Combined type cloth manufacturing method

A manufacturing method and composite technology, applied in chemical instruments and methods, rubber layered products, layered products, etc., can solve problems such as long processing time, machine shutdown, affecting the quality and stability of rubber compounds, etc.

Inactive Publication Date: 2014-02-12
FORMOSAN RUBBER GRP
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, unlike materials such as polyvinyl chloride (PVC) and polyurethane PU, rubber materials have the characteristics of light weight, easy and rapid processing, etc. Rubber materials usually need to be added with high strength, high elasticity, Excellent properties such as high wear resistance and corrosion resistance
[0004] Generally speaking, the previous vulcanization process used continuous production. Although the product can be completed at one time without segmental coiling, the limitation of the line speed of the light passing section and the abnormality of the vulcanizing section often cause other machines to stop. In addition to causing excessive processing times, it can also affect the quality and stability of vulcanized rubber compounds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined type cloth manufacturing method
  • Combined type cloth manufacturing method
  • Combined type cloth manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] see figure 1 As shown, it is a schematic flow chart of the manufacturing method of the composite cloth of the present invention, and please refer to figure 2 , which shows a schematic cross-sectional view of the composite cloth 10 produced by the manufacturing method.

[0025] The specific content of each step will be described in detail below, and please refer to image 3 , which shows a block diagram of a process machine corresponding to the manufacturing method of the composite fabric of the present invention. As in step S10, a base cloth 11 is provided, and the base cloth 11 can be selected from nylon fiber cloth, polyester fiber cloth, cotton cloth, polyester / nylon blended gauze or other blended yarn woven cloth with different composition fibers according to requirements. A sort of.

[0026] Firstly, when the base cloth 11 is transported to the pasting section of the production line, step S12 is performed, and an adhesive layer 12 is coated on the surface of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Provided is a combined type cloth manufacturing method, comprising the steps of: providing a piece of base cloth, coating an adhering layer on the surface of the base cloth, plying a sizing material on the adhering layer to form a combined type material, wherein the sizing material is formed by mixing a rubber compound comprising a main rubber processed through molding, and performing curing temperature process on the combined type material through a vertical hot air drying oven. The combined type material is light and can keep the characteristics of an original rubber.

Description

technical field [0001] The invention relates to a method for manufacturing composite cloth, and in particular to a method for manufacturing composite cloth capable of using continuous and discontinuous vulcanization procedures. Background technique [0002] Nowadays, the public is increasingly demanding thin rubber products, such as flame-resistant protective clothing, medical bed covers, bag leather and other related thin products, which have been widely used in industrial and consumer goods. [0003] However, unlike materials such as polyvinyl chloride (PVC) and polyurethane PU, rubber materials have the characteristics of light weight, easy and rapid processing, etc. Rubber materials usually need to be added with high strength, high elasticity, Excellent properties such as high wear resistance and corrosion resistance. [0004] Generally speaking, the previous vulcanization process used continuous production. Although the product can be completed at one time without segm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B25/10B32B25/12B32B7/12
Inventor 刘耀文徐正己
Owner FORMOSAN RUBBER GRP