Preparation method of ink-jet permeable micro-powder polished tile
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of inkjet penetration and polishing bricks, which is applied in the field of architectural ceramic decoration, can solve the problems of insufficient application, uneven surface, insufficient wear resistance, etc., and achieve the effect of strong pattern layering, high added value, and diversified textures
Active Publication Date: 2015-12-30
MONALISA GRP CO LTD
View PDF5 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But there are also some insurmountable defects: such as the wear resistance of these products is not enough, and the application in public places is not wide enough
[0003] CN104193415A discloses a manufacturing method of ceramic tile mud adobe, which adopts micropowder cloth and inkjet printing, but after the micropowder cloth is formed and before inkjet printing, a layer of transparent glaze needs to be applied on the adobe, and the process is relatively cumbersome. It throws out the texture by throwing blanks, and the surface is uneven
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0048] Reference figure 1 The process flow chart shown, the specific process parameters are as follows:
[0056] 5) Water content of micronized powder: 5.2~5.8%;
[0057] 3. Billet throwing
[0058] The billet thickness is 0.6mm;
[0059] 4. Penetrating inkjet
[0060] Penetrating ink: special ink for inkjet machine that can be fired at high temperature, Flow YE-401\201\511, etc.
[0061] Inkjet penetration aid: special inkjet penetration aid for ceramic products
[0062] Inkjet penetration aid channel: occupy 1 or 2 channels of the existing inkjet machine
[0063] In...
Embodiment 2
[0069] It is basically the same as Embodiment 1, except that the thickness of the cast blank is greater than 0.6 mm and less than 1.0 mm.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a preparation method of an ink-jet permeable micro-powder polished tile. The preparation method comprises the following steps of preparing a micro-powder blank through micro-powder cloth in a compression forming way; carrying out blank polishing treatment on the micro-powder blank, wherein the blank polishing thickness is 0.6 to 1.0 mm; carrying out ink-jet permeation, firing and surface polishing on a micro-powder cloth blank body which is subjected to the blank polishing treatment to obtain the ink-jet permeable micro-powder polished tile. According to the preparation method of the ink-jet permeable micro-powder polished tile, disclosed by the invention, the advantages of high pattern layering sense of a permeable product, random changing of an ink-jet printing product and the micro-powder cloth polished tile are combined, the stereoscopic impression of a pattern can be stronger, and the texture is more diversified.
Description
Technical field [0001] The invention relates to an inkjet penetrating micropowder polished tile and a preparation method thereof, and belongs to the field of architectural ceramic decoration. Background technique [0002] With the improvement of living standards and changes in lifestyles, consumers have increasingly higher aesthetic requirements for building decoration materials. This demand has strongly promoted the development of the building decoration materials industry. In recent years, with the introduction of inkjet printing technology, the decorative effects of related products such as antique tiles, polished crystal tiles, polished glazed tiles, etc. have been substantially improved, which can vividly reproduce the designer’s design and reality. The texture of the stone. But there are also some insurmountable defects: for example, these products have insufficient wear resistance and are not widely used in public places. Micro-powder cloth polished tiles have the advant...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more