Water-repellent, oil-repellent, light-resistant, twist-resistant, cold-resistant, matte film water-based coating glue for textiles and preparation method

A water-based coating, textile technology, applied in textiles, papermaking, fiber processing, etc., can solve the problem of no other functions, and achieve the effect of improving coating performance, increasing matte effect, and low surface energy.

Active Publication Date: 2017-02-01
DANDONG UNIK TEXTILE
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The chemical fiber cloth is waterproof and calendered → one coat of primer → two coats of top coat; cotton cloth is coated with one coat of primer → two coats of top coat to realize the style of textile matte film coating, and its matte film coating has certain sun resistance functional effects, but no other functions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Emulsification reaction: In the pre-emulsion tank, fully mix deionized water 100, fatty alcohol polyoxyethylene ether XL90 2, sodium dodecylbenzenesulfonate 0.5, add isooctyl acrylate 70, methacrylate iso Bornyl ester 20, glycidyl methacrylate 2, trifluoroethyl methacrylate 15, vinyltrimethoxysilane 5, hydroxypropyl acrylate 1.5, and stir evenly to obtain a pre-emulsion.

[0043] Dissolve 0.3 ammonium persulfate and 10 deionized water evenly to prepare an aqueous solution of ammonium persulfate for use.

[0044]Initiate polymerization reaction: Take 20% of the weight of the above emulsion and add it to the reaction kettle, raise the temperature to 70-75°C, add 25% of the weight of ammonium persulfate aqueous solution to initiate, and then add the remaining emulsion dropwise at 70-75°C while keeping warm. At the same time, add the remaining initiator ammonium persulfate aqueous solution dropwise, and complete the dropwise addition within 2.5-3 hours, then raise the tempe...

Embodiment 2

[0047] Emulsification reaction: In the pre-emulsion tank, fully mix deionized water 120, fatty alcohol polyoxyethylene ether XL90 2.5, sodium dodecylbenzenesulfonate 0.6, add isooctyl acrylate 73, methacrylate iso Bornyl ester 22, glycidyl methacrylate 2.5, trifluoroethyl methacrylate 12, vinyltrimethoxysilane 6, hydroxypropyl acrylate 1.8, and stir evenly to obtain a pre-emulsion.

[0048] Dissolve ammonium persulfate 0.7 plus deionized water 15 evenly and set aside.

[0049] Initiate polymerization reaction: Take 20% of the weight of the above emulsion and add it to the reaction kettle, raise the temperature to 70-75°C, add 25% of the weight of ammonium persulfate aqueous solution to initiate, and then add the remaining emulsion dropwise at 70-75°C while keeping warm. At the same time, add the remaining initiator ammonium persulfate aqueous solution dropwise, and complete the dropwise addition within 2.5-3 hours, then raise the temperature to 80-85°C and keep it warm for 1.5...

Embodiment 3

[0052] Emulsification reaction: In the pre-emulsion tank, fully mix deionized water 150, fatty alcohol polyoxyethylene ether XL90 3.5, sodium dodecylbenzenesulfonate 0.7, add isooctyl acrylate 75, methacrylic acid Isobornyl 28, glycidyl methacrylate 3, trifluoroethyl methacrylate 14, vinyltrimethoxysilane 7, and hydroxypropyl acrylate 2 were stirred evenly to obtain a pre-emulsion.

[0053] Dissolve ammonium persulfate 0.5 plus deionized water 12 evenly and set aside.

[0054] Initiate polymerization reaction: Take 20% of the weight of the above emulsion and add it to the reaction kettle, raise the temperature to 70-75°C, add 25% of the weight of ammonium persulfate aqueous solution to initiate, and then add the remaining emulsion dropwise at 70-75°C while keeping warm. At the same time, add the remaining initiator ammonium persulfate aqueous solution dropwise, and complete the dropwise addition within 2.5-3 hours, then raise the temperature to 80-85°C and keep it warm for 1.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a water-repellent, oil-repellent, sun-proof, anti-bend torsion and cold-resistant matt-leather-membrane aqueous coating adhesive for textiles and a preparation method of the matt-leather-membrane aqueous coating adhesive. The preparation method comprises the steps of emulsifying isooctyl acrylate, isobornyl methacrylate, glycidyl methacrylate, trifluoroethyl methacrylate, vinyl trimethoxysilane, hydroxypropyl acrylate, fatty alcohol ethoxylate XL90 and dodecyl benzene sulfonate to trigger polymerization, and compounding a thickening agent, namely an associated polyurethane flatting rheological agent, a cross-linking agent, namely terminated isocyanate, a flatting agent, namely polymethyl urea resin and silicon dioxide with the particle size of 2-7 microns, so as to obtain the matt-leather-membrane aqueous coating adhesive.

Description

technical field [0001] The invention relates to a water-based coating glue for matte film, which is a modified acrylic resin polymer, which is used for coating chemical fiber, pure cotton or chemical fiber and pure cotton blended fabrics, so that the fabric can achieve the effect of imitation leather. Moreover, the film has the characteristics of water repellency, oil repellency, sun resistance, twist resistance, cold resistance, soft hand feeling, and strong washing fastness. Background technique [0002] In recent years, with the improvement of living standards, consumers prefer products with both functionality and style. Water-based coating fabrics with matte film and traditional Compared with matte film fabrics, it is more functional and more environmentally friendly, which greatly improves the added value of the product. [0003] At present, there is no technical disclosure of a multi-functional matte film water-based coating adhesive with water repellency, oil repelle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/356C08F220/18C08F220/22C08F230/08C08F220/32C08F220/28
Inventor 张悦陈丽颖赵颖任亚坤葛川
Owner DANDONG UNIK TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com