Polishing method for metallographic sample of aluminum alloy
A technology for metallographic samples and aluminum alloys, which is applied in the field of metallographic sample casting of aluminum alloys, can solve the problems of poor quality of metallographic pictures, waste of medicines, easy to be scratched, etc., and achieve less surface scratches and save time. , the effect of reducing the impact
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0006] The method for polishing the metallographic sample of aluminum alloy applied to the aluminum alloy casting industry of the present invention is as follows: first, the metallographic sample of aluminum alloy is roughly polished on water sandpaper. When water sandpaper is used, the sandpaper should be soaked with water. In the casting process, it is necessary to continuously add water, generally casting for 3-5min; then use a small sample (test bar with a diameter of 6mm) to cast a metal mold (select a small cylindrical mold according to the size of the test bar-the material Steel) rough polishing is performed on the metallographic sample (the metal mold needs to be parallel to the sample and clamped), generally for 3-5 minutes; the metallographic sample will be polished on the polishing fabric after rough polishing Fine polishing (general polishing 4-6min), metallographic polishing agent (usually diamond spray polishing agent) can be sprayed in the polishing process to mak...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap