Rapid dehydration curing agent as well as preparation method and application thereof

A rapid dehydration and curing agent technology, which is applied in the field of newly repaired normal temperature asphalt surface layer and road maintenance and repair, can solve the problems of difficult curing and slow concrete dehydration, and achieve the effect of rapid moisture absorption and strong curing ability

Active Publication Date: 2015-04-08
南通福伦利新材料有限公司
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the above problems in the prior art, provide a fast dehydration curing agent and its preparation method and application, and solve the problem of slow dehydration and difficult curing of traditional modified emulsified asphalt concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid dehydration curing agent as well as preparation method and application thereof
  • Rapid dehydration curing agent as well as preparation method and application thereof
  • Rapid dehydration curing agent as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Step 1) Weigh 500g of mixed aggregate, 47.5g of asphalt mixed at room temperature, 17.5g of rapid dehydration curing agent, and 7.5g of water;

[0030] Step 2) Put the weighed mixed aggregate and fast dehydration curing agent into the mixing pot, stir for 15 seconds, and stir evenly;

[0031] Step 3) Put the weighed water into the mixing pot to moisten the aggregate;

[0032] Step 4) Add the weighed normal temperature mixed asphalt into the mixing pot, and stir for 60s;

[0033] Step 5) Put the ring-shaped test mold on the asphalt felt, mix the mixture that meets the required ratio, pour it into the test mold immediately, scrape it flat, and tamp it 75 times;

[0034] Step 6) After 45 minutes, the sample reaches the initial setting, and the sample is demoulded;

[0035] Step 7) Refer to figure 1 , figure 2 As shown, the detection performance is shown in Table 1.

[0036] Table 1

[0037]

[0038] Step 8) The performance is up to standard, mix the mixture accor...

Embodiment 2

[0042] Step 1) Weigh 500g of mixed aggregate, 50.5g of mixed asphalt at room temperature, 19.0g of rapid dehydration curing agent, and 7.5g of water;

[0043] Step 2) Put the weighed mixed aggregate and fast dehydration curing agent into the mixing pot, stir for 15 seconds, and stir evenly;

[0044] Step 3) Put the weighed water into the mixing pot to moisten the aggregate;

[0045] Step 4) Add the weighed normal temperature mixed asphalt into the mixing pot, and stir for 60 seconds;

[0046] Step 5) Put the ring-shaped test mold on the asphalt felt, mix the mixture that meets the required ratio, pour it into the test mold immediately, scrape it flat, and tamp it 75 times;

[0047] Step 6) After 45 minutes, the sample reaches the initial setting, and the sample is demoulded;

[0048] Step 7) Detection performance, see Table 2.

[0049] Table 2

[0050]

[0051] Step 8) The performance is up to standard, mix the mixture according to steps 1-4, and spread it with a paver;...

Embodiment 3

[0055] Step 1) Weigh 500g of mixed aggregate, 45.0g of mixed asphalt at room temperature, 15.0g of rapid dehydration curing agent, and 7.5g of water;

[0056] Step 2) Put the weighed mixed aggregate and fast dehydration curing agent into the mixing pot, stir for 15 seconds, and stir evenly;

[0057] Step 3) Put the weighed water into the mixing pot to moisten the aggregate;

[0058] Step 4) Add the weighed normal temperature mixed asphalt into the mixing pot, and stir for 60s;

[0059] Step 5) Put the ring-shaped test mold on the asphalt felt, mix the mixture that meets the required ratio, pour it into the test mold immediately, scrape it flat, and tamp it 75 times;

[0060] Step 6) After 45 minutes, the sample reaches the initial setting, and the sample is demoulded;

[0061] Step 7) Detection performance, see Table 3.

[0062] table 3

[0063]

[0064] Step 8) The performance is up to standard, mix the mixture according to steps 1-4, and spread it with a paver;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rapid dehydration curing agent as well as a preparation method and an application thereof. The rapid dehydration curing agent is formed by mixing anti-stripping agent powder, mineral powder, polymer rubber powder and cement. After the curing agent is added to a mixture, normal-temperature asphalt concrete is rapidly dehydrated and cured, and has a high elastoplastic surface layer and excellent weather resistance, so that the problems that the traditional modified emulsified asphalt concrete is slowly dehydrated and not easily cured are solved, and thus the construction efficiency and the social benefits are greatly improved.

Description

technical field [0001] The invention belongs to the field of newly repaired normal-temperature asphalt surface layer and road maintenance and repair, and specifically relates to a fast dehydration curing agent and its preparation method and application. Background technique [0002] At present, the general modified emulsified asphalt mixture on the market in our country has a slow process of strength formation. It has plasticity and fluidity during paving and rolling, and can be squeezed to irregular places in pits. Under the action of driving and air, the water only depends on volatilization, the asphalt gradually thickens, the distribution of room temperature asphalt mixture particles is tighter, the porosity is reduced, the mutual bonding of mineral materials is stronger, and the density of the mixture increases. This process takes several days, after which the strength will gradually increase. After a period of time, its deformation and strength will gradually stabilize,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B24/36
Inventor 蔡海军
Owner 南通福伦利新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap