Mixture for manufacturing latex mattress body, manufacturing method and latex mattress body

Abstract

The invention discloses a mixture obtained by mixing natural latex, artificial latex, nano-silver, nano-zinc oxide and active carbon according to a specific ratio to manufacture a latex mattress body and a latex mattress body which contains the above components and is prepared by the use of the mixture through a given method. The mixture comprises, by weight, 20% of natural latex containing 50% moisture, 80% of artificial latex containing 40% moisture, 3% of nano-silver weighed relative to the total weight of natural latex and artificial latex, 5% of nano-zinc oxide weighed relative to the total weight of natural latex, artificial latex and nano-silver, and 5% of active carbon weighed relative to the total weight of natural latex, artificial latex, nano-silver and nano-zinc oxide.

Description

technical field [0001] The invention relates to the technical field of latex pads, in particular to a mixture for manufacturing latex pads, a method for manufacturing latex pads from the mixture, and the latex pad. Background technique [0002] The traditional method of making latex pads is to mix natural latex and artificial latex at a ratio of 20%:80%. The natural latex is made by mixing 40% water and 60% rubber solids. The artificial latex It is made by mixing 30% water and 70% rubber solids. After mixing the artificial latex and the natural latex, add a certain amount of vulcanization accelerator, and stir at a speed of 1200 rpm for 20 minutes to form a latex mixture. [0003] Then pour the latex mixture into the high-speed foaming machine to make the mixture go through and complete the foaming process to form a foamed material; then pour the foamed material into the coating machine and inject it into the working conveying platform, the conveying speed of the working co...

AI Technical Summary

Problems solved by technology

But taking the addition of activated carbon as an example, the problem we face is that activated carbon has excellent hygroscopic properties, and whether it is natural latex or artificial latex, it is a liquid raw material containing water. If activated carbon is added to the latex mixture, its The moisture content of the latex mixture must be greatly reduced, the wet ratio of the mixture is changed, the mixture is solidified, and it is impossible to stir and follow-up process