Low-nickel steel plate for pressure vessel at low temperature of -120 DEG C and production method thereof

A technology for pressure vessels and low-temperature conditions, which is applied to low-nickel steel plates for pressure vessels under low-temperature conditions of -120°C and its production field, and can solve the problems of low alloy cost and high alloy cost

Inactive Publication Date: 2015-10-21
武汉钢铁有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially for the high cost of existing steel alloys, the alloy cost of this steel is relatively low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-nickel steel plate for pressure vessel at low temperature of -120 DEG C and production method thereof
  • Low-nickel steel plate for pressure vessel at low temperature of -120 DEG C and production method thereof
  • Low-nickel steel plate for pressure vessel at low temperature of -120 DEG C and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0087] According to the aforementioned formula and production process, five steel plates with different components and different specifications were prepared, and compared with the existing steel types.

[0088] Existing steel plate is compared, enumerate respectively the steel grade of five different compositions and percentage by weight and the comparative steel grade of two different compositions and percentage by weight, as shown in table 2: steel grade of the present invention and comparative steel grade chemical Composition (wt%).

[0089] Table 2 Chemical composition (wt%) of steel grades of the present invention and comparative steel grades

[0090]

[0091]

[0092] It can be seen from the above table 2 that the steel grade produced by the present invention has obviously lower Ni content, lower production cost, and pure steel quality.

[0093] With above-mentioned five different compositions and the steel grade of weight percentage and the comparison steel grad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-nickel steel plate for a pressure vessel at low temperature of -120 DEG C and a production method thereof. The steel plate comprises the components: C less than or equal to 0.04, Si less than or equal to 0.05, Mn between 0.85 and 1.50, P less than or equal to 0.005, S less than or equal to 0.003, Alt between 0.015 and 0.050, Ni between 2.00 and 3.00, Cu between 0.35 and 0.50, Cr between 0.55 and 1.00, N less than or equal to 0.004, at least one of Mo less than or equal to 0.35, Nb less than or equal to 0.05, Ti less than or equal to 0.025 and Ca less than or equal to 0.005, and Fe and inevitable impurities as the rest. According to the low-nickel steel plate, the defect of high cost of existing steel can be overcome, a feasible production process is adopted, mass production operation is facilitated, and pressure vessel steel with good low-temperature toughness, excellent impact performance and strong welding performance is obtained.

Description

technical field [0001] The invention relates to an alloy steel for containers and a production method thereof, in particular to a low-nickel steel plate which can be used for pressure vessels at a low temperature of -120°C and a production method thereof. Background technique [0002] Before the present invention was proposed, the steel types used in my country for the low temperature environment of -120°C were mainly 5Ni steel containing 5% nickel, and the Ni content was relatively high, resulting in high production costs. There is a Chinese patent "a steel for pressure vessels with high toughness at -140°C" (application number: CN201310046993.1), the composition and content of the steel used (chemical composition weight percentage, the same below) is: C≤0.05 , Si≤0.05, Mn: 0.50~1.00, P≤0.006, S≤0.003, Alt: 0.015~0.050, Ni: 4.50~5.30, Nb: 0.02~0.05, Ti: 0.008~0.025, N≤0.004, and also contains Cr≤0.50, Mo≤0.50, Cu≤0.30, Ca≤0.005, one or more steels, the service temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/50C22C38/48C22C38/44C22C38/42
Inventor 战国锋李书瑞刘文斌邹德辉郭斌王宪军杨秀利关云张彦文陈颜堂
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products