Rapid construction highway repair material and preparation method and application method thereof

A technology for repairing materials and roads, applied in the field of pavement repairing materials, can solve the problems of high temperature requirements for on-site construction and cumbersome construction technology, and achieve the effects of simplifying construction technology, wide application prospects, and strong practicability.

Inactive Publication Date: 2014-08-13
新疆交通科学研究院有限责任公司
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a rapid construction road repair material and its preparation method and use method, which overcomes the above-mentioned deficiencies in the prior art, and can effectively solve the problem of existing road repair In the process of repairing the pavement, there are problems of cumbersome construction technology and high temperature requirements for on-site construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, this rapid construction road repairing material, raw material counts by weight fraction, and raw material comprises the epoxy resin of 22 to 33 parts, the dibutyl phthalate of 2 to 5 parts, the ethyl phthalate of 10 to 20 parts Diamine, 2 to 5 parts of acetone, 40 to 60 parts of filler, fast construction road repair material is obtained according to the following preparation method: first step, heat the required amount of epoxy resin to 14 ° C to 65 ° C , add the required amount of dibutyl phthalate to the heated epoxy resin and stir evenly to obtain a stirring liquid, the stirring time is 30 seconds to 60 seconds; the second step is to add the required amount of dibutyl phthalate to the primary stirring liquid The required amount of acetone is stirred evenly to obtain the secondary stirring liquid, and the stirring time is 45 seconds to 60 seconds; the third step is to add the required amount of filler to the secondary stirring liquid and stir evenly to ...

Embodiment 2

[0021] Embodiment 2, this rapid construction road repairing material, raw material is counted by weight fraction, and raw material comprises the epoxy resin of 22 parts or 33 parts, the dibutyl phthalate of 2 parts or 5 parts, the ethyl phthalate of 10 parts or 20 parts Diamine, 2 or 5 parts of acetone, 40 or 60 parts of filler, rapid construction road repair material is obtained according to the following preparation method: the first step, heat the required amount of epoxy resin to 14 ° C or 65 ° C , add the required amount of dibutyl phthalate to the heated epoxy resin and stir evenly to obtain a stirring liquid, the stirring time is 30 seconds or 60 seconds; the second step is to add the required amount of dibutyl phthalate to the primary stirring liquid The required amount of acetone is stirred evenly to obtain the secondary stirring liquid, and the stirring time is 45 seconds or 60 seconds; the third step is to add the required amount of filler to the secondary stirring...

Embodiment 3

[0022] Embodiment 3, as an optimization of the above embodiment, the epoxy resin is WSR6101 type epoxy resin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of pavement repair material, and provides a rapid construction highway repair material and a preparation method and application method thereof. The rapid construction highway repair material is obtained according to the following steps: adding a required amount of dibutyl phthalate, acetone, a filling material and ethene diamine in order into heated to epoxy resin, and mixing evenly to obtain the rapid construction highway repair material. The rapid construction highway repair material provided by the invention not only has the compressive strength and flexural strength of an ordinary cement concrete, but also has the advantages of short forming time and low spreading temperature, so as to reduce the construction temperature requirement and simplify the construction process. Therefore, the rapid construction highway repair material provided by the invention has higher practicability, allows usage of the highway as soon as possible, realizes full performance of usage efficiency of the highway, and shows wide application prospect.

Description

technical field [0001] The invention relates to the technical field of road surface repair materials, and relates to a rapid construction road repair material and its preparation method and use method. Background technique [0002] Highway construction is the country's basic industry and the leading industry of economic development. During the long-term use of highways, due to temperature changes, shrinkage and creep of pavement materials, loads and freeze-thaw factors, traffic lanes (highways) often varying degrees of damage. The degree of damage to the expressway is even more serious. Therefore, how to quickly and timely carry out maintenance under the condition of ensuring vehicle traffic, how to open the passage as soon as possible, give full play to the use efficiency of the expressway, extend the service life, and improve the quality of road maintenance and repair It will be a new challenge in the process of expressway development. At present, pavement repair materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/28E01C19/48
Inventor 杨三强许文辉刘涛
Owner 新疆交通科学研究院有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com