A kind of water-based coating containing high hydroxyl methyl etherified melamine resin and preparation method thereof

A technology of high hydroxy methyl etherified melamine and melamine, applied in the direction of coating, etc., can solve the problems of high baking temperature of methyl etherified melamine resin, unable to use water-based paint, high energy consumption, etc., to prevent corruption and demulsification, improve Water separation tendency, the effect of improving the overall performance

Active Publication Date: 2016-04-27
SHANDONG ZHANHUA OSITER CHEM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to the existing preparation process, the prepared methyl etherified melamine resin has high baking temperature, high energy consumption, and low compatibility with water, so it cannot be used for water-based coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based coating containing high hydroxyl methyl etherified melamine resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The high hydroxyl methyl etherified melamine resin comprises the following raw materials: melamine, formaldehyde solution, methanol and formic acid, wherein the weight ratio of melamine, formaldehyde solution and methanol is 2:8:12; the weight ratio of formic acid and melamine is 1 :5.

[0015] The preparation method of the high-hydroxy methyl etherified melamine resin comprises the following steps: first, mix melamine and formaldehyde aqueous solution in proportion, adjust the pH to 9.5 with NaOH solution, heat up to 65°C, and keep warm for 90 minutes; then add in proportion Methanol, then add formic acid according to the ratio of formic acid: melamine weight ratio of 1:5, keep warm for etherification reaction at 50°C for 60 minutes, add NaOH solution to adjust the pH to 9.0, and finally dealcoholize and dehydrate under negative pressure, filter to obtain the resin finished product.

Embodiment 2

[0017] The high hydroxyl methyl etherified melamine resin comprises the following raw materials: melamine, formaldehyde solution, methanol and formic acid, wherein the weight ratio of melamine, formaldehyde solution and methanol is 2:10:15; the weight ratio of formic acid and melamine is 1 :5.

[0018] The preparation method of the high-hydroxy methyl etherified melamine resin comprises the following steps: first, mix melamine and formaldehyde aqueous solution in proportion, adjust the pH to 9.0 with NaOH solution, heat up to 70°C, and keep warm for 90 minutes; then add in proportion Methanol, then add formic acid according to the ratio of formic acid: melamine weight ratio of 1:5, keep warm for etherification reaction at 45°C for 60 minutes, add NaOH solution to adjust the pH to 9.0, and finally dealcoholize and dehydrate under negative pressure, filter to obtain the resin finished product.

Embodiment 3

[0020] The high hydroxyl methyl etherified melamine resin comprises the following raw materials: melamine, formaldehyde solution, methanol and formic acid, wherein the weight ratio of melamine, formaldehyde solution and methanol is 3:11:20; the weight ratio of formic acid and melamine is 1 :5.

[0021] The preparation method of the high-hydroxy methyl etherified melamine resin comprises the following steps: first, mix melamine and formaldehyde aqueous solution in proportion, adjust the pH to 8.5 with NaOH solution, heat up to 75°C, and keep warm for 90 minutes; then add in proportion Methanol, then add formic acid according to the ratio of formic acid: melamine weight ratio of 1:5, keep warm at 40°C for etherification reaction for 60 minutes, add NaOH solution to adjust the pH to 9.0, and finally dealcoholize and dehydrate under negative pressure, filter to obtain the resin finished product.

[0022] Embodiment 1, embodiment 2, embodiment 3 compare the following table with th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of paint, and particularly relates to a water-based paint containing high-hydroxyl methylated melamine resin and a preparation method thereof. The paint containing high-hydroxyl methylated melamine resin comprises the following raw materials: water, ethylene glycol, ultrafine aluminum silicate, titanium dioxide, kaolin and high-hydroxyl methylated melamine resin. By adding the high-hydroxyl methylated melamine resin into the paint, the medium and shear viscosity is greatly improved, the water distribution trend of the paint is improved, and the storage period of the paint is prolonged.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a water-based coating containing high-hydroxy methyl etherified melamine resin and a preparation method thereof. Background technique [0002] Coatings are widely used in the field of construction and home decoration. With the improvement of people's living standards, the requirements for the use and quality of coatings have been greatly increased, and the properties of coatings such as viscosity and water separation tendency directly affect the overall quality of coatings. Methylated melamine resin is a high-efficiency crosslinking agent for epoxy resin, alkyd resin, ester resin and acrylic resin. It can be used in oily coatings and can be well dissolved in alkyd resin and acrylic resin to make top-level baking paint. It is used in solvent-based decorative coatings, coil coatings, powder coatings, can coatings, high-solid coatings, and can also be used in ink indust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D161/32C09D7/12C08G12/42
Inventor 鲍志明胡晓川徐庆平
Owner SHANDONG ZHANHUA OSITER CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com