Roller device and process for continuous casting round billet rolling in two-roller reversing mill

A continuous casting round billet and roll device technology, applied in the direction of rolls, metal rolling, manufacturing tools, etc., can solve the problems of insufficient yield, limited billet size, low production efficiency, etc., to achieve good product quality and performance, and finished products The effect of high dimensional accuracy and high product dimensional accuracy

Active Publication Date: 2016-06-01
HUATIAN ENG & TECH CORP MCC
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Two-roll reversible rolling mills generally use steel ingots and continuous casting billets to produce large-size square and round steel. The production of steel ingots has problems such as low production efficiency, large quality differences, high energy consumption and high production costs. Due to the limitation of the continuous casting radius of the continuous casting machine, billets The size is limited, the compression ratio cannot meet the requirements, and corner cracks and component segregation are prone to occur due to uneven cooling during the production process
[0003] However, after the large-scale continuous casting round billet is rolled, the cross-sectional shape of the rolled piece is in the shape of a "drum" (such as figure 1 As shown), the end area of ​​the rolled piece is wider than the middle part, showing a "shovel" shape. After turning over, rolling on the two-roll reversing rolling mill is prone to falling off the square or even falling off the steel, which greatly affects the yield. Due to the problem of pass design in some steel mills, the yield is less than 40%.
However, in order to prevent the rolling parts from falling out and falling steel, the current pass design generally adopts the method of reducing the amount of reduction in the pass, and this leads to insufficient deformation of the coarse as-cast structure, which affects the grain size of the product. and organizational structure, ultimately making the quality of the product unable to be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roller device and process for continuous casting round billet rolling in two-roller reversing mill
  • Roller device and process for continuous casting round billet rolling in two-roller reversing mill
  • Roller device and process for continuous casting round billet rolling in two-roller reversing mill

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Such as figure 2 As shown, this embodiment describes the pass design and rolling process for producing 200X200 and 150X150 square steel by using Φ380mm continuous casting round billet. The complete process is: billet-heating-high-pressure water dephosphorization-transition pass 11 Rolling - two-roll reversible mill front turning steel hook turning steel - support pass 12 rolling - two roller reversing mill front turning steel hook turning steel - finished product front pass 13 rolling - two roller reversing mill front turning steel hook turning steel - Finished pass rolling - cut to length - cooling - finishing - storage. The material of the billet in this embodiment is 42CrMo, the diameter of the roll used is 1150mm, the length of the roll body is 2600mm, the speed of the roll is 0-50 / 120rpm, and the rolling temperature of the billet is 1150°C. Each pass on the roll is arranged with 7 slots according to the length of the roll body, two 200X200 and 150X150 finished sl...

Embodiment 2

[0050] Such as image 3 As shown, this embodiment describes the pass design and rolling process for producing 270X270 and 220X220 square steel by using Φ500mm continuous casting round billet. The complete process is: billet-heating-high-pressure water dephosphorization-transition pass 21 Rolling-Two-roll reversible rolling mill Front turning steel hook turning steel-Supporting pass 22 Rolling-Two-roll reversing rolling mill Front turning steel hook turning steel-Transition pass 21 Rolling-Two-roll reversing mill Front turning steel hook turning steel- Finished pass rolling - cut to length - cooling - finishing - storage. The material of the billet in this embodiment is 40Cr, the diameter of the roll used is 1150 mm, the length of the roll body is 2600 mm, the speed of the roll is 0-50 / 120 rpm, and the rolling temperature of the billet is 1150°C. According to the length of the roll body, 6 slots are arranged on the roll, two 270X270 and 220X220 square steel finished slots, and...

Embodiment 3

[0065] Such as Figure 4 As shown, this embodiment describes the pass design and rolling process for producing 320X320 and 270X270 square steel using Φ600mm continuous casting round billet. The complete process is: billet-heating-high-pressure water dephosphorization-transition pass 31 Rolling-Two-roll reversible rolling mill Front turning steel hook turning steel-Support pass 32 Rolling-Two-roll reversing rolling mill Front turning steel hook turning steel-Front pass rolling of finished product-Two-roll reversing mill Front turning steel hook turning steel- Finished pass rolling - cut to length - cooling - finishing - storage. The material of the billet in this embodiment is 40Cr, the diameter of the roll used is 1150 mm, the length of the roll body is 2600 mm, the speed of the roll is 0-50 / 120 rpm, and the rolling temperature of the billet is 1150°C. According to the length of the roll body, there are 5 hole grooves arranged on the roll, two 320X320 finished grooves, and on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a two-roller reversible mill roller device and technology using continuous casting round billets for carrying out rolling production. Four types of hole patterns including a transition hole pattern, a supporting hole pattern, a before-finished-product hole pattern and a finished product hole pattern are designed on a pair of rollers. The rolling technology comprises the steps of using the transition hole pattern (1) for rolling the continuous casting round billets, and turning over steel after rolling is accomplished, wherein the rolling reduction ranges from 40 mm to 90 mm per pass; using the supporting hole pattern for continuously rolling the drum-shaped rolled pieces obtained in the previous step to obtain rectangular or square rolled pieces which have regular shapes, and turning over the steel after rolling is accomplished, wherein the rolling reduction ranges from 40 mm 90 mm per pass; using the before-finished-product hole pattern (3) for rolling the rolled pieces to obtain rectangular or oval rolled pieces with reserved rolling reduction and reserved broadening quantity, and turning over the steel billets after rolling is accomplished, wherein the rolling reduction ranges from 20 mm to 90 mm per pass; using the finished product hole pattern for rolling one pass to obtain rolled pieces which are high in dimensional accuracy and product quality, wherein the rolling reduction of square or rectangular steel finished products ranges from 40 mm to 60 mm per pass, and the nominal rolling reduction of round steel ranges from 10 mm to 40 mm per pass.

Description

technical field [0001] The invention relates to the technical field of steel rolling process, in particular to a roll device and process produced by rolling a continuous casting round billet in a two-roll reversing rolling mill. Background technique [0002] Two-roll reversible rolling mills generally use steel ingots and continuous casting billets to produce large-size square and round steel. The production of steel ingots has problems such as low production efficiency, large quality differences, high energy consumption and high production costs. Due to the limitation of the continuous casting radius of the continuous casting machine, billets The size is limited, the compression ratio cannot meet the requirements, and corner cracks and component segregation are prone to occur due to uneven cooling during the production process. The above-mentioned problems can be solved by rolling large-section continuous casting round billets. Therefore, large-scale square and round steel ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B27/02B21B1/00
Inventor 陈志强卢勇张景旺徐勇朱庆年芦强夏兴进潘帆
Owner HUATIAN ENG & TECH CORP MCC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products