Composite electroplating bath containing nano-sized vanadium carbide

A composite electroplating and vanadium carbide technology, applied in the direction of electrolytic coating, coating, etc., can solve the problems of long time consumption, easy to rust, corrosion, etc., and achieve the effect of low wear resistance, preventing easy agglomeration, and good corrosion resistance

Inactive Publication Date: 2016-01-20
ANHUI CHANGQING ELECTRONICS MACHINERY GRP
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many scaffolds made of steel pipe materials. Generally, construction projects take a long time, and the scaffolding is exposed outside. It is easy to rust and corrode in bad weather. In order to save resources and prolong the service life of scaffolding, the surface modification method of materials will be used to achieve wear resistance and corrosion resistance. , anti-rust performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A composite electroplating solution containing nano vanadium carbide, made of the following parts by weight (kg) of raw materials: nickel sulfamate 500, cobalt sulfate 21, nickel chloride 33, boric acid 30, sodium lauryl sulfate 0.7, eleven Sodium alkyl sulfonate 0.4, styrene 4, azobisisobutyronitrile 0.2, nano vanadium carbide 7, saccharin 0.4, basalt fiber 5, stearic acid 4, ethylene glycol 2, starch 5, deionized water.

[0015] The composite electroplating solution containing nano vanadium carbide is prepared by the following specific steps:

[0016] (1) Mix and stir nano vanadium carbide, basalt fiber, starch and appropriate amount of deionized water. After heating to form a paste, calcinate at 600°C for 1 hour, cool and pulverize, ultrasonically clean with an appropriate amount of acetone solution for 20 minutes, and take it out Rinse with deionized water to make it neutral, then put it in a blast drying box for drying, and set aside;

[0017] (2) Add a certain amount of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
wear volumeaaaaaaaaaa
porosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a composite electroplating bath containing nano-sized vanadium carbide. The composite electroplating bath containing nano-sized vanadium carbide is prepared from, by weight, 500-550 parts of nickel aminosulfonate, 21-25 parts of cobaltous sulfate, 33-38 parts of nickel chloride, 30-35 parts of boric acid, 0.7-0.8 part of lauryl sodium sulfate, 0.4-0.6 part of sodium 1-undecanesulfonate, 4-6 parts of styrene, 0.2-0.3 part of azodiisobutyronitrile, 7-9 parts of the nano-sized vanadium carbide, 0.4-0.5 part of saccharin, 5-6 parts of basalt fibers, 4-5 parts of stearic acid, 2-3 parts of ethylene glycol, 5-6 parts of starch, and a proper amount of deionized water. The composite electroplating bath is environmentally friendly, nontoxic, simple in process and low in cost.

Description

Technical field [0001] The invention relates to the technical field of electroplating solutions, in particular to a composite electroplating solution containing nano vanadium carbide. Background technique [0002] Scaffolding refers to various supports erected on the construction site for workers to operate and solve vertical and horizontal transportation. A general term in the construction industry, refers to the use of external walls, internal decoration or high-rise places on construction sites that cannot be directly constructed, mainly for construction personnel to work up and down or to protect the outer safety net and install components at high altitude. Scaffolding materials usually include bamboo, wood, steel pipe or synthetic materials. Some projects also use scaffolding as templates, and are also widely used in the advertising industry, municipal administration, traffic roads and bridges, and mining. At present, there are many scaffolds made of steel pipe materials, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D15/00C25D3/12
Inventor 吴长青
Owner ANHUI CHANGQING ELECTRONICS MACHINERY GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap