Method for processing brushed effect on glass surface

A technology of glass surface and wire drawing effect, applied in the field of glass or mirror surface, can solve the problems such as the inability to meet the higher requirements of art glass and the monotony of frosted glass, so as to achieve the effect of cheap and easy-to-clean products

Inactive Publication Date: 2013-12-25
SHENZHEN DICKSON IMPORT & EXPORT CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, frosted glass can only produce a matte or translucent uniform and monotonous effect on the glass surface or mirror surface, which still cannot meet people's higher requirements for art glass.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A processing method for anti-stainless steel wire drawing material, comprising the following steps:

[0018] 1. By weight, 18.4% of 50-60°C hot water, 23.5% of ammonium bifluoride, 12.4% of sulfuric acid, 15.7% of ammonium fluoride, and 23.5% of calcium fluoride are used as the main raw materials to prepare the corrosion solution; in other embodiments, existing The solution that other various acids or strong alkalis that have are used for glass surface corrosion will not affect the effect of the present invention;

[0019] 2. Rinse the mirror surface of the glass mirror with the above-mentioned corrosive solution, which can prevent the corrosive solution from accumulating on the mirror surface. During the corrosion process, small particle crystals will be attached to the mirror surface to form a rough surface. At the same time, use a brush to touch the mirror surface evenly and Sweep back and forth in a straight line for 1-3 minutes, so that the glass is broken at inter...

Embodiment 2

[0025] The difference with embodiment 1 is that 2 is:

[0026] Rinse the glass surface with corrosive liquid, which can prevent the corrosive liquid from accumulating on the glass surface. During the corrosion process, small particle crystals will be attached to the glass surface to form a matte surface. At the same time, the compressed air will be sprayed in a direction parallel to the glass surface. Blowing across the surface of the glass, the glass will be broken by intervals while producing matte surface, thus forming groove-shaped thin straight lines with irregular sizes of 0.1μm-1mm.

Embodiment 3

[0028] The difference from Example 1 is that step 2 is:

[0029] Rinse the surface of part of the glass mirror and part of the transparent glass with corrosive liquid, which can prevent the corrosive liquid from accumulating on the glass surface. During the corrosion process, small particle crystals will be attached to the glass surface to form a rough surface. At the same time, the water will be sprayed through the nozzle Spray across the glass surface in the direction parallel to the glass surface, so that the glass will be broken at intervals while producing matte surface, thus forming groove-shaped thin straight lines with irregular sizes of 0.1μm-1mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to glass processing, and discloses a method for processing a brushed effect on a glass surface. Trench type fine lines which are 0.1mu m-1mm are processed on the glass surface corroded by a corrosion solution. According to the method disclosed by the invention, the trench type fine lines which are 0.1mu m-1mm are processed on the corroded glass surface so that the metal line effect similar with brushed stainless steel is formed on the glass surface or a mirror surface, the brushed metal effects at different colors can be processed on the glass surfaces or the mirror surfaces at different colors, and a product is easily cleaned and cannot be oxidized.

Description

technical field [0001] The invention relates to glass processing, in particular to a method capable of processing glass or a mirror surface with an effect similar to brushed stainless steel on the glass surface. Background technique [0002] In the current upsurge of decoration and decoration, artistic glass such as glass, mirror and utensils carved with various patterns and calligraphy fonts is an irreplaceable decoration for its good light transmission, visibility, heat insulation, sound insulation, environmental protection and other materials. The effect adds vitality to the space decoration and is loved by people. In recent years, as a hazy art glass, frosted glass has added beauty to space decoration. Frosted glass is almost everywhere in the decoration space, background wall, ceiling, dining table, screen, porch, partition, floor, stairs, doors and windows, glass coffee table... It is widely used in large-scale home, hotel, bar, KTV, cafe Decoration of outdoor landsc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C15/00C03C19/00
Inventor 李烈宁
Owner SHENZHEN DICKSON IMPORT & EXPORT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com