Non-phosphorus corrosion and scale inhibitor for low-hardness water system industrial recycling cooling water

A technology of phosphorus-free corrosion and scale inhibitor, which is applied in the formulation of phosphorus-free corrosion and scale inhibitor, low hardness circulating cooling water, and phosphorus-free corrosion and scale inhibitor, can solve the problem that the effect of corrosion inhibitor cannot meet the field industrial application. , failure to form an effective system, etc., to avoid eutrophication and heavy metal pollution, to protect the environment, and to achieve good stability.

Active Publication Date: 2014-01-22
CNOOC TIANJIN CHEM RES & DESIGN INST +2
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The effect of corrosion inhibitors in other studies can not meet the field industrial application
[0007] In the existing technology, the corrosion and scale inhibitors that can meet the low hardness water quality are rarely used in the circulating cooling water system due to fa

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example one:

[0017] The concentration of 30% AMPS, acrylic acid, maleic acid, sodium allyl sulfonate AMPS-AA-SAS-MA low molecular weight quaternary copolymer aqueous solution 10%; AMPS-AA-SAS-MA low molecular weight quaternary The copolymer is a commercially available product with a molecular weight between 3000 and 5000; a 50% polyaspartic acid solution 15%, long-chain alkyl sulfonate 10%, N-long-chain alkyl amino carboxylate 5%, polyhydroxy carboxylate 5%, tungstate 3%, zinc salt 2%, pH stabilizer 1%, water 49%, add them to the beaker in turn, stir evenly to obtain the required phosphorus-free corrosion and scale inhibition Agent.

Example Embodiment

[0018] Embodiment two:

[0019] The concentration of 30% acrylic acid, maleic acid, sodium allyl sulfonate AMPS-AA-SAS-MA low molecular weight quaternary copolymer aqueous solution 15%; AMPS-AA-SAS-MA low molecular weight quaternary copolymer The molecular weight is between 3000~5000; the concentration of 50% polyaspartic acid solution 10%, long-chain alkyl sulfonate 15%, N-long-chain alkyl amino carboxylate 5%, polyhydroxy carboxylic acid Salt 10%, tungstate 2%, zinc salt 2%, pH stabilizer 1%, water 40%, add them to the beaker in turn, stir evenly to obtain the required phosphorus-free corrosion and scale inhibitor.

Example Embodiment

[0020] Embodiment three:

[0021] The concentration of 30% acrylic acid, maleic acid, sodium allyl sulfonate AMPS-AA-SAS-MA low molecular weight quaternary copolymer aqueous solution 20%, AMPS-AA-SAS-MA low molecular weight quaternary copolymer The molecular weight is between 3000~5000; the concentration of 50% polyaspartic acid solution 10%, long-chain alkyl sulfonate 5%, N-long-chain alkyl amino carboxylate 10%, polyhydroxy carboxylic acid Salt 10%, tungstate 2%, zinc salt 2%, pH stabilizer 1%, water 40%, add them to the beaker in turn, stir evenly to obtain the required phosphorus-free corrosion and scale inhibitor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a non-phosphorus corrosion and scale inhibitor suitable for the low-hardness water quality. The non-phosphorus corrosion and scale inhibitor is characterized by comprising, by weight, 15% to 20% of AMPS quadripolymer water solutions with the concentration of 30%, 10% to 15% of polyaspartic acid solutions the concentration of 50%, 5% to 10% of hydroxyl carboxylate, 5% to 15% of long-chain alkyl sulfonates, 5% to 10% of N-long-chain alkyl amino carboxylate, 1% to 5% of tungstate, 1% to 3% of zinc salt, 1% to 2% of pH stabilizers selected from sodium hydroxide or hydrochloric acid, and the balance deionized water.

Description

technical field [0001] The invention relates to the technical field of industrial water treatment, in particular to a phosphorus-free corrosion and scale inhibitor for industrial circulating cooling water systems, which is suitable for low-hardness circulating cooling water with calcium hardness less than 40 mg / L. The source of water quality can be natural low-hardness water, demineralized water after ion exchange, electrodialysis, reverse osmosis and other means to reduce hardness, wastewater reuse water with dehardening process, etc. For the circulating water in the cooling system, it is required that the calcium hardness after reaching the concentration ratio is less than 40mg / L. This type of water quality is characterized by low hardness and strong corrosiveness. It relates to a product containing polyaspartic acid, polyhydroxy carboxylate, long-chain alkyl sulfonate, AMPS-AA-SAS-MA tetrapolymer, N-long-chain alkyl amino carboxylate, tungstate , Phosphorus-free corrosion...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/10C02F5/12
Inventor 王超秦立娟陶蕾王震石硕年陈军
Owner CNOOC TIANJIN CHEM RES & DESIGN INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap