High-strength steel with yield strength of 700MPa and TMCP manufacturing method

A technology of yield strength and manufacturing method, applied in the field of high-strength steel production, to achieve the effect of stable performance index and good strength

Inactive Publication Date: 2015-09-30
QINHUANGDAO SHOUQIN METAL MATERIAL
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a high-strength steel with a yield strength of 700MPa and a TMCP manufacturing method, which solves the problem of reducing the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength steel with yield strength of 700MPa and TMCP manufacturing method
  • High-strength steel with yield strength of 700MPa and TMCP manufacturing method
  • High-strength steel with yield strength of 700MPa and TMCP manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] According to the chemical composition range of the "700MPa grade construction machinery steel produced by the TMCP method" of the present invention, slab smelting, slab casting (slab specification: 250mm / 300mm×2000mm×L), Steel plate rolling (rolling specification: 20mm, 30mm).

[0032] A kind of yield strength 700MPa grade high-strength steel, the actual chemical composition (wt%) of embodiment is as shown in table 1:

[0033] Table 1 Actual chemical composition

[0034] Numbering C Si mn P S Alt V Nb Ti Ni Cr Mo B Ceq 1# 0.09 0.32 1.63 0.008 0.002 0.044 0.059 0.06 0.015 0.015 0.21 0.15 0.0016 0.44 2# 0.08 0.31 1.69 0.007 0.001 0.044 0.059 0.06 0.014 0.022 0.23 0.15 0.0016 0.43

[0035] Embodiment rolling process parameter is as shown in table 2:

[0036] Table 2 Actual rolling process parameters

[0037] Thickness / mm Temperature control thickness Finish rolling start temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses high-strength steel with the yield strength of 700MPa and a TMCP manufacturing method, and belongs to the technical field of production of the high-strength steel. The high-strength steel comprises chemical compositions including, by mass, 0.07% to 0.10% of C, 0.15% to 0.40% of Si, 1.20% to 1.80% of Mn, 0% to 0.40% of Cr, 0% to 0.30% of Mo, 0% to 0.30% of Ni, 0% to 0.0020% of B, 0% to 0.070% of Nb, 0% to 0.070% of V, 0% to 0.020% of Ti, 0% to 0.050% of Alt, not larger than 0.015% of P, not larger than 0.010% of S, 0.40% to 0.50% of carbon equivalent Ceq, and the balanced Fe and inevitable impurities. The method comprises the steps of slab casting after smelting, slab heating, billet heating, rolling and water cooling. The high-strength steel has the advantages that a performance index is stable, the requirement of the ultrahigh-strength steel for the performance can be completely met, and the good strength, plasticity, toughness and welding performance can be achieved.

Description

technical field [0001] The invention belongs to the technical field of high-strength steel production, and in particular relates to a high-strength steel with a yield strength of 700 MPa and a TMCP manufacturing method. Background technique [0002] With the rapid development of my country's machinery manufacturing industry, the requirements for the strength, toughness, plasticity and weldability of steel for construction machinery are getting higher and higher; in order to improve production efficiency, reduce the weight of equipment and reduce energy consumption in the construction machinery manufacturing industry, for The demand for steel for construction machinery with higher strength is increasing. [0003] At present, a variety of process methods can be used to produce high-strength engineering machinery steel. At present, the more common ones are controlled rolling and controlled cooling + tempering process (TMCP + tempering process), controlled rolling + quenching and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/58C22C38/54C22C38/50C22C38/48C22C38/46C22C38/40C21D8/02
Inventor 王志勇宋欣董占斌张跃飞田鹏李群王振强刘春明田士平白学军刘永利张学峰王雪松
Owner QINHUANGDAO SHOUQIN METAL MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap