Rustproof wax water emulsion for automobile chassis
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of automobile chassis and anti-rust wax, which is applied in the direction of wax coating, anti-corrosion coating, coating, etc., and can solve the problems of endangering the health of operators and high cost
Inactive Publication Date: 2014-09-03
JINAN ROSEWEL NEW BUILDING MATERIALS
View PDF2 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] At present, the existing anti-rust wax for automobile chassis (CN02115915.7, CN201110034909.5) is solvent-based and contains a relatively large proportion (40%
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] An automobile chassis antirust wax-water emulsion is characterized in that the preparation steps are as follows:
[0013] ① Put 120 kg of 80# microcrystalline wax in a 2000L stainless steel reaction kettle (outer cover insulation layer), heat to 80°C, stir at 80 rpm for 10 minutes until the paraffin is completely melted.
[0014] ② Add 60 kg of petroleum resin while stirring, stop heating when the temperature rises to 100°C, and continue stirring for 10 minutes until the petroleum resin is completely dissolved.
[0015] ③ Add 40 kg of higher fatty acid, stir to dissolve completely, and continue to stir until the temperature drops to 90°C;
[0016] ④Take 16 kg of triethanolamine, dissolve it in 85°C hot water, add it into the reaction kettle under stirring conditions, and continue to add 85°C hot water at the same time, and continue stirring until the temperature drops below 50°C.
[0017] ⑤ Take 0.5kg of metal corrosion inhibitor, dissolve it in 5 kg of wa...
Embodiment 2
[0019] An automobile chassis antirust wax-water emulsion is characterized in that the preparation steps are as follows:
[0020] ① Put 160 kg of 80# microcrystalline wax in a 2000L stainless steel reaction kettle (outer cover insulation layer), heat to 90°C, stir at 100 rpm for 15 minutes until the paraffin wax is completely melted.
[0021] ② Add 80 kg of petroleum resin while stirring, stop heating when the temperature rises to 120°C, and continue stirring for 15 minutes until the petroleum resin is completely dissolved.
[0022] ③ Add 50 kg of higher fatty acid, stir to dissolve completely, and continue to stir until the temperature drops to 100°C;
[0023] ④Take 20 kg of triethanolamine, dissolve it in 95°C hot water, add it into the reaction kettle under stirring, and continue to add 95°C hot water at the same time, and continue stirring until the temperature drops below 50°C.
[0024] ⑤Take 1.5 kg of metal corrosion inhibitor, dissolve it in 5 kg of warm...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a rustproof wax water emulsion for an automobile chassis. The rustproof wax water emulsion is prepared by using an emulsification technology through the specific steps that microcrystalline wax and petroleum resins in a certain proportion are heated to be 100-120 DEG C for melting; a composite emulsifying agent is added and fully stirred; the temperature is reduced to be 90 DEG C; hot water with the temperature of 85-95 DEG C is continuously added and continuously stirred for 30 minutes at constant temperature so as to prepare composite paraffin emulsion; the composite paraffin emulsion is cooled to be below 50 DEG C; 0.05-0.15 percent of corrosion inhibitor solutions are added and continuously stirred for 10 minutes. Volatile toxic organic solvents are replaced by water, so that the convenience of application is improved, the working environment is improved, and the health of operators is guaranteed; under the premise of guaranteeing the rustproof protection effect, the unit cost is reduced by 40 percent. The rustproof wax water emulsion is milk-white even semitransparent liquid, fine in granularity, moderate in viscosity, good in film-forming property, fast in drying, high in adhesion, and high in hydrothermal resistant property and high in rustproof protection performance.
Description
technical field [0001] The invention relates to an antirust protection liquid for automobile body and chassis, in particular to an antirust wax-water emulsion for automobile chassis. Background technique [0002] At present, the existing anti-rust wax for automobile chassis (CN02115915.7, CN201110034909.5) is solvent-based and contains a relatively large proportion (40%~90%) of volatile organic solvents. During the construction process, toxic gases will be released, which will endanger the health of operators. healthy. And the cost is higher. Contents of the invention [0003] The object of the present invention is to provide a kind of automobile chassis rust-proof wax-water emulsion in order to solve the above problems. [0004] The technical solution of the present invention to achieve the above-mentioned purpose is that an aqueous emulsion of anti-rust wax for automobile chassis adopts emulsification technology to prepare an aqueous emulsion of anti-rust wax, heat a f...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more