A kind of environment-friendly steel surface antirust agent and preparation method thereof

A technology of steel surface and rust inhibitor, applied in the field of steel surface treatment, can solve the problems of high cost, high price and complicated production of rust inhibitor, and achieve the effect of excellent construction performance, excellent environmental protection performance and protection against rust.

Active Publication Date: 2017-01-11
珠海大利刀具有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent No. CN03111171.8 proposes a formula to replace sodium nitrite, but it is complicated to make and inconvenient to use; Large, more expensive, the cost of antirust agent is much higher than that of sodium nitrite antirust agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The iron and steel antirust agent of the present embodiment is made from the following raw materials in parts by weight: 5 parts of liquefied paraffin, 4 parts of 3-aminopropyltrimethoxysilane, 2 parts of epoxy rice bran oil, and 12 parts of aminotrimethylene phosphonic acid , 3 parts of polyethylene wax, 10 parts of isopropanolamine, 4 parts of sodium gluconate, 3 parts of benzotriazole, 5 parts of surfactant, 3 parts of carboxymethyl cellulose, 4 parts of 2-methylimidazoline , 3 parts of thickener, 3 parts of sodium lauryl sulfate and 90 parts of deionized water.

[0015] The thickener is aluminum silicate.

[0016] The surfactant is polyoxyethylene fatty alcohol ether.

[0017] The antirust agent for iron and steel of this embodiment comprises the following steps: first mix polyethylene wax, liquefied paraffin, 2-methylimidazoline and deionized water in proportion by weight, stir and heat to 120°C for 1 hour, then cool to 40°C, then add 3-aminopropyltrimethoxysilan...

Embodiment 2

[0020] The iron and steel rust inhibitor of the present embodiment is made from the following raw materials in parts by weight: 6 parts of liquefied paraffin, 5 parts of 3-aminopropyltrimethoxysilane, 3 parts of epoxy rice bran oil, and 13 parts of aminotrimethylene phosphonic acid , 4 parts of polyethylene wax, 11 parts of isopropanolamine, 5 parts of sodium gluconate, 4 parts of benzotriazole, 6 parts of surfactant, 4 parts of carboxymethyl cellulose, 5 parts of 2-methylimidazoline , 4 parts of thickener, 4 parts of sodium lauryl sulfate and 92 parts of deionized water.

[0021] The thickener is diatomaceous earth.

[0022] The surfactant is polyoxyethylene fatty alcohol ether.

[0023] The antirust agent for iron and steel of this embodiment comprises the following steps: first mix polyethylene wax, liquefied paraffin, 2-methylimidazoline and deionized water in proportion by weight, stir and heat to 130°C for 1 hour, then cool to 50°C, then add 3-aminopropyltrimethoxysila...

Embodiment 3

[0026] The iron and steel antirust agent of the present embodiment is made from the following raw materials in parts by weight: 6 parts of liquefied paraffin, 5 parts of 3-aminopropyltrimethoxysilane, 5 parts of epoxy rice bran oil, and 14 parts of aminotrimethylene phosphonic acid , 4 parts of polyethylene wax, 14 parts of isopropanolamine, 6 parts of sodium gluconate, 4 parts of benzotriazole, 7 parts of surfactant, 5 parts of carboxymethyl cellulose, 8 parts of 2-methylimidazoline , 4 parts of thickener, 5 parts of sodium lauryl sulfate and 98 parts of deionized water.

[0027] The thickener is bentonite.

[0028] Surfactant is coconut oil fatty acid diethanolamide.

[0029] The antirust agent for iron and steel of this embodiment comprises the following steps: first mix polyethylene wax, liquefied paraffin, 2-methylimidazoline and deionized water in proportion by weight, stir and heat to 120°C for 1 hour, then cool to 50°C, then add 3-aminopropyltrimethoxysilane, epoxy r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly steel surface anti-rust agent and a preparation method thereof. The preparation method comprises the following steps: mixing polyethylene wax, liquefied paraffin, methyl-2-imidazoline and deionized water according to weight parts, stirring and heating to 120-130 DEG C, insulating for 1 hour, and cooling to 40-50 DEG C; adding 3-aminopropyltrimethoxysilane, epoxy rice bran oil, amino trimethylene phosphonic acid, isopropanolamine, sodium gluconate, benzotriazole, a surfactant, carboxymethyl cellulose, a thickening agent and sodium lauryl sulfate, and stirring until the components are completely dissolved. The anti-rust agent uses water as a dispersing medium, has excellent environment-friendly performance, is non-combustible and unexplosive, does not have pollution, and does not have toxicity and risk on human bodies. The anti-rust agent has an excellent construction performance, cannot corrode metal in the using process, is simple and convenient to apply, and can be used for effectively protecting metal from corrosion by soaking, spraying, coating and other modes. The anti-rust period of the anti-rust agent can be 10-12 months in a normal environment.

Description

technical field [0001] The invention relates to a steel surface treatment technology, in particular to an environment-friendly steel surface antirust agent and a preparation method thereof. Background technique [0002] At present, with the continuous development of industry, the use of steel is also increasing. However, during the production process or the storage process of finished products, steel plates are easily oxidized and rusted when encountering humid air and rainy days, which affects the appearance quality of products. This has brought problems to the use of steel, and the annual loss of steel due to corrosion is very alarming. In order to prevent surface corrosion, antirust treatment must be carried out; Protective oil film, so as to isolate the corrosion of metal by water vapor in the air, and achieve the purpose of rust prevention. However, the use of antirust oil requires a large amount of oil raw materials, which intensifies energy consumption and increases c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/173
Inventor 陈伟
Owner 珠海大利刀具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com