High-strength reinforced concrete pipe culvert and preparation method thereof

A reinforced concrete, high-strength technology, applied in the field of concrete pipes and culverts, can solve the problems that the index of crack load and failure load is difficult to reach the standard, and the quality of high-strength reinforced concrete pipes and culverts is poor

Inactive Publication Date: 2015-11-25
ANHUI YUTE CONCRETE STRUCTURE TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, concrete is the decisive factor to determine the performance of pipe culverts, but the quality of high-strength reinforced concrete pipe culverts formed after the existing concrete is poured under severe cold conditions is poor, mainly manifested in that the index of crack load and failure load is difficult. up to standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The invention provides a method for preparing a high-strength reinforced concrete pipe culvert, comprising:

[0015] 1) Soak the calcined shells in the activation solution, then filter, dry and sieve to obtain the calcined shells;

[0016] 2) Mixing cement, calcined shells, stones, sand, fly ash and water to prepare concrete;

[0017] 3) Concrete is poured into the reinforced skeleton, and then cured to obtain high-strength reinforced concrete pipe culverts;

[0018] Wherein, the activation solution contains water, hydrochloric acid, citric acid and potassium chromate.

[0019] In the activation solution of the present invention, the amount of each component can be selected within a wide range, but in order to enable the activation solution to further activate the calcined shells, preferably, in step 1), relative to 100 parts by weight of water , the consumption of hydrochloric acid is 15-20 parts by weight, the consumption of citric acid is 7-11 parts by weight, and ...

Embodiment 1

[0029] 1) Soak the calcined shells in the activation solution at 80°C for 16 hours (the weight ratio of the calcined shells to the activation solution is 100:400), then filter, dry at 135°C until the moisture content is lower than 1%, and pass through 200 mesh The activated shell calcined product is obtained by sieving; wherein, the activation solution contains water, hydrochloric acid, citric acid and potassium chromate (weight ratio is 100:17:8:4).

[0030] 2) Mix cement, calcined shells, stones, sand, fly ash and water (weight ratio: 100:30:180:200:60:270) to make concrete.

[0031] 3) Concrete was poured into the steel skeleton, and then cured for 4 days under the conditions of -3°C and 55% relative humidity to prepare high-strength reinforced concrete pipe culvert A1.

Embodiment 2

[0033] 1) Soak the calcined shells in the activation solution at 70°C for 12 hours (the weight ratio of the calcined shells to the activation solution is 100:300), then filter, dry at 120°C until the moisture content is lower than 1%, pass through 200 mesh The activated shell calcined product is prepared by sieving; wherein, the activation solution contains water, hydrochloric acid, citric acid and potassium chromate (weight ratio is 100:15:7:3).

[0034] 2) Mix cement, calcined activated shells, stones, sand, fly ash and water (weight ratio: 100:20:150:180:50:250) to prepare concrete.

[0035] 3) Concrete was poured into the steel skeleton, and then cured for 3 days under the conditions of -5°C and 50% relative humidity to prepare high-strength reinforced concrete pipe culvert A2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength reinforced concrete pipe culvert and a preparation method thereof. The preparation method includes the steps that firstly, shell calcined matter is soaked into activation liquid, and then activated shell calcined matter is obtained through filtering, drying and screening; secondly, cement, the activated shell calcined matter, pebbles, sand, coal ash and water are mixed so that concrete can be prepared; thirdly, the concrete is poured into a reinforcement cage, and then the high-strength reinforced concrete pipe culvert is prepared through curing, wherein the activation liquid comprises water, hydrochloric acid, citric acid and potassium chromate. The high-strength reinforced concrete pipe culvert prepared through the method has excellent fracture load and failure load indexes.

Description

technical field [0001] The invention relates to a concrete pipe culvert, in particular to a high-strength reinforced concrete pipe culvert and a preparation method thereof. Background technique [0002] Culvert refers to a culvert constructed with reinforced concrete box-shaped pipe joints. Pipe culverts consist of one or more square or rectangular sections, generally made of reinforced concrete or masonry, but reinforced concrete is widely used, when the span is less than 4m, pipe culverts are used, for pipe culverts, high-strength reinforced concrete pipes The culvert is a cheap alternative, and the piers, upper and lower slabs are all poured in the same way. [0003] At present, the construction of pipes and culverts generally adopts cast-in-place. The bottom layer is set in the excavated trench, a layer of concrete cushion is poured, and then the processed steel bars are bound on site, and the inner and outer molds are supported. Larger pipes and culverts generally Fir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B14/02C04B20/10
Inventor 肖吕阳
Owner ANHUI YUTE CONCRETE STRUCTURE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com