Quick-drying high-temperature-resistant undercoat used for steel, and preparation method thereof

A technology of high temperature resistance and primer, applied in coatings, epoxy resin coatings, etc., can solve the problems of operator health hazards, reduce equipment life, poor high temperature resistance, etc., to improve physical and mechanical properties, eliminate air bubbles, etc. , the effect of improving gloss

Inactive Publication Date: 2014-12-24
JIANGSU MARINE VICTORY COATING
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many types of primers on the market, but they generally have the defects of slow drying, poor corrosion resistance, and poor high temperature resistance, which not only reduces the service life of the equipment, increases costs, but also leads to low work efficiency due to long drying time, and It is easy to emit chemical odor during processing, which will bring harm to the health of operators

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-drying high-temperature-resistant undercoat used for steel, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The present embodiment provides a quick-drying high-temperature-resistant primer for steel, which is composed of bisphenol F type liquid epoxy resin, iron red powder, titanium dioxide, defoamer, flame retardant, mica, multifunctional auxiliary Agent AMP-95, graphite powder and water-based acrylic resin, its weight percent composition is: bisphenol F type liquid epoxy resin: 26%, iron red powder: 6.5%, titanium dioxide: 11%, defoamer: 8%, Flame retardant: 5.5%, mica: 3.2%, multifunctional additive AMP-95: 8%, graphite powder: 12.2%, and the balance is water-based acrylic resin; the preparation method of the quick-drying high-temperature resistant primer for steel Follow these steps:

[0033] Step (1): first put the water-based acrylic resin and bisphenol F liquid epoxy resin into the stirring tank for mixing, control the temperature in the stirring tank at 65°C, set the stirring speed at 950r / min, and stir for 2 hours. Then put in titanium dioxide and continue to stir, ...

Embodiment 2

[0038]The present embodiment provides a quick-drying high-temperature-resistant primer for steel, which is composed of bisphenol F type liquid epoxy resin, iron red powder, titanium dioxide, defoamer, flame retardant, mica, multifunctional auxiliary Agent AMP-95, graphite powder and water-based acrylic resin, its weight percent composition is: bisphenol F type liquid epoxy resin: 28%, iron red powder: 6.8%, titanium dioxide: 13%, defoamer: 10%, Flame retardant: 5.8%, mica: 3.8%, multifunctional additive AMP-95: 12%, graphite powder: 12.5%, and the balance is water-based acrylic resin; the preparation method of the quick-drying high-temperature resistant primer for steel Follow these steps:

[0039] Step (1): First put the water-based acrylic resin and bisphenol F liquid epoxy resin into the stirring tank for mixing, control the temperature in the stirring tank at 66°C, set the stirring speed at 955r / min, and stir for 2.6 hours , and then put in titanium dioxide and continue s...

Embodiment 3

[0044] The present embodiment provides a quick-drying high-temperature-resistant primer for steel, which is composed of bisphenol F type liquid epoxy resin, iron red powder, titanium dioxide, defoamer, flame retardant, mica, multifunctional auxiliary Agent AMP-95, graphite powder and water-based acrylic resin, its weight percent composition is: bisphenol F type liquid epoxy resin: 27%, iron red powder: 6.6%, titanium dioxide: 12%, defoamer: 9%, Flame retardant: 5.7%, mica: 3.5%, multifunctional additive AMP-95: 9%, graphite powder: 12.3%, and the balance is water-based acrylic resin; the preparation method of the quick-drying high-temperature resistant primer for steel Follow these steps:

[0045] Step (1): First, put the water-based acrylic resin and bisphenol F liquid epoxy resin into the stirring tank for mixing, control the temperature in the stirring tank at 68°C, set the stirring speed at 960r / min, and stir for 3 hours. Then put in titanium dioxide and continue stirring...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a quick-drying high-temperature-resistant undercoat for steel. The undercoat comprises the following component in percentage by weight: 26-28% of bisphenol F-type liquid epoxy resin, 6.5-6.8% of iron oxide red powder, 11-13% of titanium dioxide, 8-10% of a defoamer, 5.5-5.8% of a fire retardant, 3.2-3.8% of mica, 8-12% of a multifunctional additive AMP-95, 12.2-12.5% of graphite powder, and the balance of watercraft acrylic resin. According to the preparation method for the quick-drying high-temperature-resistant undercoat used for the steel, the undercoat is dried quickly, has no peculiar smell, and is good in adhesive property, stable to alkaline and most solvents, good in corrosion resistance, gas resistance, inflaming retarding, water resistance, thermal insulation and the like , and excellent in friction resistance and high temperature resistance.

Description

technical field [0001] The invention relates to a primer and a preparation method thereof, in particular to a quick-drying high-temperature resistant primer for steel and a preparation method thereof. Background technique [0002] At present, many mechanical surface treatments need to be painted with primer, and its main function is to protect the steel from atmospheric corrosion during processing. There are many types of primers on the market, but they generally have the defects of slow drying, poor corrosion resistance, and poor high temperature resistance, which not only reduces the service life of the equipment, increases costs, but also leads to low work efficiency due to long drying time, and During the processing, it is easy to emit chemical odor, which is harmful to the health of operators. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a quick-drying high-temperature-resistant primer for steel and a pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/02C09D7/12
Inventor 郑化陈廷生刘小林
Owner JIANGSU MARINE VICTORY COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap