A welding process and cylinder technology, applied in welding equipment, welding/welding/cutting items, manufacturing tools, etc., can solve the problems of high labor intensity, difficult to guarantee welding quality, time-consuming and labor-intensive, etc., to reduce labor and save welding material effect

Active Publication Date: 2016-01-13
SHANGHAI ZHENHUA HEAVY IND
View PDF6 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is labor-intensive and time-consuming, and the labor intensity of the workers is high, the production environment is harsh, and the welding quality is difficult to guarantee

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding technology for barrel
  • Welding technology for barrel
  • Welding technology for barrel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] first reference figure 1 as shown, figure 1 A schematic diagram of a groove structure formed in a cylinder welding process according to an embodiment of the present invention is disclosed. Such as figure 1 As shown, the groove is a narrow gap U-shaped groove, and the groove can be roughly divided into two parts: the outer groove and the inner groove. external bevel figure 1 In the upward part of the middle opening, the outer bevel is a U-shaped bevel with a slightly inclined side wall and an open opening, and the root of the outer bevel is a rounded corner. internal groove figure 1 Inverted V-groove. After the internal groove and the external groove are all processed and formed, the root of the internal groove overlaps with the external groove, so the internal groove is not a complete inverted V shape, but an inverted V shape with the tip part missing. The inner groove meets the outer groove.

[0041] continue to refer figure 1 as shown, figure 1 The letters in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
radiusaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding technology for a barrel. The welding technology comprises the following steps: an inner groove machining step, wherein an inner groove is formed through machining and assembling, and the inner groove is an inverted-V-shaped groove; an inner groove welding step, wherein the inner groove is welded, and double-power three-wire submerged arc welding is adopted for welding of the inner groove; an outer groove machining and inner groove back chipping step, wherein the outer groove machining and the inner groove back chipping are performed through one step, and the outer groove is a U-shaped groove; and an outer groove welding step, wherein the outer groove is welded, and double-power three-wire submerged arc welding is adopted for welding of the outer groove. According to the welding technology for the barrel disclosed by the invention, the problems in the prior art that the welding efficiency of the low-alloy high-strength steel thick plate of the barrel is low; manual carbon arc air gouging backing chipping needs to be performed at root parts; the metal filling amount is large at the weld joint; and the like are solved. The welding efficiency and the production efficiency of the welding technology is improved by 2-3 times compared with a traditional technology; the welding material is saved by 10%-20%; carbon arc air gouging backing chipping is not needed; and manual work is reduced by 50%.

Description

technical field [0001] The invention relates to a welding process, more specifically, to a welding process for high-strength steel thick plates. Background technique [0002] A large number of low-alloy high-strength steels are used in marine engineering equipment, and the steel parts formed by these steels need to be welded. For low-alloy high-strength steels, especially those with thicker plates, welding is more difficult. [0003] Offshore wind power system is an important product in offshore equipment. Wind power pipe piles are an important part of wind power systems. The barrel material of offshore wind power pipe piles is generally S355 grade low-alloy high-strength steel with a plate thickness of 40-100 mm. The welded joints generally require high low-temperature impact toughness and CTOD value. In traditional production, manual arc welding is used for bottom welding of cylinder ring longitudinal seam, single-wire submerged arc welding is used to fill cover surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/18B23K9/235B23K33/00B23K103/04
CPCB23K9/18B23K9/235B23K33/004B23K2103/04
Inventor 崔佃忠杜渝包孔郭云飞周弋琳汪兴隆陈阿静
Owner SHANGHAI ZHENHUA HEAVY IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com