A sand-proof and coating technology, applied in the field of coatings, can solve the problems of poor weather resistance and poor wear-resistance of sand-proof coatings, and achieve excellent wear resistance, good fracture resistance, chemical resistance and impact resistance. Effect
Inactive Publication Date: 2016-01-27
SUZHOU MINGXUAN FLOORING COATINGS
View PDF5 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The technical problem mainly solved by the present invention is to provide a wear-resistant and anti-wind and sand coating, which solves the problems of poor wear resistance and poor weather resistance of the anti-wind and sand coating.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0015] Embodiment 1 of the present invention includes: a wear-resistant and anti-wind and sand coating, comprising the following components in proportion:
[0016] 22 parts polyimide
[0017] 22 parts vinyl
[0018] 28 parts of polyethylene terephthalate
[0019] 40 parts of water-based polyurethane emulsion
[0020] 24 parts of glass fiber reinforced plastic particles
[0021] 13 parts of benzenesulfonic acid
[0022] 21 parts of titanium dioxide
[0023] 3 parts of dispersant.
Embodiment 2
[0024] Embodiment 2 of the present invention includes: a wear-resistant and anti-wind and sand coating, comprising the following components in proportion:
[0025] 25 parts polyimide
[0026] 28 parts vinyl
[0027] 30 parts of polyethylene terephthalate
[0028] 42 parts of water-based polyurethane emulsion
[0029] 27 parts of glass fiber reinforced plastic particles
[0030] 15 parts of benzenesulfonic acid
[0031] 23 parts of titanium dioxide
[0032] Dispersant 5 parts.
Embodiment 3
[0033] Embodiment 3 of the present invention includes: a wear-resistant and anti-wind sand coating, comprising the following components in proportion:
[0034] 28 parts of polyimide
[0035] 34 parts vinyl
[0036] 32 parts of polyethylene terephthalate
[0037] 44 parts of water-based polyurethane emulsion
[0038] 30 parts of glass fiber reinforced plastic particles
[0039] 16 parts of benzenesulfonic acid
[0040] 25 parts of titanium dioxide
[0041] 6 parts of dispersant.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses wear resistant and wind-sand resistant paint. The wear resistant and wind-sand resistant paint comprises the following components according to the following content ratio: 22 to 28 parts of polyimide, 22 to 34 parts of vinyl, 28 to 32 parts of poly-terephthalyl alcohol, 40 to 44 parts of aqueous polyurethane emulsion, 24 to 30 parts of glass fiber reinforced plastic particles, 13 to 16 parts of benzenesulfonic acid, 21 to 25 parts of titanium dioxide and 3 to 6 parts of dispersant. By the abovementioned mode, the wear resistant and wind-sand resistant paint is provided, and the wear resistant and wind-sand resistant paint has the characteristics of super weatherability, high elasticity, wind-sand resistance, high and low-temperature deformation resistance, good breaking resistance, excellent wear resistance, strong chemical resistance and impact resistance and the like.
Description
technical field [0001] The invention relates to the field of coatings, in particular to a wear-resistant and sand-proof coating. Background technique [0002] Coating refers to the formation of a thin film attached to the surface of an object under certain conditions, which can perform functions such as protection and decoration. A class of liquid or solid materials such as insulation, rust prevention, mildew resistance, heat resistance, etc. However, the current wear-resistant coatings usually have the problem of poor wear resistance, and they may fall off or even break during use. Therefore, it is very necessary to have a coating with better performance and more wear resistance. At present, the wear resistance of the existing coatings is average, and the coatings are often subject to friction on some exposed coating parts and are easy to wear; moreover, in environments with large temperature differences, peeling and cracking are prone to occur, which are extremely serious...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more