The Method of Making Musical Instruments with Nixing Pottery

A Nixing pottery and musical instrument technology, applied in the field of Nixing pottery to make musical instruments, can solve the problems of non-compact structure, low degree of vitrification, calm percussion sound, etc., achieve internal uniformity, reduce porosity, and crisp percussion sound Effect

Active Publication Date: 2016-09-28
钦州达志文化有限责任公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many kinds of Nixing pottery products, but Nixing pottery cannot be made into pure Nixing pottery due to the fact that Nixing pottery has not been vitrified or has a low degree of vitrification, its structure is not compact, its cross section is rough, its porosity is large, and the knocking sound is calm. Musical instruments with timbre, such as Tao Ou, Tao Guanzhong, Tao Chime, Tao Fangxiang, Tao Chime, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1) Mix the east mud and the west mud in a ratio of 6:4, grind them into a mud by a ball mill, press filter, vacuum the mud, and stale, that is, the Nixing pottery mud, the particle size of the Nixing pottery mud is 4-8μm.

[0018] 2) The kaolin is ground into a slurry by a ball mill, filtered, vacuum smelted, and aged, which is the kaolin mud. The particle size of the kaolin mud is 1 to 2 μm.

[0019] 3) Add kaolin clay and potassium phosphate to Nixing pottery clay. The amount of kaolin clay added is 6% of the weight of Nixing pottery clay, and the amount of phosphate added is 0.1% of the weight of Nixing pottery clay. Mix evenly to form the blank.

[0020] 4) The blanks are made into the blanks of musical instruments such as ou, tube clock, chime, square ring, and chime.

[0021] 5) Dry the body naturally in the shade.

[0022] 6) Send the dried musical instrument blanks into the kiln, and heat up to 980°C at a rate of 100°C per hour, heat and burn at this temperature for 20 m...

Embodiment 2

[0024] 1) Mix the east mud and the west mud in a ratio of 4:6, grind them into a mud by a ball mill, press filter, vacuum the mud, and stale, that is, the Nixing pottery mud. The particle size of the Nixing pottery mud is 4-8μm.

[0025] 2) The kaolin is ground into a slurry by a ball mill, filtered, vacuum smelted, and aged, which is the kaolin mud. The particle size of the kaolin mud is 1 to 2 μm.

[0026] 3) Add kaolin clay and sodium phosphate to the Nixing pottery clay. The amount of kaolin clay added is 8% of the weight of the Nixing pottery clay, and the addition amount of phosphate is 0.5% of the weight of the Nixing pottery clay. Mix evenly to form the blank.

[0027] 4) The blanks are made into the blanks of musical instruments such as ou, tube clock, chime, square ring, and chime.

[0028] 5) Dry the body naturally in the shade.

[0029] 6) Send the dried instrumental shape body into the kiln, heat it up to 990°C at a rate of 150°C per hour, heat it for 25 minutes at this te...

Embodiment 3

[0031] 1) Mix the east mud and the west mud at a ratio of 5:5, grind them into a slurry by a ball mill, press filter, vacuum slush the mud, and stale, that is, the Nixing pottery mud, the particle size of the Nixing pottery mud is 4-8μm.

[0032] 2) The kaolin is ground into a slurry by a ball mill, filtered, vacuum smelted, and aged, which is the kaolin mud. The particle size of the kaolin mud is 1 to 2 μm.

[0033] 3) Add kaolin clay and potassium dihydrogen phosphate to the Nixing pottery clay. The amount of kaolin clay added is 7% of the weight of the Nixing pottery clay, and the amount of phosphate added is 0.3 of the weight of the Nixing pottery clay. %, mix well, it is the blank.

[0034] 4) The blanks are made into the blanks of musical instruments such as ou, tube clock, chime, square ring, and chime.

[0035] 5) Dry the body naturally in the shade.

[0036] 6) Send the dried musical instrument green body into the kiln, heat it up to 985°C at a rate of 120°C per hour, heat it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a method of using Nixing pottery to make a musical instrument. The method includes the steps of blank material preparing, blank forming, blank drying and blank firing. Blank material preparing includes the following steps: 1), using east mud and west mud to make a Nixing pottery mud material according to a conventional method; 2), grinding kaolin to be slurry through a ball grinder, and obtaining a kaolin mud material through press filtering, vacuum mud refining and staling; 3), adding the kaolin mud material and phosphate into the Nixing pottery mud material, and mixing well to obtain the blank material, wherein adding amount of the kaolin mud material is 6-8% of weight of the Nixing pottery mud material, and adding amount of phosphate is 0.1-0.5% of the weight of the Nixing pottery mud material. The musical instrument made by the Nixing pottery is clear and melodious in knocking sound and capable of being on a par with musical instruments made by ceramic in tone.

Description

Technical field [0001] The invention relates to a method for making Nixing pottery, in particular to a method for making musical instruments with Nixing pottery. Background technique [0002] Qinzhou Nixing pottery, Yixing Zisha pottery in Jiangsu, Jianshui pottery in Yunnan, and Rongchang pottery in Sichuan are among the four famous potteries in China and are well-known both at home and abroad. Nixing pottery clay has the characteristics of fine texture, good plasticity, high green strength, strong support in the furnace, etc. There is no need to add any pigments during the firing process, and kiln changes can occur during the firing process, resulting in various colorful colors and Texture, after polishing, many colors such as sky blue, bronze, tiger pattern, dark green can be found on the surface. At the same time, Nixing pottery also has a unique natural double-pore structure, breathable and impervious to water, ceramic products are acid and alkali resistant and non-toxic, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/04C04B33/13
Inventor 钟恒成