Quick evaluation test method of anti-corrosion performance of tin-plated board

A technology for evaluating tests and test methods, which is applied in the fields of weather resistance/light resistance/corrosion resistance, measuring devices, instruments, etc., can solve the problems of obtaining tin-plated products' corrosion resistance performance indicators, disadvantages, etc., and achieve quantitative ratings and convenient methods Effect

Inactive Publication Date: 2016-01-13
SHANGHAI MEISHAN IRON & STEEL CO LTD
View PDF16 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the above-mentioned test methods are mechanistic and microscopic studies, which require expensive testing equipment and a long test cycle to complete th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick evaluation test method of anti-corrosion performance of tin-plated board
  • Quick evaluation test method of anti-corrosion performance of tin-plated board
  • Quick evaluation test method of anti-corrosion performance of tin-plated board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of rapid evaluation test method of tinplate corrosion resistance, the concrete steps of described test method are as follows:

[0045] 1) Select the tin plate and perform pretreatment, and select the thickness of the tin layer to be 1.1g / m 2 , passivation film thickness is 4mg / m 2 Tinplate; such a tinplate can clearly evaluate the corrosion resistance level of the tinplate;

[0046] 2) Place the above sample in the salt spray corrosion test box, and hang the sample on the suspension rod in the box;

[0047] 3) Select the basic corrosion medium as NaCl solution with a mass concentration of 2%, and add a certain concentration of NaHSO 3 solution; sequentially adjust the six dimensions of the four test parameters such as the concentration of the corrosion medium, the settlement of the corrosion medium, the temperature and the test period, and carry out the corrosion test; the four factors of the concentration of the corrosion medium, the settlement of the corrosio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a quick evaluation test method of anti-corrosion performance of a tin-plated board. The quick evaluation test method is characterized by comprising the following steps: 1) selecting a tin-plated board being 1.1 g/m<2> in tin layer thickness and 4 mg/m<2> in passivated film thickness and pre-treating the tin-plated board; 2) placing the test sample in a salt fog corrosion test box, wherein the test sample is hanged on a hanging rod in the box body; 3) selecting a NaCl solution being 2% in mass concentration as a basic corrosion medium with a NaHSO3 solution in a certain concentration matched therewith, successively adjusting six dimensions of four test parameters comprising corrosion medium concentration, corrosion medium settlement quantity, temperature and test period to carry out a corrosion test; 4) when the corrosion test is finished, taking out the test sample and washing the sample through deionized water at 20-30 DEG C for 30-60 s, and air-drying the sample with cold air; and 5) comparing the test sample with six test result legends under the six dimensions, and evaluating and recording a result according to two characteristic parameters comprising corrosion area and corrosion point diameter to achieve quantitative evaluation of the anti-corrosion performance of the tin-plated board.

Description

technical field [0001] The invention relates to a rapid evaluation test method, in particular to a rapid evaluation test method for the corrosion resistance of a tinplate. Background technique [0002] Tinplate has many advantages such as firmness, beauty, and good formability, and is widely used in food cans, chemical cans, spray cans, carbonated beverage cans, packaging materials, etc. Tinplates will be corroded during production and transportation, especially in sea and humid climates, which will aggravate the corrosion of tinplates. Therefore, it is necessary to continuously improve the quality of tinplates to improve their corrosion resistance. Tinplate is a thin coating product, and the coating weight is 1.1 and 2.8g / m 2 Mainly, and with the decrease of tin resources, the thinning of tin plating has become the mainstream. For a long time, there is no good test method for quickly evaluating the corrosion resistance of tinplate, and the corrosion resistance of tinplate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N17/02
Inventor 陆永亮陆伟星
Owner SHANGHAI MEISHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap