Oily titanium ingot high-temperature-oxidation-resistant coating, applications thereof and titanium ingot producing method

A technology for resisting high temperature oxidation and titanium ingots, applied in the field of metal high temperature resistant coatings, can solve problems such as unsatisfactory protection of titanium ingots, and achieve the effects of increasing production costs and production time, improving yield and reducing production costs.

Active Publication Date: 2014-11-26
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defect that the protection of titanium ingots by existing high-temperature protective coatings is not ideal, and to provide a new oily titanium ingot high-temperature oxidation-resistant coating and its application and production method for titanium ingots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oily titanium ingot high-temperature-oxidation-resistant coating, applications thereof and titanium ingot producing method
  • Oily titanium ingot high-temperature-oxidation-resistant coating, applications thereof and titanium ingot producing method
  • Oily titanium ingot high-temperature-oxidation-resistant coating, applications thereof and titanium ingot producing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment is used to illustrate the oily titanium ingot anti-high temperature oxidation coating and the production method of titanium ingot of the present invention.

[0047] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 100g of oily epoxy resin (solid content 50% by weight) and place it in a container;

[0048] (2) Add 5g of polypropylene glycol diglycidyl ether (purchased from Changzhou Mingtai Chemical Technology Co., Ltd., model: 207), and stir evenly;

[0049] (3) Weigh 800g Al powder, 30g Zn powder, 20g Sn powder and 25g Cu powder, and slowly add them into the container under stirring;

[0050] (4) Weigh 1g SiO 2 , add to the container, and stir evenly;

[0051] (5) Weigh 0.5 g of polyvinyl alcohol (purchased from Qingdao Anmao International Trade Co., Ltd., Z-200) into a container, stir until the liquid is in a uniform and stable phase, and obtain oily titanium ingot high temperature oxidation resistant coating A1.

[0052] The solid conte...

Embodiment 2

[0055] This embodiment is used to illustrate the oily titanium ingot anti-high temperature oxidation coating and the production method of titanium ingot of the present invention.

[0056] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 54g of oily epoxy resin (solid content 40% by weight) and place it in a container;

[0057] (2) Add 2.6g propylene oxide butyl ether (purchased from Changzhou Mingtai Chemical Technology Co., Ltd., model: 501), and stir evenly;

[0058] (3) Weigh 800g Al powder, 16g Zn powder, 16g Sn powder and 16g Cu powder, and slowly add them into the container under stirring;

[0059] (4) Weigh 1.7g SiO2 2 , add to the container, and stir evenly;

[0060] (5) Weigh 0.68g of polyvinylpyrrolidone (purchased from Guangzhou Batai Chemical Co., Ltd., PVPK90) into a container, stir until the liquid is in a uniform and stable phase, and obtain oily titanium ingot high temperature oxidation resistant coating A2.

[0061] The solid content of the oily...

Embodiment 3

[0064] This embodiment is used to illustrate the oily titanium ingot anti-high temperature oxidation coating and the production method of titanium ingot of the present invention.

[0065] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 141g of oily epoxy resin (solid content 60% by weight) and place it in a container;

[0066] (2) Add 6.8g of ethylene glycol diglycidyl ether (purchased from Changzhou Mingtai Chemical Technology Co., Ltd., model: 669), and stir evenly;

[0067] (3) Weigh 767g Al powder, 30g Zn powder, 30g Sn powder and 23g Cu powder, slowly add in the container under stirring;

[0068] (4) Weigh 2.55g SiO2 2 , add to the container, and stir evenly;

[0069] (5) Weigh 0.85g polyethylene oxide (purchased from Gongbike New Material Technology (Shanghai) Co., Ltd., PEO-5) into the container, stir until the liquid is in a uniform and stable phase, and obtain an oily titanium ingot anti-high temperature oxidation coating A3.

[0070] The solid conten...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

Oily titanium ingot high-temperature-oxidation-resistant coating is disclosed. The coating is prepared by uniformly mixing a raw material mixture. The raw material mixture comprises an oxidation protective agent and an oily film forming agent. The oxidation protective agent comprises Al powder, Zn powder, Sn powder and Cu powder. The weight ratio of the Al powder, the Zn powder, the Sn powder and the Cu powder is 1:0.01-0.1:0.01-0.1:0.01-0.1. Applications of the coating in titanium ingot production and a titanium ingot producing method are also disclosed. The coating can ensure that surfaces of titanium ingots are not oxidized or cracked after the titanium ingots are disposed at a constant high temperature of 1000 DEG C for 8 h, and largely reduce formation of oxygen dissolving layers. The coating is environmental friendly and simple in preparation process, and can adopt a plurality of coating manners. The titanium ingot producing method has a wide popularization and application prospect in production of titanium plates and titanium tubes.

Description

technical field [0001] The invention relates to the field of metal high-temperature-resistant coatings, in particular to an oily titanium ingot high-temperature oxidation-resistant coating, the application of the oily titanium ingot high-temperature oxidation-resistant coating in the production of titanium ingots, and a production method for titanium ingots. Background technique [0002] Titanium ingots generally undergo annealing treatment during the production process. Annealing is generally carried out at a high temperature of about 900°C. At high temperatures, oxygen will enter the surface of the titanium ingot to form a hard dissolved oxygen layer. The titanium ingot is heated at 900°C for 4 hours. Deep cracks with a depth of about 20mm will appear on the above surface. In order to ensure the subsequent rolling of titanium tubes and the surface quality of hot-rolled titanium plates, it is necessary to cut and grind the titanium ingots during the rolling process to remov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/38C09D163/00C09D175/04C09D133/00C09D167/08C21D1/68
Inventor 许哲峰王莹彭琳肖聪李军
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com