Explosive special for powdery emulsion explosive welding and preparation method thereof

An explosive welding and powdery technology, which is applied in the direction of explosives, etc., to achieve the effect of simple production process and reasonable component formula

Active Publication Date: 2014-01-29
HUBEI SHUAILI CHEM
View PDF12 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] According to the search, there is no patent application identical to the present invention in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1: The detonation velocity is 2400-2500m / s, and the special explosive for detonation ≥ 3.2cm powder emulsified explosion welding and its preparation method

[0023] The described detonation velocity is 2400-2500m / s, and the weight components of the powdery emulsified explosion welding special explosive base drug of ≥3.2cm are: 90.5% ammonium nitrate, 3.8% composite wax, 1.0% rosin, 1.2% emulsifier, Water (PH7) 3.5%, from the raw materials of the above five weight components according to specific process regulations to prepare powdery emulsified explosion welding special explosive base medicine, and then powdery emulsified explosive welding special explosive base medicine according to 100% weight components Mix evenly with 15% porous granular ammonium nitrate, 10% talcum powder, and 10% wood powder to prepare a special explosive for welding with a detonation velocity of 2400-2500m / s and a ≥3.2cm powder emulsion explosion;

[0024] The described detonation velo...

Embodiment 2

[0035] Embodiment 2: The detonation velocity is 2500-2600m / s, and the special explosive for detonation ≥ 3.5cm powder emulsified explosion welding and its preparation method

[0036] The described detonation velocity is 2500-2600m / s, and the weight components of the powdery emulsified explosion welding special explosive base drug of ≥3.5cm are: 90.5% ammonium nitrate, 3.8% composite wax, 1.0% rosin, 1.2% emulsifier, Water (PH7) 3.5%, from the raw materials of the above five weight components according to the specific process regulations to prepare powdery emulsified explosion welding special explosive base medicine, and then powdery emulsified explosive welding special explosive base medicine according to 100% weight components Mix evenly with 14% porous granular ammonium nitrate, 9% talcum powder, and 9% wood powder to prepare a special explosive for welding with a detonation velocity of 2500-2600m / s and a ≥3.5cm powder emulsion explosion;

[0037] The described detonation ve...

Embodiment 3

[0043] Embodiment three: the detonation velocity is 2600-2700m / s, and the powdery emulsified explosion welding special explosive of ≥3.8cm and its preparation method

[0044] The described detonation velocity is 2600-2700m / s, and the weight components of the powdered emulsified explosion welding special explosive base drug of ≥3.8cm are: 90.5% ammonium nitrate, 3.8% composite wax, 1.0% rosin, 1.2% emulsifier, Water (PH7) 3.5%, from the raw materials of the above five weight components according to specific process regulations to prepare powdery emulsified explosion welding special explosive base medicine, and then powdery emulsified explosive welding special explosive base medicine according to 100% weight components Mix evenly with 13% porous granular ammonium nitrate, 8% talcum powder, and 8% wood powder to prepare a special explosive for welding with a detonation velocity of 2600-2700m / s and a ≥3.8cm powder emulsion explosion;

[0045] The described detonation velocity is 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an explosive special for powdery emulsion explosive welding and a preparation method thereof and relates to the technical field of explosives. The explosive special for powdery emulsion explosive welding comprises the following components in percentage by weight: 90.5 percent of ammonium nitrate, 3.8 percent of complex wax, 1.0 percent of rosin, 1.2 percent of emulsifying agent and 3.5 percent of water at the pH value of 7. The preparation method comprises the following steps: performing aqueous phase preparation, oil phase preparation, emulsification, powder preparation by spraying, cooling and discharging on the materials according to a specific technological procedure to obtain a basic explosive special for powdery emulsion explosive welding; uniformly mixing 100 weight percent of the basic explosive special for powdery emulsion explosive welding with 13-15 percent of porous granular ammonium nitrate, 8-10 percent of talcum powder and 8-10 percent of wood flour to obtain the explosive special for powdery emulsion explosive welding. The explosive velocity of the explosive is 2400-2700m / s, the requirements of explosive welding processes of various metal composite materials can be met, the component formula is reasonable, the production process is simple, a novel process device is not required to be increased, and the explosive can be industrially produced in a large scale. The explosive can be applied to all powdery emulsion explosive manufacturing enterprises.

Description

technical field [0001] The invention relates to the technical field of explosives, in particular to a special powdery emulsified explosive for explosive welding and a preparation method thereof. Background technique [0002] Explosion welding is a solid phase welding method, usually used for welding between dissimilar metals. Modern industry needs a variety of metal composite materials, such as titanium steel and carbon steel, stainless steel and carbon steel welded composite plates...etc. Titanium, copper, aluminum, steel and other metal materials with different chemical compositions and physical properties It is difficult to achieve welding with other welding methods. And modern industry needs a variety of metal composite materials, so the explosive welding process came into being. Explosion welding is to use the energy of explosives to weld two (or more) composite materials together under the action of detonation waves to achieve high-speed oblique collision. As a spec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C06B31/28
Inventor 邓华智周佐玉薛海洋马志新周庭宋雅民邓毅戈江华
Owner HUBEI SHUAILI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap