Regenerated cellulose fiber containing microencapsulated anti-mite medicine and preparation method thereof

A technology of regenerated cellulose and microencapsulation, which is applied in the field of textile production to achieve the effect of good persistence and cool and fragrant smell

Active Publication Date: 2014-08-27
JIANGSU GOLDSUN TEXTILE SCI & TECH
View PDF14 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After literature search, there is no such thing as adding borneol, which has the triple effects of health care, repelling mites, and antibacterial, into cellulose spinning solution as an anti-mite drug to spin regenerated cellulose fibers that have anti-mite function and have no toxic side effects on the human body. Technology and Products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Regenerated cellulose fiber containing microencapsulated anti-mite medicine and preparation method thereof
  • Regenerated cellulose fiber containing microencapsulated anti-mite medicine and preparation method thereof
  • Regenerated cellulose fiber containing microencapsulated anti-mite medicine and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The 99% purity borneol extract from the natural plant dipterocarp was dissolved in wormwood essential oil to prepare borneol-wormwood essential oil with a mass concentration of borneol of 5%.

[0027] In parts by weight, get 2 parts of toluene diisocyanate and 4 parts of borneol-wormwood essential oil solution and mix uniformly to form an oil phase, put this oil phase into 10 parts of water containing wt1% emulsifier polyvinyl alcohol (Mw1500), and use high-speed emulsification Machine emulsification, rotating speed 9200-9600r / min, emulsification 5min, get oil-in-water emulsion. To make the emulsion stable, add 10 parts of aqueous solution containing wt0.13% dispersant sodium alginate, add 4.6 parts of polyethylene glycol (Mw400-600) and 1% catalyst dibutyltin dilaurate at the same time, stir at room temperature for 2 hour, then the temperature was raised to 70°C, the chain extender ethylenediamine was added, and the stirring was continued for 1 hour to cure the wall ma...

Embodiment 2

[0032] The synthetic borneol with a purity of 98% was dissolved in wormwood essential oil to prepare borneol-wormwood essential oil with a mass concentration of borneol of 10%.

[0033] In parts by weight, get 5 parts of toluene diisocyanate and 5 parts of borneol-wormwood essential oil solution and mix uniformly to form an oil phase, put this oil phase into 12 parts of water containing wt1.2% emulsifier polyvinyl alcohol (Mw1500), use Emulsify with a high-speed emulsifier at a speed of 9200-9600r / min for 5 minutes to obtain an oil-in-water emulsion. To make the emulsion stable, add 10 parts of aqueous solution containing wt0.15% dispersant sodium alginate, add 5.4 parts of polyethylene glycol (Mw400-600) and 1% catalyst dibutyltin dilaurate at the same time, stir at room temperature for 2 hour, then the temperature was raised to 70°C, the chain extender ethylenediamine was added, and the stirring was continued for 1 hour to cure the wall material. The obtained slurry is rins...

Embodiment 3

[0038] The 99% purity borneol extract from the natural plant dipterocarp was dissolved in wormwood essential oil to prepare borneol-wormwood essential oil with a mass concentration of borneol of 5%.

[0039] In parts by weight, get 2 parts of toluene diisocyanate and 4 parts of borneol-wormwood essential oil solution and mix uniformly to form an oil phase, put this oil phase into 10 parts of water containing wt1% emulsifier polyvinyl alcohol (Mw1500), and use high-speed emulsification Machine emulsification, rotating speed 9200-9600r / min, emulsification 5min, get oil-in-water emulsion. To make the emulsion stable, add 10 parts of aqueous solution containing wt0.13% dispersant sodium alginate, add 4.6 parts of polyethylene glycol (Mw400-600) and 1% catalyst dibutyltin dilaurate at the same time, stir at room temperature for 2 hour, then the temperature was raised to 70°C, the chain extender ethylenediamine was added, and the stirring was continued for 1 hour to cure the wall ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides regenerated cellulose fiber containing a microencapsulated anti-mite medicine and a preparation method thereof. The regenerated cellulose fiber comprises a viscose-rayon spinning solution and the microencapsulated anti-mite medicine, the microencapsulated anti-mite medicine accounts for 0.05-2% by mass of methyl cellulose in the viscose-rayon spinning solution, methyl cellulose accounts for 99.95-98% by mass of dry regenerated cellulose fiber, and borneol and argy wormwood essential oil are taken as a capsule core. The preparation method comprises: firstly preparing a solution of borneol and argy wormwood essential oil, then preparing microcapsules from the solution of borneol and argy wormwood essential oil through a microencapsulation technology, adding the microcapsules into the viscose-rayon spinning solution, mixing uniformly, and finally utilizing a viscose-rayon wet spinning technology to prepare the regenerated cellulose fiber containing the microencapsulated anti-mite medicine. The regenerated cellulose fiber containing microencapsulated anti-mite medicine has the repelling rate on dermatophagoides farina of 95% or more, and has extremely strong anti-mite effect, and has the antibacterial rate on staphylococcus aureus, escherichia coli and other pathogens of 90% or more.

Description

technical field [0001] The invention belongs to the technical field of textile production, and in particular relates to a regenerated cellulose fiber containing microencapsulated anti-mite medicine and a preparation method thereof. Background technique [0002] Mites are small arthropods with a body length of usually 0.1-0.5 mm. The harm to the human body is mainly reflected in parasitism, stinging, poisonous stings, blood-sucking, allergic diseases, and spreading diseases. It can cause asthma, rhinitis, and dermatitis , tinea corporis and other diseases have caused serious harm to human health. [0003] Natural borneol is a crystal extracted from the resin and volatile oil of dipterocarp, an arbor plant of Dipterocarpaceae, also known as "borneol" or "plum slice", which is a nearly pure D-triterpene compound. The isomer synthesized by chemical methods is "synthetic borneol", and its quality standard should meet the requirements of the Chinese Pharmacopoeia. Borneol, hard ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08D01D5/06
Inventor 毛军陈红霞陆鹏丁可敬
Owner JIANGSU GOLDSUN TEXTILE SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com