Catalyst used for preparation of polyester, preparation method and application thereof

A catalyst, polyester technology, applied in the preparation of this catalyst, poly(trimethylene terephthalate), the field of polyester production, can solve the problem of polyester that has not been reported

Active Publication Date: 2016-01-27
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In the above reports, there is no report on the preparation of a catalyst with high catalytic activity in the esterification and polycondensation stages of polyester, especially poly(trimethylene terephthalate).

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst used for preparation of polyester, preparation method and application thereof
  • Catalyst used for preparation of polyester, preparation method and application thereof
  • Catalyst used for preparation of polyester, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] Mix 142g of tetraisopropyl titanate with 46g of ethanol and 90g of lactic acid, and react for 4 hours at a temperature of 100°C in a stirred reactor. Add 36g of magnesium acetate and 91g of triethyl phosphate to the reactant. In the reactor, the reaction was carried out for 4 hours under the temperature condition of 120°C. The reaction product is placed in a reactor equipped with a fractionation device, and ethanol and isopropanol are distilled off to make a catalyst. The catalyst is mixed with 1,3-propanediol, wherein the mass fraction of titanium atoms is 4%.

[0056] 600 grams of terephthalic acid, 440 grams of 1,3 propylene glycol and 1.49 g of catalyst were mixed to form a slurry, which was added to a polymerization kettle for esterification reaction. The esterification temperature was 230 ° C and the pressure was 0.25 MPa. The device discharges the water generated by the reaction, reacts for 2 hours, and the esterification rate is 96%. After the esterification i...

Embodiment 2

[0059] Mix 142g of tetraisopropyl titanate with 46g of ethanol and 192g of citric acid, and react for 4 hours at 100°C in a stirred reactor, add 36g of magnesium acetate and 91g of triethyl phosphate to the reactant, and In a stirred reactor, the reaction was carried out at a temperature of 120° C. for 4 hours. The reaction product is placed in a reactor equipped with a fractionation device, and ethanol and isopropanol are distilled off to make a catalyst. The catalyst is mixed with 1,3-propanediol, wherein the mass fraction of titanium atoms is 4%.

[0060] 600 grams of terephthalic acid, 440 grams of 1,3 propylene glycol and 1.49 g of catalyst were mixed to form a slurry, which was added to a polymerization kettle for esterification reaction. The esterification temperature was 230 °C and the pressure was 0.25 MPa. The device discharges the water generated by the reaction, and reacts for 2 hours, and the esterification rate is 97%. After the esterification is completed, the...

Embodiment 3

[0063] Mix 142g of tetraisopropyl titanate with 46g of ethanol and 192g of citric acid, and react for 4 hours at a temperature of 100°C in a stirred reactor, and add 61g of zinc lactate and 91g of triethyl phosphate to the reactant. In a stirred reactor, the reaction was carried out at a temperature of 120° C. for 4 hours. The reaction product is placed in a reactor equipped with a fractionation device, and ethanol and isopropanol are distilled off to make a catalyst. The catalyst is mixed with 1,3-propanediol, wherein the mass fraction of titanium atoms is 4%.

[0064] 600 grams of terephthalic acid, 440 grams of 1,3 propylene glycol and 1.49 g of catalyst were mixed to form a slurry, which was added to a polymerization kettle for esterification reaction. The esterification temperature was 230 ° C and the pressure was 0.25 MPa. The device discharges the water generated by the reaction, reacts for 2 hours, and the esterification rate is 96%. After the esterification is complet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a catalyst used for preparation of polyester, a preparation method and application thereof. The catalyst mainly solves the problem of absence of the catalyst with high catalytic activity in the stages of esterification and polycondensation of polytrimethylene terephthalate in the prior art. A technical scheme of the invention adopts reaction products which comprise the following components: a) a titanium compound, b) a hydroxyl compound, c) organic metal salt, and d) a phosphorus compound; the preparation method for the catalyst comprises the following steps: subjecting the titanium compound and the hydroxyl compound to reaction at 0 to 200 DEG C for 0.1 to 24 hours so as to obtain an intermediate product, adding the metal organic salt and the phosphorus compound into the obtained intermediate product, and carrying out reaction at 0 to 200 DEG C for 0.1 to 24 hours so as to obtain the catalyst used for preparation of polyester; thus, the problem is well solved, and the catalyst can be applied in preparation of polytrimethylene terephthalate, polyethylene terephthalate and polybutylene terephthalate.

Description

technical field [0001] The present invention relates to a catalyst composition, which is particularly useful in the manufacture of polyesters, especially polytrimethylene terephthalate, and to a process for the preparation of such a catalyst. Background technique [0002] The promotion of catalyst is essential in the preparation of polyester. Several metals and metal-containing compositions can be used to catalyze the synthesis of polyesters. Antimony compounds are most commonly used in the manufacture of antimony-based catalysts, titanium compounds such as titanium alkoxides can also be used in the preparation of polyester. Polypropylene terephthalate is a new type of polyester material. Its fiber products have both the advantages of nylon and polyester. It is suitable for the manufacture of high-end clothing, wool-like fabrics, car carpets and other products. It is considered to be a new type of polyester that is expected to replace polyester. product. However, the intr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G63/85C08G63/83C08G63/183
Inventor 宋歌熊金根周文乐
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com