Novel modified cotton fiber for infants based on liquid freezing and preparation process thereof

A preparation process, infant technology, applied in fiber processing, plant fibers, textiles and papermaking, etc., can solve the problem of moisture absorption decline, achieve the effect of improving anti-wrinkle performance, facilitating refinement, and improving durability

Active Publication Date: 2016-01-13
南通市昊逸阁纺织品有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The liquid-freezing-based modified cotton fiber for infants and young children prepared by the present invention overcomes the problem of hygroscopicity reduction in traditional liquid ammonia treatment, and the prepared cotton fiber is wrinkle-resistant, hygroscopic, breathable, soft and comfortable, and also has antibacterial and health-care effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel modified cotton fiber for infants based on liquid freezing and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) After the cotton fibers are removed from the surface impurities, they are immersed in deionized water, taken out and aired to obtain cotton fibers with a moisture content of 20%, and the moisture-containing cotton fibers are placed in a subzero-10°C environment to freeze to obtain pretreated cotton fibers. fiber.

[0028] (2) Put the pretreated cotton fiber prepared in step (1) into the sarong of the liquid ammonia treatment tank, vacuumize, and process 2 times through intermittent and repeated liquid ammonia treatment, wherein the intermittent and repeated liquid ammonia treatment includes dispensing a sufficient amount of liquid ammonia Immerse the cotton fiber for 10s, drain the ammonia and pump out the ammonia gas, and remove the ammonia by microwave for 3min at a power of 50kW to obtain the cotton fiber treated by liquid freezing.

[0029] (3) the cotton fiber of the liquid freezing treatment that step (2) is prepared is placed in the chitosan treatment liquid ...

Embodiment 2

[0030] (1) After the cotton fibers are removed from the surface impurities, they are immersed in deionized water, taken out and aired to obtain cotton fibers with a moisture content of 60%, and the hydrated cotton fibers are placed in a subzero-20°C environment to freeze to obtain pretreated cotton fibers. fiber.

[0031] (2) Put the pretreated cotton fiber prepared in step (1) into the sarong of the liquid ammonia treatment tank, vacuumize, and process 3 times through intermittent and repeated liquid ammonia treatment, wherein the intermittent and repeated liquid ammonia treatment includes dispensing a sufficient amount of liquid ammonia Immerse the cotton fiber for 20s, drain the ammonia and pump the ammonia gas, and remove the ammonia by microwave at 80kW power for 5min to obtain the cotton fiber treated by liquid freezing.

[0032] (3) the cotton fiber of the liquid freezing treatment that step (2) is prepared is placed in the chitosan treatment liquid with a bath ratio of...

Embodiment 3

[0034] (1) After the cotton fibers are removed from the surface impurities, they are immersed in deionized water, taken out and dried to obtain cotton fibers with a moisture content of 50%, and the hydrated cotton fibers are placed in a subzero-15°C environment to freeze to obtain pretreated cotton fibers. fiber.

[0035] (2) Put the pretreated cotton fiber prepared in step (1) into the sarong of the liquid ammonia treatment tank, vacuumize, and process 2 times through intermittent and repeated liquid ammonia treatment, wherein the intermittent and repeated liquid ammonia treatment includes dispensing a sufficient amount of liquid ammonia Immerse the cotton fibers for 15s, drain the ammonia and pump out the ammonia gas, and remove the ammonia by microwave at 60kW power for 4min to obtain the cotton fibers treated by liquid freezing.

[0036] (3) the cotton fiber of the liquid freezing treatment that step (2) is prepared is placed in the chitosan treatment liquid with a bath ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a novel modified cotton fiber for infants based on liquid freezing and a preparation process thereof. The novel modified cotton fiber comprises the steps: (1) after surface impurities are removed from the cotton fiber, soaking the cotton fiber in deionized water, taking out and airing the cotton fiber to obtain a water-containing cotton fiber, placing the water-containing cotton fiber in the subzero environment to perform freezing, and obtaining the pretreated cotton fiber; (2) placing the pretreated cotton fiber in a yarn cage of a liquid ammonia treatment tank, performing vacuumizing, and performing intermittent repeated liquid ammonia treatment 2-3 times to obtain the cotton fiber having undergone liquid freezing treatment; (3) placing the cotton fiber having undergone liquid freezing treatment in treating fluid according to the bath ratio of 1:(30-40), performing ultrasonic oscillation, taking the cotton fiber out, performing washing and drying, and obtaining the modified cotton fiber for infants based on liquid freezing. The prepared modified cotton fiber for infants based on liquid freezing first undergoes soaking treatment and then undergoes liquid freezing treatment, so that the surface of the cotton fiber is flat, the anti-wrinkle performance is improved while the water absorption is not affected much, and the antibiosis and health care effects are achieved finally through chitosan treatment.

Description

Technical field: [0001] The invention belongs to the technical field of textile materials, and in particular relates to a modified cotton fiber for infants based on liquid freezing and a preparation process thereof. Background technique: [0002] As we all know, the infant period is the most delicate and fragile period in a person's life. Although the innovation of modern textile technology has caused great changes in the structure of clothing fabrics, the choice of infant clothing is still based on hygienic and comfortable natural fibers. Mainly, cotton fiber, as one of the four natural fibers cotton, wool, silk, and hemp, has always been favored by people because of its unique and excellent properties such as softness, warmth, and comfort. [0003] Cotton fiber has good softness, warmth, moisture absorption and conductivity, but poor wrinkle resistance, poor durability, easy to mold, and single function, it is difficult to meet the growing consumer demand, and the improvem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/03D06M11/61D06M15/11D06M101/06
Inventor 董荣琴
Owner 南通市昊逸阁纺织品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com