Corrosion-proof ice-covering-proof coating

An anti-icing and anti-corrosion technology, applied in anti-corrosion coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., to achieve good adhesion

Inactive Publication Date: 2014-05-14
南通新昱化工有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A kind of anti-corrosion and anti-icing coating for oil rod drill pipe. At present, there is no special anti-corrosion and anti-icing coating on the market, which can meet the working conditions of oil rod drill pipe. Impact resistance, acid and alkali resistance, but also anti-icing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Take the following recipe:

[0015] Table 1

[0016] materials Mass percentage / % Bisphenol A epoxy resin E14 20 PTFE resin 10 nano silicon oxide 24 polyamide resin 10 toughened resin 1 Titanium dioxide mixture 5 Fluorine-containing acrylate modified polyurethane resin 25 methyl ethyl ketone 5

[0017] An anti-corrosion and anti-icing coating for the prepared oil rod and drill pipe is applied by brushing, wiping, manual roller construction, air spray gun or airless spray gun spray, electrostatic spray, thermal spray, roller coating or dip coating, etc. The conventional construction method is applied to the oil rod drill pipe, and its performance is shown in Table 2.

[0018] Table 2

[0019] project Require result state in container before / after stirring No hard lumps / homogeneous state Construction brush two coats barrier free Coating Appearance Crack resistance no c...

Embodiment 2

[0021] Take the following recipe:

[0022] table 3

[0023] materials Mass percentage / % Bisphenol A epoxy resin E03 15 PTFE resin 12 nano silicon oxide 20 Phenolic Resin 15 toughened resin 3 Titanium dioxide mixture 10 Fluorine-containing acrylate modified polyurethane resin 15 ethyl acetate 10

[0024] An anti-corrosion and anti-icing coating for the prepared oil rod and drill pipe is applied by brushing, wiping, manual roller construction, air spray gun or airless spray gun spray, electrostatic spray, thermal spray, roller coating or dip coating, etc. The conventional construction method is applied to the oil rod drill pipe, and its performance is shown in Table 4.

[0025] Table 4

[0026] project Require result state in container before / after stirring No hard lumps / homogeneous state Construction brush two coats barrier free Coating Appearance Crack resistance no crack ...

Embodiment 3

[0028] Take the following recipe:

[0029] table 5

[0030] materials Mass percentage / % Bisphenol A epoxy resin E42 20 PTFE resin 10 nano silicon oxide 24 Phenolic Resin 10 toughened resin 1 Titanium dioxide mixture 5 Fluorine-containing acrylate modified polyurethane resin 25 Ethylene glycol ether acetate 5

[0031] An anti-corrosion and anti-icing coating for the prepared oil rod and drill pipe is applied by brushing, wiping, manual roller construction, air spray gun or airless spray gun spray, electrostatic spray, thermal spray, roller coating or dip coating, etc. The conventional construction method is applied to the oil rod drill pipe, and its performance is shown in Table 6.

[0032] Table 6

[0033] project Require result state in container before / after stirring No hard lumps / homogeneous state Construction brush two coats barrier free Coating Appearance Crack resistan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of corrosion-proof ice-covering-proof coatings, and particularly relates to a corrosion-proof ice-covering-proof coating. The corrosion-proof ice-covering-proof coating comprises the following components in percentage by weight: 15%-30% of epoxy resin, 10%-15% of fluoroolefin resin, 15%-40% of nanometer silicon oxide, 10%-20% of solidifying agents, 1%-5% of toughening resin, 5%-10% of titanium dioxide blending agents, 15%-30% of fluorinated acrylate modified polyurethane resin and 5%-15% of organic solvents, wherein each titanium dioxide blending agent comprises polyurethane, biuret, polyester J4, butyl alcohol, ethanol ethyl ester, petroleum type dimethyl benzene, titanium dioxide, fine particle calcium carbonate, talcum powder, sodium pentachlorophenate and tri-butyl alcohol, and the weight ratio of polyurethane to biuret to polyester J4 to butyl alcohol to ethanol ethyl ester to petroleum type dimethyl benzene to titanium dioxide to fine particle calcium carbonate to talcum powder to sodium pentachlorophenate to tri-butyl alcohol is (1.5-2.5):(1-2):(1.5-2):(1.5-2):(1-1.5):(2-2.5):(1.5-2):(1-2):(1-1.5):(0.1-0.3):(0.3-0.5). The corrosion-proof ice-covering-proof coating disclosed by the invention has good adhesive force, can meet the requirements for use conditions of an oil drill rod in a using process in a cold place, and has the advantages of acid resistance, alkali resistance, corrosion proofing and ice-covering proofing.

Description

technical field [0001] The invention relates to the field of anti-corrosion and anti-icing coatings, in particular to an anti-corrosion and anti-icing coating. Background technique [0002] Paint is a chemical mixture that can firmly cover the surface of an object for protection, decoration, marking and other special purposes. It is an anti-corrosion and anti-icing coating. An authoritative book "An Anti-corrosion and Anti-icing Coating Technology" in the field of anti-corrosion and anti-icing coating in China is defined as follows: "An anti-corrosion and anti-icing coating is a kind of material. The material can be coated on the surface of the object by different construction techniques to form a solid film with firm adhesion, certain strength and continuity. The film formed in this way is commonly called a coating film, also known as a paint film or a coating." Belongs to organic chemical polymer materials , the formed coating film belongs to the polymer compound type. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D127/12C09D127/18C09D175/04C09D5/08C09D7/12
Inventor 蒋灿
Owner 南通新昱化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap