Zinc-plated plate oxidation spot removing washing agent as well as preparation method and application thereof

A technology for galvanized sheets and oxidation spots, applied in the field of cleaning agents, can solve the problems of inability to completely remove oxidation spots, slow removal of oxidation spots, and large damage to the galvanized layer, and achieve good cleaning and passivation effects, strong market vitality and Practicality and the effect of using less equipment

Active Publication Date: 2015-09-16
YONGXIN ELECTRONICS CHANGSHU
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the galvanized sheet is cleaned with strong acid to remove oxidation spots (oxidized white spots), the damage to the galvanized layer will be greater, which will cause the galvanized sheet to rust and affect the later use
If weak acid is used to clean the oxidation spots (oxidation spots), the removal speed of the oxidation spots (oxidation spots) is slow, and the oxidation spots (oxidation spots) cannot be completely removed, and the effect is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zinc-plated plate oxidation spot removing washing agent as well as preparation method and application thereof
  • Zinc-plated plate oxidation spot removing washing agent as well as preparation method and application thereof
  • Zinc-plated plate oxidation spot removing washing agent as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] First add 0.5 parts by weight of octylphenol polyoxyethylene ether into 60 parts by weight of water to dissolve, then add 20 parts by weight of phytic acid and 10 parts by weight of acetic acid, stir evenly, then add 6 parts by weight of sodium phytate and 5 parts by weight of sulfuric acid Cerium, stir well.

[0036] The cleaning agent prepared by the above method is easy to store. It only needs to be sealed and stored in a place above 5°C, away from direct sunlight, in a cool and dry place with ventilation, and the storage period is 12 months.

[0037] Use the prepared cleaning agent and adopt the traditional method of dipping to remove oxidation spots (oxidation spots) on the surface of the galvanized sheet to form a passivation film, and expose the steel matrix after the surface of the galvanized sheet, especially the zinc layer is damaged. A passivation film is formed on the part, the immersion temperature is 30°C, and the immersion time is 30 seconds.

[0038] Af...

Embodiment 2

[0047] First add 1 weight part of octylphenol polyoxyethylene ether into 65 parts by weight of water to dissolve, then add 25 parts by weight of phytic acid and 15 parts by weight of acetic acid, stir evenly, then add 8 parts by weight of sodium phytate and 6 parts by weight of sulfuric acid Cerium, stir well.

[0048] The cleaning agent prepared by the above method is easy to store. It only needs to be stored in a place above 5°C, away from direct sunlight, in a cool and dry place with ventilation, and it will not deteriorate for one year in sealed storage.

[0049] Use the prepared cleaning agent and adopt the traditional method of dipping to remove oxidation spots (oxidation spots) on the surface of the galvanized sheet to form a passivation film, and expose the steel matrix after the surface of the galvanized sheet, especially the zinc layer is damaged. A passivation film is formed on the part, the immersion temperature is 20°C, and the immersion time is 60 seconds.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a zinc-plated plate oxidation spot removing washing agent as well as a preparation method and application thereof. The zinc-plated plate oxidation spot removing washing agent comprises the following components in parts by weight: 20-25 parts of phytic acid, 10-15 parts of acetic acid, 0.5-1 part of octaphenyl polyoxyethyiene and 60-65 parts of water; preferably, the zinc-plated plate oxidation spot removing washing agent further comprises 6-8 parts of sodium phytate and 5-6 parts of cerous sulfate. The zinc-plated plate oxidation spot removing washing agent has an economical formula and good washing effect. The preparation method is a mixing and stirring method. The process is simple and used equipment is few. The application is as follows: a traditional method of impregnating is used for removing oxidation spots formed by exposing the surface of a zinc-plated plate in the air, and one layer of a passivated film is formed on the surface of the zinc-plated plate, particularly the part which is exposed out of a steel base body after a zinc layer is damaged; the impregnating temperature is 20-30 DEG C and the impregnating time is 30-60 seconds. The workpiece is good for improving the quality of relative products and the market competitiveness.

Description

technical field [0001] The present invention relates to a cleaning agent, more specifically, the present invention relates to a galvanized sheet cleaning agent for removing oxidation spots, and at the same time, the present invention also relates to a preparation method and application of the galvanized sheet cleaning agent for removing oxidation spots . technical background [0002] When the hot-dip galvanized sheet is in humid air, especially when the air contains CO 2 , SO 2 When acidic substances are waiting, the surface of the galvanized layer will quickly form loose white spots, that is, oxidation spots (oxidation spots). The main components of oxidation spots (oxidized white spots) are zinc oxide (ZnO) and zinc hydroxide (Zn(OH) 2 ). This oxidation spot (oxidation white spot) not only affects the appearance of the galvanized sheet, but also brings difficulties to the future use. [0003] At present, factories usually use pickling to remove oxidation spots (oxidiz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G1/10C23C22/50C23C22/53
Inventor 吴昊吴骏邹宜哲高况忠
Owner YONGXIN ELECTRONICS CHANGSHU