An acidic plating flux containing zinc phytate

A technology of zinc phytate and plating flux, which is applied in hot-dip plating process, coating, metal material coating process, etc., can solve the problems of affecting the adhesion of the coating, affecting the appearance of the coating, and the failure of the plating flux, so as to improve the surface Quality, Sindelin effect suppression, adhesion increase effect

Active Publication Date: 2018-02-02
TIANCHANG FEILONG BRAND STEEL GRID
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the addition of aluminum element in hot-dip galvanizing is greater than 0.06%, the conventional ammonium zinc chloride flux will be invalidated, resulting in problems such as missing plating of the plated parts, making the hot-dip galvanized aluminum alloy coating in production and application heavily restricted
Moreover, for ordinary carbon steel commonly used for hot-dip galvanizing, especially active silicon-containing steel, a thick zinc-iron alloy layer is easy to form due to the Sandelin effect. The thickening of this alloy layer not only affects the appearance of the coating, but also affects the adhesion of the coating. focus on

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of acid plating flux containing phytic acid zinc proposed by the present invention, its component comprises by weight: 50 parts of ammonium chloride, 30 parts of sodium fluoride, 40 parts of aluminum chloride, 30 parts of stannous chloride, chlorine 10 parts nickel, 40 parts zinc phytate, 60 parts zinc oxide, 20 parts borax, 10 parts hydrogen peroxide, K 2 Be(SO 4 ) 2 40 parts, 60 parts of water, 10 parts of citric acid, 20 parts of oxalic acid, 15 parts of octylphenol polyoxyethylene ether, 30 parts of methanol, 2 parts of urea, 10 parts of N-hydroxyethyl perfluorooctane sulfonamide.

Embodiment 2

[0017] A kind of acid plating flux containing phytic acid zinc proposed by the present invention, its component comprises by weight: 70 parts of ammonium chloride, 25 parts of sodium fluoride, 43 parts of aluminum chloride, 28 parts of stannous chloride, chlorine 16 parts nickel, 30 parts zinc phytate, 100 parts zinc oxide, 18 parts borax, 14 parts hydrogen peroxide, KBe 2 B 3 o 7 35 parts, 65 parts of water, 9 parts of citric acid, 23 parts of oxalic acid, 12 parts of octylphenol polyoxyethylene ether, 32 parts of methanol, 1.8 parts of urea, and 12 parts of N-hydroxyethyl perfluorooctane sulfonamide.

Embodiment 3

[0019] A kind of acid plating flux containing phytic acid zinc proposed by the present invention, its component comprises by weight: 90 parts of ammonium chloride, 20 parts of sodium fluoride, 47 parts of aluminum chloride, 25 parts of stannous chloride, chlorine 19 parts nickel, 25 parts zinc phytate, 120 parts zinc oxide, 17 parts borax, 16 parts hydrogen peroxide, KBe 2 B 3 o 7 25 parts, 70 parts of water, 6 parts of citric acid, 24 parts of oxalic acid, 9 parts of octylphenol polyoxyethylene ether, 34 parts of methanol, 1.4 parts of urea, and 13 parts of N-hydroxyethyl perfluorooctane sulfonamide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an acidic plating assistant agent containing zinc phytate. The acidic plating assistant agent comprises the following components in parts by weight: 50-100 parts of ammonium chloride, 15-30 parts of sodium fluoride, 40-50 parts of aluminum chloride, 20-30 parts of stannous chloride, 10-20 parts of nickel chloride, 20-40 parts of zinc phytate, 60-150 parts of zinc oxide, 15-20 parts of borax, 10-20 parts of hydrogen peroxide, 20-40 parts of KyAnXm, 60-75 parts of water, 5-10 parts of citric acid, 20-25 parts of oxalic acid, 5-15 parts of octaphenyl polyoxyethylene ether, 30-35 parts of methanol, 1-2 parts of urea, and 10-15 parts of N-hydroxyethyl perfluorooctane sulfonamide, wherein in KyAnXm, A is a rare earth cation or zirconium ion and X is sulfate or borate or fluorine ion. By the acidic plating assistant agent, a matrix metal is subjected to hot-dip plating treatment, the wetting infiltration effect and adhesion force of the plating assistant agent on the matrix metal are increased, the plating assistant effect is improved, the mechanical properties of the matrix metal are enhanced, the oxidation resistance is increased so that the matrix metal is more beautiful.

Description

technical field [0001] The invention relates to the technical field of hot-dip plating, in particular to an acidic zinc phytate-containing flux. Background technique [0002] At present, the anti-corrosion coating of the base metal in China mainly includes different systems such as electro-galvanizing, hot-dip galvanizing, aluminum, zinc-aluminum alloy, etc., using the above-mentioned process method, a layer of corrosion-resistant coating is coated on the surface of the base metal to achieve the protection of the base metal. Protect. Due to the deterioration of the global atmospheric environment quality, the content of some corrosive gases such as some acid gases in the air is increasing day by day, and the corrosion of the coating is intensified. The corrosion resistance and service life of single metal coatings, especially zinc coatings, have been difficult to meet the material protection requirements of modern industries. . [0003] Hot-dip galvanizing is one of the mos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C2/06
CPCC23C2/06
Inventor 孙长志
Owner TIANCHANG FEILONG BRAND STEEL GRID
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products