Production method of low-oxygen copper rod with diameter of 8 mm

A production method, low-oxygen copper technology, applied in the field of copper processing, can solve the problems of insufficient production consistency, high cost, high defective rate, etc., to achieve the effect of ensuring consistency, improving casting yield, and improving casting efficiency

Inactive Publication Date: 2015-11-25
安徽天大铜业有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of society and economy, the demand for copper is increasing, and the demand for copper products, especially copper rods with a diameter of 8mm, is increasing, and the quality of copper products affects the performance in the market. In the existing production process, The service life of the melting furnace itself, when it enters rolling after casting, due to the high temperature of the slab and the inconsistent speed of the slab entering the rolling mill, the production consistency of the product is not good enough, the defective rate is too high, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Embodiments of the present invention will be described in detail below.

[0014] A kind of 8mm diameter hypoxic copper rod production method, comprises the following steps:

[0015] S1. Ingredients: according to the methods described in GB / T5152 and YS / T464, the chemical composition of the electrolytic copper raw materials is tested, and the electrolytic copper raw materials with a Cu mass fraction of not less than 99.996% are classified as effective raw materials, and the effective raw materials are fed in batches;

[0016] S2. Smelting: The raw materials are put into the furnace and melted to obtain molten copper. In order to protect the furnace, a replaceable protective plate is used at the entrance of the furnace to protect the entrance of the furnace. The molten copper passes through the outlet of the furnace and the upper launder to the holding furnace for refining, furnace and heat preservation The furnace temperature difference is controlled within 5°C, and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of a low-oxygen copper rod with the diameter of 8 mm. The production method mainly comprises the steps of compounding, smelting, casting, rolling, cleaning and cooling, blow-drying, flaw detecting, waxing, rod winding and packaging. According to the production method, energy is saved, environment friendliness is achieved, and the production cost is low. The produced finished low-oxygen copper rod with the diameter of 8 mm is stable in performance, high in quality grade and product consistency and good in economic benefit.

Description

technical field [0001] The invention relates to the field of copper processing, in particular to a method for producing a low-oxygen copper rod with a diameter of 8 mm. Background technique [0002] With the development of society and economy, the demand for copper is increasing, and the demand for copper products, especially copper rods with a diameter of 8mm, is increasing, and the quality of copper products affects the performance in the market. In the existing production process, The service life of the furnace itself, when the cast slab enters rolling after casting, due to the high temperature of the slab and the inconsistent speed of the slab entering the rolling mill, the production consistency of the product is not good enough, the defective rate is too high, and the cost is high. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for producing a low-oxygen copper rod with a diameter of 8 mm, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
CPCB23P15/00
Inventor 李长江李定勇何云龙王春
Owner 安徽天大铜业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com