High heat-resistant low-smoke flame-retardant ABS material and preparation method thereof

An ABS material, low-smoke flame-retardant technology, applied in the chemical industry, can solve the problems of large smoke generation, low thermal deformation temperature and impact strength, and achieve the effects of inhibiting decomposition, increasing thermal deformation temperature, and reducing costs

Inactive Publication Date: 2018-07-27
SHANGHAI QISHEN ENG PLASTICS CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the above-mentioned technical problems in the prior art, the present invention provides a high heat-resistant low-smoke flame-retardant ABS material and a preparation method thereof. The high heat-resistant low-smoke flame-retardant ABS material and its preparation method need to solve The technical problems of the ABS material in the prior art are large smoke generation, heat distortion temperature and low impact strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High heat-resistant low-smoke flame-retardant ABS material and preparation method thereof
  • High heat-resistant low-smoke flame-retardant ABS material and preparation method thereof
  • High heat-resistant low-smoke flame-retardant ABS material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] Table 1 Raw material composition distribution ratio

[0026]

[0027]

[0028] The parts by weight of each raw material are shown in Table 1

[0029] 1) Add ABS resin and various additives into the high-speed mixer and stir for 2 minutes at high speed.

[0030] 2) into the main feeder of the extruder,

[0031] 3) Then add it to a twin-screw extruder for basic granulation. The temperature distribution of the extruder is as follows: from the feed section to the head: 180°C, 200°C, 200°C, 200°C, 190°C, 190°C, 190°C, 180°C, 180°C, die head: 190°C ,

[0032] 4) After the material is extruded, it is water-cooled, pelletized, and then packed. The pellets were dried in a blast oven at 100°C for 4 hours, and then test specimens were prepared by an injection molding machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high heat-resistant low-smoke flame-retardant ABS material. The high heat-resistant low-smoke flame-retardant ABS material is composed of the following components in percentage by mass: 58-80% of ABS resin, 8%-20% of brominated flame retardant, 3%-10% of stibium flame retardant, 1-2% of a compound smoke suppressor, 1%-5% of an inorganic flame-retardant synergist, 0.1-1.0% of an anti-dripping agent and 1%-5% of other processing aids. The invention further provides the preparation method of the high heat-resistant low-smoke flame-retardant ABS material. The ABS resin is used as a matrix to prepare the high heat-resistant low-smoke flame-retardant ABS material through the smart combination of the flame retardant, the smoke suppressor and the special processing aids. The high heat-resistant low-smoke flame-retardant ABS material can be widely applied to the communication industry, the automobile industry, building materials, decorative materials, cables and the electric appliance industry.

Description

Technical field: [0001] The invention belongs to the field of chemical industry, and in particular relates to an ABS material, in particular to a high-heat-resistant, low-smoke, flame-retardant ABS material and a preparation method thereof. Background technique: [0002] Acrylonitrile-butadiene-styrene copolymer English name: Acrylonitrile butadiene Styrenecopolymers, ABS for short. ABS is a thermoplastic polymer material structure with high strength, good toughness and easy processing. In ABS resin, the synergistic properties between the three components can be exhibited: the properties of acrylonitrile component in ABS are heat resistance, chemical resistance, rigidity, and tensile strength, and the properties of butadiene are impact resistance Strength, styrene is characterized by processing fluidity and gloss. The combination of these three components complement each other, so that ABS resin has excellent comprehensive performance, good rigidity, high impact strength, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08K13/02C08K3/22C08K5/03C08K5/3492C08K5/13C08K3/34C08K3/38B29C47/92B29B9/06B29C48/92
Inventor 倪永明沈颖房军潘石刚穆金龙
Owner SHANGHAI QISHEN ENG PLASTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap