Weather-proof anti-ultraviolet nylon material and preparation method thereof

A technology of anti-ultraviolet light and weather resistance, applied in the field of polymer materials, can solve the problems of poor thermal stability and dimensional stability, low elongation rate, etc., and achieve improved elongation at break, increased tensile strength, and good thermal stability The effect of sex and dimensional stability

Inactive Publication Date: 2015-12-09
高瑞杰
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention provides a weather-resistant UV-resistant nylon material and a preparation method thereof to improve the existing weather-resistant UV-resistant nylon material with poor thermal and dimensional stability and low elongation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of weather-resistant and anti-ultraviolet light nylon material, its composition is as follows in parts by weight: 50 parts of caprolactam, 3 parts of maleic anhydride grafted with polyethylene and polyolefin elastomer, 3 parts of EPDM rubber grafted with maleic anhydride 3 parts of maleic anhydride, 10 parts of polyethylene and EPDM grafted maleic anhydride, 0.3 parts of epoxy resin, 5 parts of thermosetting resin, 5 parts of carbon fiber, 1 part of toluene 2,4-diisocyanate, 1 part of sodium hydroxide 1 part, 1 part of nano-zinc oxide, 0.5 part of diphenylmethane diisocyanate, 2 parts of flame retardant, 1 part of solid lubricant, 0.5 part of TDI curing agent, 0.5 part of plasticizer, 0.5 part of toughening agent, heat stabilizer 0.5 parts, 0.2 parts of benzotriazole.

[0036] Flame retardants are functional additives that impart flame retardancy to flammable polymers.

[0037] Plasticizers can make the product more flexible and easy to process.

[0038] Toughe...

Embodiment 2

[0049] A weather-resistant and UV-resistant nylon material, the composition of which is as follows in parts by weight: 70 parts of caprolactam, 5 parts of polyethylene and polyolefin elastomer grafted with maleic anhydride, EPDM rubber grafted with maleic anhydride 5 parts of maleic anhydride, 20 parts of polyethylene and EPDM grafted maleic anhydride, 0.5 parts of epoxy resin, 15 parts of thermosetting resin, 8 parts of carbon fiber, 3 parts of toluene 2,4-diisocyanate, 3 parts of sodium hydroxide 3 parts, 3 parts of nano zinc oxide, 1.5 parts of diphenylmethane diisocyanate, 5 parts of flame retardant, 3.5 parts of solid lubricant, 2 parts of TDI curing agent, 1.5 parts of plasticizer, 1.5 parts of toughening agent, heat stabilizer 2 parts, 0.5 parts of benzotriazole.

[0050] The preparation method of the weather-resistant and anti-ultraviolet light nylon material provided by this implementation comprises the following steps:

[0051] S1. Prepare materials according to the f...

Embodiment 3

[0059] A kind of weather resistance anti-ultraviolet light nylon material, its composition is as follows in parts by weight:

[0060] Caprolactam 60 parts, polyethylene and polyolefin elastomer mixture grafted maleic anhydride 4 parts, EPDM rubber grafted maleic anhydride 4 parts, polyethylene and EPDM mixture grafted maleic anhydride 15 parts, epoxy resin 0.4 10 parts of thermosetting resin, 6 parts of carbon fiber, 2 parts of toluene 2,4-diisocyanate, 2 parts of sodium hydroxide, 2 parts of nano zinc oxide, 1 part of diphenylmethane diisocyanate, 4 parts of flame retardant , 2 parts of solid lubricant, 1 part of TDI curing agent, 1 part of plasticizer, 1 part of toughening agent, 1 part of heat stabilizer, 0.4 part of benzotriazole. The weather-resistant and ultraviolet-resistant nylon material provided by the invention has good thermal stability and dimensional stability, and the elongation rate is also high. The present invention also provides a method for preparing the w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a weather-proof anti-ultraviolet nylon material and a preparation method thereof, and relates to the field of polymer materials. The nylon material comprises the following components in parts by weight: 50-70 parts of caprolactam, 3-5 parts of a polyethylene and polyolefin elastomer mixture grafted with maleic anhydride, 3-5 parts of an ethylene-propylene-diene monomer (EPDM) grafted with maleic anhydride, 10-20 parts of a polyethylene and EPDM mixture grafted with maleic anhydride, 0.3-0.5 part of epoxy resin, 5-15 parts of thermosetting resin, 5-8 parts of a carbon fiber, 1-3 parts of 2,4-toluene diisocyanate, 1-3 parts of sodium hydroxide, 1-3 parts of nanometer zinc oxide, 0.5-1.5 parts of diphenylmethane diisocyanate, 2-5 parts of a flame retardant, 1-3.5 parts of a solid lubricant, 0.5-2 parts of a TDI curing agent, 0.5-1.5 parts of a plasticizer, 0.5-1.5 parts of a flexibilizer, 0.5-2 parts of a heat stabilizer and 0.2-0.5 part of benzotriazole. The nylon material is high in airtightness, heat stability and dimensional stability, and relatively high in stretching rate.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a weather-resistant and ultraviolet-resistant nylon material and a preparation method thereof. Background technique [0002] Because of its high mechanical strength, good wear resistance, and superior self-lubricating properties, nylon is widely used in industries such as auto parts, electronic appliances, and petrochemicals. However, the existing nylon materials have the disadvantages of poor light aging resistance, poor thermal stability and dimensional stability, and low elongation rate. It is difficult to carry out engineering applications in some strong ultraviolet light environments, so that its application range has been greatly restricted. Big restrictions. Contents of the invention [0003] In view of this, the present invention provides a weather-resistant and UV-resistant nylon material and a preparation method thereof, so as to improve the problems of poor thermal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L51/00C08L51/04C08L63/00C08L101/00C08K13/04C08K3/22C08K7/06C08K5/3475C08G69/14C08G69/16
CPCC08L77/02C08G69/14C08G69/16C08K2201/011C08L2201/08C08L2205/02C08L2205/025C08L2205/035C08L51/003C08L51/04C08L63/00C08L101/00C08K13/04C08K2003/2296C08K7/06C08K5/3475C08K3/22
Inventor 高瑞杰
Owner 高瑞杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap