Epoxy resin modified waterborne polyurethane flame retardant paint and preparation method thereof

A water-based polyurethane and epoxy resin technology, used in polyurea/polyurethane coatings, fire-retardant coatings, coatings, etc., can solve the problems of water resistance, low hardness and low surface gloss of water-based polyurethane flame-retardant coatings. Long fire resistance, good flame retardancy and less smoke

Inactive Publication Date: 2016-01-13
SKSHU PAINT
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a water-based polyurethane flame-retardant coating modified by epoxy resin and a preparation method thereof, which solves technical problems such as low coating film hardness, low surface gloss, and water resistance of the water-based polyurethane flame-retardant coating. Long fire-resistant time, good flame retardancy, non-toxic and harmless, safe, energy-saving and other advantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin modified waterborne polyurethane flame retardant paint and preparation method thereof
  • Epoxy resin modified waterborne polyurethane flame retardant paint and preparation method thereof
  • Epoxy resin modified waterborne polyurethane flame retardant paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1. Synthesis of epoxy resin modified waterborne polyurethane

[0030] In a five-neck flask equipped with a stirrer, a thermometer, a condensing device and a nitrogen protection, add pretreated 7.5wt% propylene carbonate diol, stir and heat up to 50°C, add 2wt% sodium ethylenedisulfamate Chain extender and 0.1wt% catalyst dibutyltin dilaurate and 24.4wt% toluene diisocyanate, heat up to 70°C and react for 1.5h, then slowly add 2wt% ethylene glycol chain extender compound, keep 80°C for reaction 0.5h, when the reaction is halfway through the chain extension stage, add 6wt% epoxy resin E-51 and keep it at 70°C for 0.5h; then cool down to room temperature, add 3wt% ammonia water dropwise for neutralization, and the titration time is controlled at After 15 minutes, add 53wt% water and 2wt% acetone to the prepolymer for emulsification, vigorously stir for 30 minutes, vacuum reduce and evaporate the acetone to obtain an epoxy resin modified waterborne polyurethane coating.

...

Embodiment 2

[0036] 1. Synthesis of epoxy resin modified waterborne polyurethane

[0037] In a five-necked flask equipped with a stirrer, a thermometer, a condensing device and a nitrogen protection, add pretreated 17.5wt% propylene carbonate diol, stir and heat up to 55°C, add 1wt% adipic acid dihydrazide Chain extender and 0.5wt% catalyst dibutyltin dilaurate and 14wt% 4,4-diphenylmethane diisocyanate, after heating up to 80°C for 3 hours, slowly add metered amount of 8wt% butanediol chain extender Compound, kept at 70°C for 0.8h. When the reaction was halfway through the chain extension stage, 4wt% epoxy resin 711 was added, and kept at 80°C for 1h; then cooled to room temperature, and 1wt% triethylamine was added dropwise for neutralization. After the titration time was controlled at 20 minutes, 49 wt % water and 5 wt % acetone were added to the prepolymer for emulsification, vigorously stirred for 30 min, and the acetone was evaporated under vacuum to obtain an epoxy resin modified wa...

Embodiment 3

[0044] 1. Synthesis of epoxy resin modified waterborne polyurethane

[0045]In a five-neck flask equipped with a stirrer, thermometer, condensing device and nitrogen protection, add pretreated 13.5wt% polypropylene carbonate diol, stir and heat up to 60°C, add 5wt% 2,2-bis Methylol propionic acid chain extender and 0.3wt% catalyst dibutyltin dilaurate and 19.2wt% diisocyanate including isophorone diisocyanate, after heating up to 85°C for 2 hours, slowly add quantitative 4wt% of small molecules For the chain extender compound, keep the reaction at 85°C for 1h. When the reaction is halfway through the chain extension stage, add 2wt% epoxy resin and keep it at 85°C for 0.8h; After neutralization, the titration time is controlled at 30 minutes, and then 45 wt % of water and 6 wt % of acetone are added to the prepolymer for emulsification, vigorously stirred for 30 min, and the acetone is removed by vacuum reduction to obtain an epoxy resin modified waterborne polyurethane coating...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an epoxy resin modified waterborne polyurethane flame retardant paint, which is prepared from the following components by weight percentage: 25-35wt% of a waterborne polyurethane emulsion, 20-28wt% of a flame retardant, 15-23wt% of alcohol, and 20-34wt% of deionized water. The waterborne polyurethane flame retardant paint provided by the invention has the advantages of high film hardness and good water resistance, long fire resistance period, small smoke amount, good flame retardancy, no toxicity and no harm.

Description

technical field [0001] The invention relates to the field of chemical technology, in particular to an epoxy resin-modified waterborne polyurethane flame-retardant coating and a preparation method thereof. Background technique [0002] In the past ten years in my country, on average, there are about 30,000 to 40,000 fires caused by building fires every year, the death toll reaches about 3,000 people, and the fire loss exceeds 200 million yuan. Therefore research and development has important meaning and huge market prospect with flame-retardant coating. [0003] Flame retardant coating refers to a functional coating that is painted on the surface of the substrate to prevent the spread of flame or isolate the fire source, reduce the flammability of the surface of the coated material, prevent the rapid spread of fire, and improve the fire resistance limit. Flame retardant coatings consist of two parts: base material and flame retardant substance. According to its fireproof fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D5/18C08G18/66C08G18/58C08G18/44C08G18/10
Inventor 洪杰詹俊英
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka