Hot-continuous-rolled steel belt for oil casing of grade N80 and production method thereof
A technology for oil casing and production method, which is applied in the field of hot continuous rolling steel strip for N80 grade oil casing and its production, can solve the problems of high heat treatment cost, pollution, consumption of large energy and the environment, etc. Low consumption and low cost effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0023] Example 1
[0024] The chemical composition is: C0.25wt%, Si0.10wt%, Mn1.20wt%, P0.01wt%, S0.002wt%, Nb0.018wt%, Cr0.30wt%, Ti0.010wt%, the rest are Fe and non For the steel to avoid impurities, the continuous casting billet production is completed according to the steelmaking process route of "full three removal" smelting, LF refining, and slab casting to obtain a cast slab with a thickness of 230mm.
[0025] Then the cast slab is subjected to surface flame cleaning and sent to a heating furnace for heating. The heating temperature is 1240℃, and the temperature equalization time is ≥30min. After being discharged from the furnace, rough rolling is carried out. The thickness of the intermediate slab is 38mm, and the roughing exit temperature is 1000℃. Stand continuous rolling, the final rolling temperature is 800℃, the intermediate pyrometer value of the two-stage cooling process system is 630℃, the air cooling time is 7s, and the coiling temperature is 510℃, so as to obtain ...
Example Embodiment
[0026] Example 2
[0027] The chemical composition is: C0.29wt%, Si0.25wt%, Mn1.46wt%, P0.01wt%, S0.002wt%, Nb0.029wt%, Cr0.38wt%, Ti0.016wt%, the rest is Fe and non For the steel with avoided impurities, the continuous casting billet is produced according to the steelmaking process route of "full three-removal" smelting, LF refining, and slab casting to obtain a slab with a thickness of 232mm.
[0028] Then the cast slab is subjected to surface flame cleaning and sent to a heating furnace for heating. The heating temperature is 1230℃, and the temperature equalization time is ≥30min. After being discharged from the furnace, rough rolling is carried out. The thickness of the intermediate slab is 40mm, and the rough rolling outlet is 1040℃. Rolling, the final rolling temperature is 820℃, the middle high temperature value of the two-stage cooling process system is 650℃, and the coiling temperature is 530℃, so as to obtain the N80 grade petroleum casing hot continuous rolled steel stri...
Example Embodiment
[0029] Example 3
[0030] The chemical composition is: C0.35wt%, Si0.30wt%, Mn1.80wt%, P0.02wt%, S0.005wt%, Nb0.050wt%, Cr0.50wt%, Ti0.020wt%, the rest are Fe and non For the steel with avoided impurities, the continuous casting billet production is completed according to the steelmaking process route of "full three removal" smelting, LF refining, and slab casting to obtain a cast billet with a thickness of 235mm.
[0031] Then the cast slab is subjected to surface flame cleaning, and then sent to a heating furnace for heating. The heating temperature is 1220℃, the temperature equalization time is ≥30min, and the rough rolling is carried out after being discharged. The thickness of the intermediate slab is 42mm, and the rough rolling outlet is 1060℃. Rolling, the final rolling temperature is 840℃, the middle high temperature value of the two-stage cooling process system is 680℃, and the coiling temperature is 560℃, so as to produce N80 grade petroleum casing hot continuous rolled s...
PUM
Property | Measurement | Unit |
---|---|---|
Yield strength | aaaaa | aaaaa |
Tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap