tire is prolonged. The tire provided by the invention also has low rolling resistance, good wetland road holding capacity and high abrasion resistance.

Description

technical field [0001] The invention relates to the technical field of tires, in particular to a tire with low rolling resistance. Background technique [0002] When a car is running, it will produce various driving resistances, nearly 80% of which are air resistance, and the remaining 20% ​​are rolling resistance. Due to the existence of rolling resistance, tires will consume extra fuel and release CO due to frictional heat during driving. 2 , some data show that the CO released during the tire friction heat generation process 2 It has already accounted for 3% of the greenhouse gases released by global fossil fuels; moreover, a considerable part of the fuel consumption of automobiles is also used to overcome the frictional resistance of tires. According to measurement data, every 7% reduction in tire rolling resistance can reduce vehicle fuel consumption by 1%, and the reduction in rolling resistance can also greatly reduce CO 2 emissions. Therefore, by reducing the rol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/06C08L9/02C08L9/00C08L11/00C08K13/02C08K3/04C08K5/09C08K3/22C08K3/06C08K5/548B60C1/00
CPCY02T10/86
Inventor 罗才仁
Owner CHENG SHIN RUBBER CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap