Wear resistant rubber

A wear-resistant rubber and neoprene technology, applied in the field of wear-resistant rubber, can solve the problem of high wear resistance of wear-resistant rubber, and achieve the effects of low cost, good wear resistance and high strength

Inactive Publication Date: 2015-03-11
ANHUI LONGCHUAN RUBBER & PLASTIC TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rubber can be obtained from the sap of some plants, or it can be man-made. Both have quite a lot of applications and products, such as tires, gaskets, etc., which need to have strong wear resistance, but to increase the wear resistance of rubber high wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] A kind of wear-resistant rubber, comprising by weight: 100 parts of neoprene rubber, 60 parts of nitrile rubber, 8 parts of paraffin-based rubber softening oil, 35 parts of carbon black N95, 4 parts of zinc oxide, 2 parts of polyethylene wax, dioxin 2.5 parts of ester, 2 parts of silane coupling agent, 1 part of 2-mercaptobenzothiazole, 0.8 part of zinc dibutyldithiocarbamate, 1 part of N-cyclohexyl-2-benzothiazole sulfenamide, 2 parts of sulfur, 0.5 parts of 2,2'-dithiodibenzothiazole.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wear resistant rubber. The wear resistant rubber comprises 100 parts of chloroprene rubber, 60 parts of nitrile butadiene rubber, 8 parts of paraffin-based rubber softening oil, 35 parts of carbon black N95, 4 parts of zinc oxide, 2 parts of polyethylene wax, 2.5 parts of dioctyl phthalate, 2 parts of a silane coupling agent, 1 part of 2-mercaptobenzothiazole, 0.8 parts of zinc dibutyl dithiocarbamate, 1 part of N-cyclohexyl-2-benzothiazolesulfenamide, 2 parts of sulfur, and 0.5 parts of 2,2'-dibenzothiazole disulfide. The wear resistant rubber has the advantages of good wear resistance, high strength and low cost.

Description

technical field [0001] The invention belongs to the field of rubber, in particular to a wear-resistant rubber. Background technique [0002] Rubber is an elastic polymer. Rubber can be obtained from the sap of some plants, or it can be man-made. Both have quite a lot of applications and products, such as tires, gaskets, etc., which need to have strong wear resistance, but to increase the wear resistance of rubber higher wear resistance. Contents of the invention [0003] The object of the present invention is to provide a wear-resistant rubber, which improves the wear-resistant performance of the rubber. [0004] The present invention is realized through the following technical solutions: [0005] A kind of wear-resistant rubber, comprising by weight: 100 parts of neoprene rubber, 60 parts of nitrile rubber, 8 parts of paraffin-based rubber softening oil, 35 parts of carbon black N95, 4 parts of zinc oxide, 2 parts of polyethylene wax, dioxin 2.5 parts of ester, 2 part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L9/02C08K13/02C08K3/04C08K3/22C08K5/47
Inventor 王银川
Owner ANHUI LONGCHUAN RUBBER & PLASTIC TECH CO LTD