Screw tap machining method

A processing method and tap technology are applied in the processing field of taps to achieve the effects of improving processing progress, simple processing method and convenient use.

Inactive Publication Date: 2014-12-31
吴加庆
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] When the drill is used for a period of time, the threads will be worn and broken. In order to save materials and funds, taps should be used to tap the drill, but the tapping of the tap The department often becomes scrapped due to wear and tear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of processing method of screw tap

[0018] Coarse materials are acidified and polished to remove the dirt on the steel surface of the coarse materials. Get blanks.

[0019] Aging heat treatment is carried out on the blank.

[0020] Then carry out heat treatment, the temperature of low-temperature preheating is 245°C, the temperature of tempering is 124°C, and the tempering time is 30mm.

[0021] The taps are machined on the lathe, and the tapped parts are deburred and quenched.

[0022] The quenching temperature is 500°C, the tap part is frosted, and then carburized.

[0023] After taking it out, soak it in the mixed solution of polyurethane and sodium benzoate, the concentration of polyurethane is 45% and sodium benzoate 4%, and the balance is water.

[0024] Finally, the workpiece is coated with anti-rust oil.

Embodiment 2

[0026] A kind of processing method of screw tap

[0027] Coarse materials are acidified and polished to remove the dirt on the steel surface of the coarse materials. Get blanks.

[0028] Aging heat treatment is carried out on the blank.

[0029] Then carry out heat treatment, the temperature of low temperature preheating is 300°C, the temperature of tempering is 345°C, and the tempering time is 70m.

[0030] The taps are machined on the lathe, and the tapped parts are deburred and quenched.

[0031] The quenching temperature is 500°C, the tap part is frosted, and then carburized.

[0032] After taking it out, soak it in the mixed solution of polyurethane and sodium benzoate, the concentration of polyurethane is 60% and sodium benzoate 5%, and the balance is water.

[0033] Finally, the workpiece is coated with anti-rust oil.

Embodiment 3

[0035] A kind of processing method of screw tap

[0036] Coarse materials are acidified and polished to remove the dirt on the steel surface of the coarse materials. Get blanks.

[0037] Aging heat treatment is carried out on the blank.

[0038] Then conduct heat treatment, the temperature of low temperature preheating is 270°C, the temperature of tempering is 200°C, and the tempering time is 50m.

[0039] The taps are machined on the lathe, and the tapped parts are deburred and quenched.

[0040] The quenching temperature is 500°C, the tap part is frosted, and then carburized.

[0041] After taking it out, soak it in the mixed solution of polyurethane and sodium benzoate, the concentration of polyurethane is 50% and sodium benzoate 4.5%, and the balance is water.

[0042] Finally, the workpiece is coated with anti-rust oil.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A screw tap machining method is characterized in that coarse steel material is acidized and polished to remove surface dirt so as to obtain a blank, aging treatment is performed on the blank, thermal treatment is then performed on the blank, low-temperature preheating temperature is 245-300 DEG C, tempering temperature is 124-345 DEG C, tempering time is 30-40 minutes, machining a screw tap on a lathe, burr and quenching treatments are performed on a tapping part, quenching temperature is 500 DEG C, sand conditioning is performed on a screw tap part, carburization is then performed, the taken-out screw tap is soaked in mixed solution of polyurethane and sodium benzoate, the concentration of the polyurethane is 45-60%, and the concentration of the sodium benzoate is 4-5%. By the method which is simple and few in steps, the screw tap with the durable screw tap part can be manufactured, use of the screw tap is facilitated, and machining progress is increased.

Description

technical field [0001] The invention belongs to the field of mechanical processing, and in particular relates to a processing method of a screw tap. Background technique [0002] When the drill bit is used for a period of time, the threads will be worn and broken. In order to save materials and funds, a tap should be used to tap the drill bit. However, the tapping part of the tap is often worn out and scrapped. Contents of the invention [0003] The invention provides a processing method of a screw tap. The method can produce a higher-strength screw tap tapping part, prolong the life of the screw tap, and reduce material waste and purchase cost. [0004] A kind of processing method of screw tap [0005] Coarse materials are acidified and polished to remove the dirt on the steel surface of the coarse materials. Get blanks. [0006] Aging heat treatment is carried out on the blank. [0007] Then carry out heat treatment, the temperature of low-temperature preheating ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/52
CPCB23P15/52
Inventor 吴加庆
Owner 吴加庆
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap