Method for preparing ceramic lace

A lace and ceramic technology, applied in the field of inorganic non-metallic materials (ceramics), can solve the problems that can no longer be folded up, and three-dimensional ceramic lace has not yet appeared, and achieve the effect of strong plasticity, tight combination and low production cost

Active Publication Date: 2015-05-06
景德镇市隆祥陶瓷有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of the ceramic material, the folded effect cannot be realized after setting the mesh. So far, although there are ceramic lace for flat decoration on the market, there has not been a three-dimensional ceramic lace that can be used for skirt decoration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The first step, configure the lace mud

[0020] Configure 1000g of lace mud according to the weight percentage of the following lace mud formula:

[0021] Calcined kaolin 70g, clay 180g, quartz 150g, feldspar 260g, mica 240g, maltose 40g, epoxy resin 60g;

[0022] Then pass the configured mud through a 200-mesh vibrating sieve and remove iron from a magnetic separator, then crush the mud into a volume of 2 cm 3 granules, then soaked in water for 9 hours, and ball milled for 13 hours to control the specific gravity of the milled slurry to 58kg / cm 3 .

[0023] The second step, configure the viscous agent and add it to the lace mud

[0024] Stir 330g of viscous agent and 1650g of 60°C hot water to make it into a liquid state, and adjust its specific gravity to 42 kg / cm 3 Finally, add in the ball milled lace mud, and continue ball milling for 7 hours, control the specific gravity of the milled lace mud to be 59 kg / cm 3 .

[0025] Wherein the composition of 330g of vis...

Embodiment 2

[0046] The first step, configure the lace mud

[0047] Configure 1000g of lace mud according to the weight percentage of the following lace mud formula:

[0048] Calcined kaolin 120g, clay 190g, quartz 170g, feldspar 220g, mica 200g, maltose 30g, acrylic resin 70g;

[0049] Then pass the configured mud through a 200-mesh vibrating sieve and remove iron from a magnetic separator, then crush the mud into a volume of 2 cm 3 granules, then soaked in water for 11 hours, and ball milled for 15 hours to control the specific gravity of the milled slurry to 63 kg / cm 3 .

[0050] The second step, configure the viscous agent and add it to the lace mud

[0051] Stir 330g of viscous agent with 1650g of 60°C hot water to make it liquid, and adjust its specific gravity to 43 kg / cm 3 Finally, add in the ball milled lace mud, and continue ball milling for 11 hours, control the specific gravity of the milled lace mud to be 64 kg / cm 3 .

[0052] Wherein the composition of 330g of viscous age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a ceramic lace. Natural minerals and chemical raw materials are adopted, and the formula of the lace pug comprises the following components in percentage by weight: 5-15 percent of calcined kaolin, 18-22 percent of clay, 15-20 percent of quartz, 22-26 percent of feldspar, 20-25 percent of mica, 3-7 percent of maltose and 5-10 percent of a resin. The preparation method comprises the following steps: dosing, screening, removing iron, performing ball milling, adding a thickener, manufacturing a lace blank, decorating the ceramic body and firing to obtain the product, wherein the firing temperature ranges from 1280 DEG C to 1300 DEG C. The ceramic lace is fired in a reducing atmosphere, is tightly combined with the ceramic body and is clear in meshes and high in stereoscopic impression, and the artistic effects of ceramic products are obviously improved. Therefore, the ceramic lace has wide market prospects.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a preparation method of ceramic lace. Background technique [0002] Lace first appeared in the United States. It is a hand-knitted product composed of many meshes knitted with silk threads or yarns according to a certain pattern. It is generally used on women's clothing, especially evening dresses and wedding dresses, to highlight the Noble and elegant status. Since the production of lace is a very complicated process, besides the need to set the mesh, it also needs to be consciously folded when decorating the skirt, so that it has a three-dimensional effect like water waves. But due to the self characteristic of ceramic material, can't realize the folding effect again after mesh is set, therefore although there is the ceramic lace that planar decoration is used on the market so far, the three-dimensional ceramic lace that can be used for sk...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/22C04B33/24C04B35/16C04B35/622
Inventor 阮礼祥
Owner 景德镇市隆祥陶瓷有限公司