Environment-friendly propylene pigment containing tea stalk powder and preparation thereof

A technology of acrylic paint and tea stalk powder, applied in the field of art pigments, can solve the problems of low utilization rate of tea stalks, poor physical stability of pigments, etc., and achieve the effects of improving utilization value, low utilization rate and significant economic benefits

Active Publication Date: 2014-08-20
福建春伦集团有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of environment-friendly acrylic paint containing tea stem powder and its preparation for the shortcomings of low tea stem utilization rate and poor physical stability of pigments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of environment-friendly acrylic paint containing tea stalk powder, comprising agent A and agent B; calculated in parts by mass,

[0025] Agent A: 8 parts of hydroxypropyl methylcellulose, 10 parts of gum arabic, 10 parts of water, 15 parts of tea stem powder, 55 parts of polyacrylic acid emulsion, 2 parts of dispersant, 5 parts of pigment powder, JSA-206 water-based wetting 6 parts of agent, 3 parts of sodium benzoate;

[0026] Agent B: 40 parts of acrylic resin, 5 parts of hydroxypropyl methylcellulose, 10 parts of distilled water, 2 parts of dispersant, 3 parts of defoamer, 2 parts of sodium benzoate, 2 parts of filler, and 2 parts of wetting agent.

[0027] Tea stalk powder is made by pulverizing tea stalks with a ball mill and passing through a 1000-1200 mesh sieve.

[0028] The preparation method of the environment-friendly acrylic paint containing tea stalk powder is specifically:

[0029] (1) Preparation of agent A: first mix hydroxypropyl methylcellulos...

Embodiment 2

[0033] A kind of environment-friendly acrylic paint containing tea stalk powder, comprising agent A and agent B; calculated in parts by mass,

[0034] Agent A: 10 parts of thickener, 7 parts of gum arabic, 12 parts of water, 12 parts of tea stem powder, 52 parts of polyacrylic acid emulsion, 2 parts of dispersant, 7 parts of pigment powder, 10 parts of propylene glycol, 5 parts of benzoic acid;

[0035] Agent B: 50 parts of acrylic resin, 2 parts of sodium carboxymethylcellulose, 12 parts of distilled water, 3 parts of dispersant, 5 parts of defoamer, 3 parts of benzoic acid, 5 parts of filler, and 4 parts of wetting agent.

[0036] A method for preparing the above-mentioned environment-friendly acrylic paint containing tea stalk powder, specifically:

[0037] (1) Preparation of agent A: first mix the thickener and gum arabic evenly, add water, and swell for 5 hours; heat to a temperature of 70°C for 10 minutes to prepare an adhesive glue; then Wetting agent and tea stalk pow...

Embodiment 3

[0041] A kind of environment-friendly acrylic paint containing tea stalk powder, comprising agent A and agent B; calculated in parts by mass,

[0042] Agent A: 11 parts of thickener, 5 parts of gum arabic, 15 parts of water, 10 parts of tea stem powder, 50 parts of polyacrylic acid emulsion, 2 parts of dispersant, 8 parts of pigment powder, 4 parts of glycerin, 4 parts of sodium benzoate;

[0043] Agent B: 55 parts of acrylic resin, 5 parts of hydroxyethyl cellulose, 15 parts of distilled water, 4 parts of dispersant, 8 parts of defoamer, 3 parts of sodium benzoate, 3 parts of filler, and 5 parts of wetting agent.

[0044] A method for preparing the above-mentioned environment-friendly acrylic paint containing tea stalk powder, specifically:

[0045] (1) Preparation of agent A: first mix the thickener and gum arabic evenly, add water, and swell for 4 hours; heat to 65°C for 15 minutes to prepare the adhesive glue; then Wetting agent and tea stalk powder were mixed for 10 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly propylene pigment containing tea stalk powder. The propylene pigment comprises an agent A and an agent B, wherein the agent A comprises a thickener, Arabic gum, water, the tea stalk powder, polyacrylic emulsion, a dispersant, pigment powder, a wetting agent and a preservative; and the agent B comprises acrylic resin, a thickener, distilled water, a dispersant, a defoaming agent, a preservative, a filler and a wetting agent. After the agent A is used for 3-5d, the agent B is sprayed to the surface of the agent A, so that the color of the pigment can be effectively protected, the pigment is unlikely to fade, weather-resistant and pollution-free, the original color of the pigment is not changed, and the color fullness of the pigment is improved. Tea polyphenol in tea stalks can react with harmful gases such as formaldehyde and dimethyl benzene to form non-volatile harmless high molecular chain matters, so that the harmful gases in air are effectively cleared. However, the utilization rate of the tea stalks is low at present, so that great resource waste is produced. The tea stalk powder is added in the pigment, so that the utilization rate of the tea stalks is improved, and the prepared pigment is environment-friendly and pollution-free.

Description

Technical field [0001] The present invention is the field of art for art, and it involves an environmentally friendly acrylonitrite pigment and preparation of tea -containing powder. Background technique [0002] Tea stalks refer to the leaf stalks of tea.For a long time, people have no habit of drinking tea.A large number of tea stalks were thrown away, and the utilization rate was very low.In fact, tea stalks contain a considerable amount of aroma and have many uses.For example, the tea stalk contains aromatic substances to promote sleep, improve the quality of sleep, calm the mind, eliminate brain fatigue, and relieve tension pressure; contain tannins, phenol, and organic acids, which have the functions of sterilization and anti -inflammatory.Therefore, more and more people fill the tea stalks in the pillow core and make a tea pillow.The tea polyphenols in the tea stalk can react with harmful gases such as formaldehyde and dysrene, forming an unacceptable harmless polymer chai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/06C09D133/00C09D105/00C09D197/02C09D7/12
Inventor 傅伟鸿
Owner 福建春伦集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com