Polyethylene eco-friendly flame-retardant foaming plastic and preparation method thereof

A foamed plastic and polyethylene technology, which is applied in the field of polyethylene environmentally friendly flame-retardant foamed plastics and its preparation, can solve the problems of poor tensile strength of materials, excessive flame retardants, waste of production resources, etc., and achieve improved tensile properties , reduce the content of use, and save production costs

Inactive Publication Date: 2015-07-01
冼冰
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the above-mentioned deficiencies of the prior art, and provide a polyethylene environmentally friendly flame-retardant foamed plastic, which aims to solve the problem that the existing flame-retardant foamed materials use too many flame retardants, waste production resources, and the material is pulled The problem of poor tensile strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyethylene eco-friendly flame-retardant foaming plastic and preparation method thereof
  • Polyethylene eco-friendly flame-retardant foaming plastic and preparation method thereof
  • Polyethylene eco-friendly flame-retardant foaming plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] Correspondingly, the embodiment of the present invention also provides a preparation method of the above-mentioned polyethylene environment-friendly flame-retardant foamed plastic, the process flow of which is as follows figure 1 shown. The method includes the following steps:

[0032] S01. Weigh the components of polyethylene environmentally friendly flame-retardant foamed plastic: weigh each component according to the above-mentioned formula of polyethylene environmentally friendly flame-retardant foamed plastic;

[0033] S02. Add each component in stages and banbury for processing to obtain a cross-linked material: After stirring the weighed polyoxymethylene, add high-pressure low-density polyethylene, ultra-high molecular weight polyethylene, chopped basalt fiber, zircon powder and The flame retardant is subjected to one-stage banburying treatment, and then zinc oxide and stearic acid are added for second-stage banburying treatment, and then high-temperature foamin...

Embodiment 1

[0043] A polyethylene environment-friendly flame-retardant foamed plastic, comprising the following components by weight:

[0044]

[0045] The preparation method of the polyethylene environment-friendly flame-retardant foamed plastic of above-mentioned embodiment 1 comprises the following steps:

[0046] S11. Weigh each component according to the specific formula of the above-mentioned polyethylene environment-friendly flame-retardant foamed plastic;

[0047] S12. Put the weighed polyoxymethylene into a mixer at a temperature of 180° C. to 230° C. and stir for 1 to 3 minutes to soften it. Then put it into the internal mixer together with the weighed ultra-high molecular weight polyethylene, high-pressure low-density polyethylene, chopped basalt fiber, zircon powder and melamine phosphate; The temperature gauge measures 55°C to 65°C, and the pressure cover and dust cover are covered for banburying. When the temperature rises to about 65°C, add zinc oxide and stearic acid ...

Embodiment 2

[0050] A polyethylene environment-friendly flame-retardant foamed plastic, comprising the following components by weight:

[0051]

[0052]

[0053] The preparation method of the polyethylene environment-friendly flame-retardant foamed plastic in Example 2 is the same as the preparation method of the above-mentioned Example 1, and will not be described here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle sizeaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses polyethylene eco-friendly flame-retardant foaming plastic and a preparation method thereof. The polyethylene eco-friendly flame-retardant foaming plastic comprises, by weight, 3.5-4.7 parts of high pressure low density polyethylene, 1.2-2.5 parts of ultrahigh molecular weight polyethylene, 0.8-2.3 parts of paraform, 1.2-3 parts of short cut basalt fibers, 0.8-2.5 parts of zirconium silicate powder, 2.2-3.5 parts of a fire retardant and 0.9-1.6 parts of chemical auxiliary agents. The preparation method improves polyethylene eco-friendly flame-retardant foaming plastic stretching performances, realizes excellent flame retardation effects, reduces a fire retardant use amount, and saves a production cost. The polyethylene eco-friendly flame-retardant foaming plastic is nontoxic and eco-friendly and obviously enlarges a product application scope. The preparation method substantially improves a yield of the polyethylene eco-friendly flame-retardant foaming plastic, has simple processes and a low cost, can be operated and controlled easily and is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polyethylene environment-friendly flame-retardant foamed plastic and a preparation method thereof. Background technique [0002] High-pressure low-density polyethylene is the lightest variety among polyethylene resins, and its crystallinity (55%-65%) and softening point (90-100°C) are low; it has good flexibility, extensibility, and transparency , cold resistance and processability; its chemical stability is good, it can resist acid, alkali and salt solution; it has good electrical insulation and air permeability, and low water absorption; it is soft, has good extensibility, electrical insulation properties, chemical stability, processability and low temperature resistance (-70°C). But the disadvantage is that it is easy to burn, which brings great safety hazards to daily life, and its mechanical strength is poor, and it is easy to age and decompose and change color ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L59/00C08K13/04C08K7/10C08K3/34C08K5/3492C08K3/22C08K5/09C08K5/14C08J9/10B29B7/02B29B7/28
CPCC08L23/06B29B7/02B29B7/286C08J9/103C08L2201/02C08L2205/025C08L2205/03C08L2207/066C08L2207/068C08L59/02C08K13/04C08K7/10C08K3/34C08K5/3492C08K5/14C08K2003/2296C08K5/09
Inventor 冼冰
Owner 冼冰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap