A kind of preparation method of high nitrogen steel

A high-nitrogen steel and molten steel technology, applied in the field of high-nitrogen steel smelting, can solve the problems of limited thickness of nitriding layer, unsuitable for large-scale production, long nitriding time, etc., and achieve obvious effects

Active Publication Date: 2017-10-27
KUNMING UNIV OF SCI & TECH
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nitriding time of solid solution nitriding is long, and the thickness of the nitriding layer is limited. It is mainly used for surface modification and is not suitable for large-scale production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high nitrogen steel
  • A kind of preparation method of high nitrogen steel
  • A kind of preparation method of high nitrogen steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] In this embodiment, Cr9Mn11Ni0.5 austenitic stainless steel (see Table 1 for composition) is used as the processing object, and specifically includes the following steps:

[0024] Table 1 Composition of stainless steel Cr9Mn11Ni0.5 alloy used in experiments (%)

[0025]

[0026] (1) Place the alloy Cr9Mn11Ni0.5 austenitic stainless steel in the melting crucible 2, close the melting furnace, start the vacuum device 5 to evacuate to 100Pa, turn on the melting device 3 to heat the sample until it melts, and open the nitrogen cylinder valve 4 to fill 0.6MPa industrial nitrogen (nitrogen purity over 99%); the molten metal is kept in a high-pressure nitrogen atmosphere for 20 minutes and the temperature of the molten metal is kept at 1450°C to ensure that the N 2 fully dissolved;

[0027] (2) Adjust the power to keep the molten metal at 1400°C (the liquidus temperature is 1430°C, the solidus temperature is 1330°C), the holding time is 5min, 10min, 15min, 20min respectivel...

Embodiment 2

[0031] This embodiment takes Cr9Mn11Ni0.5 austenitic stainless steel as the processing object, specifically including the following steps:

[0032] (1) Place the alloy Cr9Mn11Ni0.5 austenitic stainless steel in the melting crucible 2, close the melting furnace, start the vacuum device 5 to evacuate to 100Pa, turn on the melting device 3 to heat the sample until it melts, and open the nitrogen cylinder valve 4 to fill 0.1MPa industrial nitrogen (nitrogen purity over 99%); the molten metal is kept in a high-pressure nitrogen atmosphere for 15 minutes and the temperature of the molten metal is kept at 1550°C to ensure that the N 2 fully dissolved;

[0033] (2) Adjust the power to keep the molten metal at 1380°C (the liquidus temperature is 1430°C, the solidus line temperature is 1330°C), the holding time is 5min, 10min, 15min, 20min, and the temperature is controlled during the whole process With the help of thermocouple 8, turn off the power of the equipment after the heat pres...

Embodiment 3

[0037] This embodiment takes Cr9Mn11Ni0.5 austenitic stainless steel as the processing object, specifically including the following steps:

[0038](1) Place the alloy Cr9Mn11Ni0.5 austenitic stainless steel in the melting crucible 2, close the melting furnace, start the vacuum device 5 to evacuate to 100Pa, turn on the melting device 3 to heat the sample until it melts, and open the nitrogen cylinder valve 4 to fill 2MPa industrial nitrogen (nitrogen purity over 99%); the molten metal is kept warm for 30 minutes under a high-pressure nitrogen atmosphere and the temperature of the molten metal is kept at 1400°C to ensure that the N 2 fully dissolved;

[0039] (2) Adjust the power to keep the molten metal at 1350°C (the liquidus temperature is 1430°C, the solidus temperature is 1330°C), the holding time is 5min, 10min, 15min, 20min respectively, and the temperature is controlled during the whole process With the help of thermocouple 8, turn off the power of the equipment after ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of high nitrogen steel, and belongs to the technical field of high nitrogen steel smelting. The method comprises specific steps of clearing up a smelting pot, preparing experimental steel, closing an induction furnace, carrying out vacuumizing treatment, after vacuumizing, starting a heating smelting device, smelting the experimental steel, and controlling the overheating degree of the temperature; opening a nitrogen inlet valve, inflating nitrogen to serve as a nitrogen source, after nitrogen in molten metal is satured, adjusting the power of an induction coil outside a casting crucible to control the cooling rate, preserving the temperature when the molten metal is below the liquid phase line temperature and above the solid phase line temperature, and cooling to the room temperature along with the crucible. The method is suitable for improving the content of nitrogen in the steel, and on the basis of the prior art, the nitrogen content in the steel can be further improved; and a new thinking is provided for high nitrogen steel preparation.

Description

technical field [0001] The invention relates to a preparation method of high nitrogen steel, which belongs to the technical field of high nitrogen steel smelting. Background technique [0002] Nitrogen alloying has many benefits for stainless steel: first, nitrogen alloying can significantly increase the strength of stainless steel, but does not reduce plasticity; secondly, nitrogen is a strong austenite stabilizing element, which can reduce or even replace nickel in stainless steel, economic benefits Significantly; in addition, nitrogen alloying can also improve the corrosion resistance of stainless steel. The steel whose nitrogen content exceeds the upper limit that steel can achieve under conventional smelting conditions (0.08% for ferrite matrix and 0.4% for austenite matrix) is called high nitrogen steel, because the solubility of nitrogen in austenite is much greater than its The solubility in ferrite and martensite, the research work on nitrogen alloying is more arou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/00C22C33/04
Inventor 金青林阳康
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com