High-oil-absorption resin and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of high oil-absorbing resin and oil phase, applied in chemical instruments and methods, other chemical processes, etc., can solve the problem of insufficient adsorption capacity and achieve the effect of increasing adsorption capacity
Inactive Publication Date: 2016-01-20
BLUESTAR CHENGDU NEW MATERIALS
View PDF5 Cites 23 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0006] The purpose of the present invention is to solve the problem that although the oil-absorbing resin in the prior art can be used to recover oil slicks on the water surface, the adsorption capacity is st
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0031] A high oil-absorbing resin, comprising the following raw materials in parts by weight:
[0032] Oil phase:
[0033] 4 parts divinylbenzene
[0034] 20 parts of styrene
[0035] Lauryl acrylate 20 parts
[0036] 20 parts of butyl acrylate
[0037] Butadiene rubber 20 parts
[0038] Azobisisobutyronitrile 3 parts
[0039] 40 parts of toluene;
[0040] water box:
[0041] 5 parts polyvinyl alcohol
[0042] 10 parts gelatin
[0043] 5 parts of NaCl
[0044] CaCO 3 5 copies
[0045] 500 parts of deionized water.
Embodiment 2
[0047] A high oil-absorbing resin, comprising the following raw materials in parts by weight:
[0048] Oil phase:
[0049] 8 parts of divinylbenzene
[0050] 30 parts of styrene
[0051] Lauryl acrylate 30 parts
[0052] 30 parts of butyl acrylate
[0053] Butadiene rubber 30 parts
[0054] Azobisisobutyronitrile 9 parts
[0055] 50 parts of toluene;
[0056] water box:
[0057] 9 parts polyvinyl alcohol
[0058] 20 parts gelatin
[0059] 8 parts of NaCl
[0060] CaCO 3 10 copies
[0061] 600 parts of deionized water.
Embodiment 3
[0063] A high oil-absorbing resin, comprising the following raw materials in parts by weight:
[0064] Oil phase:
[0065] 6 parts of divinylbenzene
[0066] 25 parts of styrene
[0067] Lauryl acrylate 25 parts
[0068] 25 parts of butyl acrylate
[0069] Butadiene rubber 25 parts
[0070] Azobisisobutyronitrile 6 parts
[0071] 45 parts of toluene;
[0072] water box:
[0073] 7 parts polyvinyl alcohol
[0074] 15 parts gelatin
[0075] NaCl6.5 parts
[0076] CaCO 3 7.5 servings
[0077] 550 parts of deionized water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to high-oil-adsorption resin and a preparation method thereof, and belongs to the technical field of oil-adsorption resin. The high-oil-adsorption resin comprises an oil phase and a water phase, wherein the oil phase is prepared from, by weight, 4-8 parts of divinyl benzene, 20-30 parts of styrene, 20-30 parts of n-lauryl acrylate, 20-30 parts of butyl acrylate, 20-30 parts of butadiene rubber, 3-9 parts of azodiisobutyronitrile and 40-50 parts of methylbenzene, and the water phase is prepared from, by weight, 5-9 parts of polyvinyl alcohol, 10-20 parts of gelatin, 5-8 parts of NaCl, 5-10 parts of CaCO3 and 500-600 parts of deionized water. According to the high-oil-adsorption resin and the preparation method thereof, the high-oil-adsorption resin is prepared by taking adopting a suspension polymerization technology, taking the styrene, the n-lauryl acrylate, the butyl acrylate and the butadiene rubber as the raw materials, taking the azodiisobutyronitrile as an initiator and taking the divinyl benzene as a cross-linking agent, and the adsorption quantity of the oil-adsorption resin is greatly increased.
Description
technical field [0001] The invention relates to a resin and a preparation method thereof, more specifically, the invention relates to a high oil-absorbing resin and a preparation method thereof, belonging to the technical field of oil-absorbing resins. Background technique [0002] High oil-absorbing resins can absorb various oily substances, and are especially suitable for the adsorption and recovery of oil slicks or spilled oils on water surfaces and other solid surfaces. At the same time, it can also be used for separation and purification of oily wastewater. [0003] This type of high oil-absorbing resin has a certain cross-linked network structure, good toughness and elasticity, and also has good heat brushing, cold resistance, not easy to age, and fast oil absorption. It overcomes the shortcomings of traditional oil-absorbing materials. The cross-linked molecules have a three-dimensional cross-network structure, and there are certain micropores inside. The resin can b...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more